多尺度钢纤维混杂增强水泥基材料抗冲击性能及阻裂能力

doi:10.11896/cldb.22030271

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (29934KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to better study the reinforcement effect of hybrid steel fiber on cement-based materials, three kinds of steel fibers with lengths of 6 mm (S), 13 mm (M) and 35 mm (H) were used to prepare cylindrical specimens for drop weight impact test. The effects of steel fiber hybrid methods on the impact resistance and crack resistance of cement-based materials were explored from the aspects of impact times, energy consumption, failure pattern and crack width development. The test results show that the impact resistance of steel fiber increases gradually from single to triple mixing. The increasing effect of steel fiber on the strength and impact resistance of cement-based materials is M＞H＞S. The combination mode of steel fiber double mixing is M+H＞S+M＞S+H. When 1.5%M and 0.5%H were mixed, the strengthening and toughening effect of steel fiber was the best, and the bending strength of steel fiber was 22.6 MPa at 28 d, which was 3.2% and 31.4% higher than that of M and H alone. The compressive strength of 28 d was 154.8 MPa, which was 40.1% and 65.5% higher than that of M and H, respectively. The energy consumption of initial crack shock was 23.5% and 425% higher than that of two fibers, and the energy consumption of failure shock was 36.7% and 300% higher than that of two fibers, respectively. The optimal dosage of the three kinds of steel fibers was 0.5%S, 0.5%M and 1%H, respectively, and the energy consumption of initial cracking and failure shock was 33.3% and 1.9% higher than that of the optimal dual-mixing group (M1.5H0.5), respectively. The two parameter Weibull distribution can reasonably describe N1 and N2 of steel fiber hybrid reinforced cement-based materials. S inhibits the creation and expansion of microcracks, while M and H prevent the development of macroscopic cracks at different stages of loading. The various fibers act as progressive crack arrestors at different structural levels and in different loading stages.

Key words： cement-based material hybrid steel fiber impact resistance crack resistance capacity

Published: 25 January 2024 Online: 2024-01-26

CLC number:

TU528.572

Fund:Science and Technology Research Project of Chongqing Education Commission (KJZD-K201901201, KJZD-202101201), Top-notch Young Talents in Chongqing(CQYC201905086), Wanzhou District Innovation and Entrepreneurship Demonstration Team, and Chongqing Three Gorges Reservoir Bank Slope and Engineering Structure Disaster Prevention and Control Engineering Technology Research Center Open Fund Project (SXAPGC21MS05).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	GUO Yuanchen
	LIU Xinzhou
	WANG Xue
	YE Qing
	XIANG Kai
	WANG Rui

Cite this article:

GUO Yuanchen,LIU Xinzhou,WANG Xue, et al. Multiscale Hybrid Steel Fiber Enhances the Impact Resistance and Crack Resistance of Cement-based Materials[J]. Materials Reports, 2024, 38(2): 22030271-8.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22030271 OR http://www.mater-rep.com/EN/Y2024/V38/I2/22030271

