湿热环境下端径比对复合材料螺栓连接结构静力拉伸失效的影响

doi:10.11896/cldb.22100282

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (18365KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to study the static properties of the carbon fiber reinforced composite (CFRP) bolted joint structure under hygrothermal environment,the static tensile tests of the T300 composite single-bolt single-lap bolted jointed structure with different end-to-diameter ratios were conducted,and the failure mode of the joint was revealed by the variation of the ultimate failure load and the failure strength of the 25 ℃ room temperature dry (RTD) and 70 ℃ equilibrium temperature wet (ETW) environment with different end-to-diameter ratios.A finite element model of composite single-bolt single-lap bolted connection was established,and the optimal end-to-diameter ratio of 3 was obtained by comparing it with the test.The damage forms of different plies of the optimal end-to-diameter ratio connection structure in the hygrothermal environment were studied.The results show that when the end-to-diameter ratio is increased from 1 to 3,the ultimate failure load of the connection structure under the RTD and ETW environments is increased by 1.1 times and 1 times respectively,the failure strength is increased by 1 times,and when the end-to-diameter ratio is increased from 3 to 4,the ultimate failure load in the RTD and ETW environments is reduced by 6.56% and 9.08% respectively,the failure intensity is reduced by 6.83% and 9.35% respectively.When the optimal end-to-diameter ratio is 3,the ultimate failure load and failure strength of the connection structure in the ETW environment are reduced by 9.25% and 9.52% respectively,compared with the RTD environment.By scanning electron microscopy,it was found that the compression damage around the hole of the laminate plate under the ETW environment was more severe,and more obvious fiber bundle uplift and fiber fragmentation could be found.

Key words： composite hygrothermal environment end-to-diameter ratio bolted joint single-bolt single-lap static tensile

Published: 10 March 2024 Online: 2024-03-18

CLC number:

V214

Fund:National Natural Science Foundation of China (U2033209).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	JIA Baohui
	REN Peng
	SONG Ting
	CUI Kaixin
	XIAO Haijian

Cite this article:

JIA Baohui,REN Peng,SONG Ting, et al. Effect of End-to-diameter Ratio on Static Tensile Failure of Composite Bolted Joints Under Hygrothermal Environment[J]. Materials Reports, 2024, 38(5): 22100282-7.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22100282 OR http://www.mater-rep.com/EN/Y2024/V38/I5/22100282

1 Li J, Chen X B. Materials Reports, 2022, 36(14), 206(in Chinese).
李军, 陈祥宝. 材料导报, 2022, 36(14), 206.
2 Feng Z H, Li J N, Tian Y L, et al. Acta Materiae Compositae Sinica, 2022, 39(9), 4187(in Chinese).
冯志海, 李俊宁, 田跃龙, 等. 复合材料学报, 2022, 39(9), 4187.
3 Loeliger A, Yang E, Bomphray I. In:26th International Conference on Automation and Computing(ICAC). University of Portsmouth, UK, 2021.
4 Delzendehrooy F, Akhavan-Safar A, Barbosa A Q, et al. Journal of Advanced Joining Processes, 2022, 5, 100098.
5 Sivakumar D M, Lin F N, Chew R M, et al. International Review of Mechanical Engineering, 2017, 11(2), 138.
6 Li M Z, Liu Z P, Yan R J, et al. Marine Structures, 2022, 85, 103259.
7 Lee Y G, Choi E, Yoon S J. Composites Part B: Engineering, 2015, 75, 1.
8 Awadhani L V, Bewoor A K. Materials Today: Proceedings, 2017, 4(8), 7345.
9 Meziere Y, Bunsell A R, Favry Y, et al. Composites Part A, 2005, 36(12), 1627.
10 Chen H S. Composite Structures, 2001, 52(3-4), 295.
11 Zhang J R, Shan M J, Huang W, et al. Acta Materiae Compositae Sinica, 2021, 38(7), 10(in Chinese).
张娇蕊, 山美娟, 黄伟, 等. 复合材料学报, 2021, 38(7), 10.
12 Du Y, Ma Y E. Acta Materiae Compositae Sinica, 2022, 39(2), 431(in Chinese).
杜永, 马玉娥. 复合材料学报, 2022, 39(2), 431.
13 Shan M J, Zhao L B, Liu F R, et al. Composite Structures, DOI:10. 1016/j. compstruct. 2020. 112166.
14 Wu Q Q. Research on the influence of temperature and humidity upon the strength of composite bolted joints. Master's Thesis, Nanjing University of Aeronautics and Astronautics, China, 2018(in Chinese).
吴婧婧. 温度和湿度对复合材料螺栓连接强度影响研究. 硕士学位论文, 南京航空航天大学, 2018.
15 Laszlo P, George S. Mechanics of composite structures, Cambridge University Press, Britain, 2003.
16 Camanho P P, Matthews F L. Journal of Composite Materials, 1999, 33(24), 2248.
17 Zhang J Y, Zhou L W, Chen Y L, et al. Journal of Composite Materials, 2016, 50(16), 2271.
18 Shan M J, Zhao L B, Hong H M, et al. International Journal of Fatigue, 2018, 111, 299.
19 Conshohocken W. Standard test method for moisture absorption properties and equilibrium conditioning of polymer matrix composite materials, ASTM D5229M-14, ASTM International, 2014.
20 Liu W, Yu F, He Z, et al. Modelling and Simulation in Materials Science and Engineering, 2019, 27(6), 065011.
21 Cooper C, Turvey G J. Composite Structures, 1995, 32(1-4), 217.