冷轧变形对Al-Cu-Mg合金的显微组织与力学性能的影响

doi:10.11896/cldb.21120197

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (16206KB)
Export: BibTeX | EndNote (RIS)

Abstract The effects of cold deformation on the microstructure and properties of hot rolled Al-Cu-Mg alloy were studied by optical microscopy, scanning electron microscopy, EBSD technology, transmission electron microscopy and a universal tensile testing machine. The microstructure observation results show that with increasing cold rolling deformation, the undissolved Al₂CuMg [Fe,Mn] phase and Al₂Cu [Fe,Mn] phase in the alloy are broken. There are many rod-like Al₂₀Cu₂Mn₃ phases in the matrix, and there are a large number of entanglement dislocations near the T phase, which have an obvious strengthening effect on the alloy. When the cold rolling deformation is 19%, the dislocation density reaches the maximum. At the same time, with the increase in cold rolling deformation, the texture content of S, R, Cube, Goss and Brass increases, and the texture content of 〈111〉〈110〉 decreases. The results of the mechanical property tests show that with increasing cold rolling deformation, the strength of the alloy increases, and the elongation remains at a high level. When the cold rolling deformation is 11%, the comprehensive mechanical properties of the alloy in the rolling direction are the best, with a tensile strength of 465.0 MPa, yield strength of 291.6 MPa and elongation of 19.0%. At this time, the transverse tensile strength of the alloy is 469.9 MPa, the yield strength is 318.0 MPa, and the elongation is 16.9%.

Key words： Al-Cu-Mg alloy cold rolling deformation microstructure mechanical property second phase

Published: 10 June 2023 Online: 2023-06-19

CLC number:

TG166.3

Fund:“Hundred Thousand Million” Engineering Science and Technology Major Special Project of Heilongjiang Province (2019ZX10A01, 2020ZX03A03).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Shuai
	GUO Erjun
	FENG Yicheng
	FU Jinlai
	MA Baoxia
	ZHAO Sicong
	WANG Lei

Cite this article:

WANG Shuai,GUO Erjun,FENG Yicheng, et al. Effect of Cold Rolling Deformation on Microstructure and Mechanical Properties of Al-Cu-Mg Alloy[J]. Materials Reports, 2023, 37(11): 21120197-7.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21120197 OR http://www.mater-rep.com/EN/Y2023/V37/I11/21120197

1 Huang G, Li Z H, Sun L M, et al. Rare Metals, 2020, 40(9),2523.
2 Du S, Zhang Y A, Yan L Z, et al. Rare Metals, 2020, 40(10),2937.
3 Chen Y, Liu Z, Bai S, et al.Journal of Materials Engineering and Performance, 2019, 28(6), 3590.
4 Zuiko I, Kaibyshev R. Materials Science and Engineering: A, 2017, 702,53.
5 Tong D L, Yi Y P, Huang S Q, et al.Materials Reports, 2020, 34(6),6100(in Chinese).
童灯亮, 易幼平, 黄始全, 等. 材料导报, 2020, 34(6), 6100.
6 Zhu Z Y, Tu H, Wu C J, et al.Materials Reports, 2021, 35(4),4129(in Chinese).
朱振宇, 涂浩, 吴长军, 等. 材料导报, 2021, 35(4),4129.
7 Zlaticanin B, Duric S, Jordovic B, et al. Materials Science and Technology, 2013, 20(1), 138.
8 Zhou Q, Wang J,Misra A, et al. International Journal of Plasticity, 2016, 87, 100.
9 Staszczyk A, Sawicki J, Adamczyk-Cieslak B. Materials (Basel), 2019, 12(24),4168.
10 Wang H, Yi Y, Huang S.Journal of Alloys and Compounds, 2016, 685,941.
11 Doppalapudi D, Venkatachalam P, Ramesh Kumar S, et al. Transactions of the Indian Institute of Metals, 2010, 63(1), 31.
12 Chen Z, Ren J, Yuan Z, et al.Materials Science and Engineering: A, 2020, 787, 139447.
13 Shi W N, Zhou H F, Zhang X F.Materials Science Forum, 2020, 990,3.
14 Wang S C,Starink M J. Acta Materialia, 2007, 55(3),933.
15 Zhang X, Hashimoto T, Lindsay J, et al.Corrosion Science, 2016, 108,85.
16 Wang K M.Light Metals, 1994(7),46 (in Chinese).
王奎民. 轻金属, 1994(7), 46.
17 Wang K M, Zhang Y Z.Light Alloy Fabrication Technology, 1996(10), 32(in Chinese).
王奎民,张玉洁. 轻合金加工技术, 1996(10),32.
18 Ning A L, Liu Z Y, Zeng S M. Transactions of Nonferrous Metals Society of China, 2006, 16(6), 1341.
19 Ning A L, Liu Z Y, Zeng S M, et al. Materials Reports, 2007(3),74 (in Chinese).
宁爱林, 刘志义, 曾苏民, 等. 材料导报, 2007(3),74.
20 Li C M, Zeng S M, Chen Z Q, et al.Computational Materials Science, 2014, 93,210.
21 Ma G F, Lu Z Y, He C L.Journal of Shenyang University(Natural Science), 2017, 29(6), 435(in Chinese).
马国峰, 鲁志颖, 贺春林. 沈阳大学学报(自然科学版), 2017, 29(6), 435.
22 Engler O, Hirsch J. Materials Science and Engineering: A, 2002, 336(1-2),249.
23 Zhou D Y. Texture, Microindentation and corrosion behavior of cold rolled AA6061 aluminum alloy. Ph. D. Thesis, Taiyuan University of Technology, China, 2018 (in Chinese).
周琱玉. 冷轧AA6061铝合金的织构、微米压痕与腐蚀性能研究. 博士学位论文,太原理工大学, 2018.