1 Zhou K T, Fang Z, Deng S J, et al. In:Proceedings of the 21st National Symposium on Modern Structural Engineering. Shijiazhuang, 2021, pp. 348(in Chinese).
周科廷, 方震, 邓盛杰, 等. 第二十一届全国现代结构工程学术研讨会论文集. 石家庄, 2021, pp. 348.
2 Prem P R, Murthy A R, Bharatkumar B H, et al. Magazine of Concrete Research, 2015, 67(18), 1.
3 Peng G F, Niu X J, Zhao Y L. Journal of Building Materials, 2016, 19(6), 1013(in Chinese).
朋改非, 牛旭婧, 赵怡琳. 建筑材料学报, 2016, 19(6), 1013.
4 Hung C C, Chen Y T, Yen C H. Construction and Building Materials, 2020, 260, 119944.
5 Gou H X, Zhu H B, Zhou H Y, et al. Journal of the Chinese Ceramic Society, 2020, 48(11), 1756(in Chinese).
苟鸿翔, 朱洪波, 周海云, 等. 硅酸盐学报, 2020, 48(11), 1756.
6 Wu Z M, Shi C J, Khayat K H. Composites Part B, 2019, 174, 107021.
7 Huang Z Y, Wu Z. Highway Engineering, 2018, 43(2), 84(in Chinese).
黄政宇, 吴峥. 公路工程, 2018, 43(2), 84.
8 Jung-Jun P, Doo-Yeol Y, Gi-Joon P, et al. Materials, 2017, 10(2), 118.
9 Yoo D Y, Kang S T, Yoon Y S. Construction and Building Materials, 2014, 64, 67.
10 Song W M, Yin J. Materials, 2016, 9(8), 704.
11 Rambo D A S, Silva F D A, Filho R D T. Cement and Concrete Compo-sites, 2014, 54, 100.
12 Chi Y, Yin C R, Xu L H, et al. Journal of the Chinese Ceramic Society, 2021, 49(11), 2331(in Chinese).
池寅, 尹从儒, 徐礼华, 等. 硅酸盐学报, 2021, 49(11), 2331.
13 Okeh C A O, Begg D W, Barneett S J, et al. Construction and Building Materials, 2019, 202, 753.
14 Li L, Cao M L, Feng J Q. Journal of Basic Science and Engineering, 2018, 26(4), 843(in Chinese).
李黎, 曹明莉, 冯嘉琪. 应用基础与工程科学学报, 2018, 26(4), 843.
15 Zhang B M, Li J, Li X. Journal of Materials Engineering, 2014(7), 107(in Chinese).
张博明, 李嘉, 李煦. 材料工程, 2014(7), 107.
16 Wu K R, Li S J. Journal of Building Materials, 2005(6), 599(in Chinese).
吴科如, 李淑进. 建筑材料学报, 2005(6), 599.
17 Zhang X Z, Sun W, Zhang Q Q, et al. Journal of Southeast University(Natural Science Edition), 2008(1), 156(in Chinese).
张秀芝, 孙伟, 张倩倩, 等. 东南大学学报(自然科学版), 2008(1), 156.
18 Wei J Y, Liu H W, Zhang Y. Concrete, 2017(12), 51(in Chinese).
魏金源, 刘宏伟, 张勇. 混凝土, 2017(12), 51.
19 Li Y F, Wang H F, Syu J Y, et al. Materials, 2021, 14(19), 5881.
20 Xia D T, Zhu F, Fu M, et al. Concrete, 2020(11), 31(in Chinese).
夏冬桃, 朱峰, 付敏, 等. 混凝土, 2020(11), 31.
21 Rai B, Singh N K. Journal of Building Engineering, 2021, 44, 2352.
22 Yu R, Spiesz P, Brouwers H J H. Construction and Building Materials, 2014, 68, 158.
23 Ozyurt N, Mason T, Shah S P. Cement and Concrete Composites, 2007, 29(2), 70.
24 Alberti M G, Enfedaque A, Galvez J C. Cement and Concrete Compo-sites, 2017, 77, 29.
25 Ding Y N, Wang Q, Lin Y D. Acta Materiae Compositae Sinica, 2017, 34(8), 1853(in Chinese).
丁一宁, 王卿, 林宇栋. 复合材料学报, 2017, 34(8), 1853.
26 Wang Q X, Ding Y N, Zhang Y L, et al. Structural Concrete, 2020, 22(1), 503.
27 Murali G, Gayathri R, Ramkumar V R, et al. KSCE Journal of Civil Engineering, 2018, 22(1), 257.
28 Rahmani T, Kiani B, Shekarchi M, et al. Construction & Building Materials, 2012, 37, 360.
29 Chen X Y, Ding Y N, Azebedo C. Journal of Central South University of Technology, 2011, 18(5), 1677.
30 Li D, Ding Y N. Journal of Vibration and Shock, 2017, 36(2), 123(in Chinese).
李冬, 丁一宁. 振动与冲击, 2017, 36(2), 123.
31 Nia A A, Hedayatian M, Nili H, et al. International Journal of Impact Engineering, 2012, 46, 62.
32 Sun W W, Zhang Z Y, Dong H L, et al. Concrete, 2016(12), 86(in Chinese).
孙巍巍, 张正洋, 董浩林, 等. 混凝土, 2016(12), 86.
33 Ding Y N, Li D, Zhang Y L, et al. Construct Build Mater, 2017, 136, 495.
34 Wang L, Xu L H, Deng F Q, et al. Journal of Building Materials, 2020, 23(4), 865(in Chinese).
王力, 徐礼华, 邓方茜, 等. 建筑材料学报, 2020, 23(4), 865.
35 Wang C Q, Wu K R. Journal of Building Materials, 2005(3), 250(in Chinese).
王成启, 吴科如. 建筑材料学报, 2005(3), 250.
36 Xu L H, Deng F Q, Chi Y. Construction and Building Materials, 2017, 145, 619.