基于加工硬化率的新型轻质钢动态再结晶临界条件及变形机制研究

doi:10.11896/cldb.21050251

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (13457KB)
Export: BibTeX | EndNote (RIS)

Abstract In this work, the stress-strain curves of the experimental steel were obtained after isothermal compression deformation within the temperature 850—1 050 ℃ of and the strain rate of 0.01—5 s^-1 on Gleeble3500 thermal-mechanical simulator. The work hardening rate-strain curves, dynamic recrystallization critical stress and critical strain of the experimental steel were further obtained by data processing. The microstructures evolution and deformation mechanism of the experimental steel were analyzed by OM, TEM and EBSD. The results show that for the experimental steel, there is an obvious ‘secondary increase’ phenomenon of the flow stress, for the the dominant position is occupied again by work hardening as the strain increases at relatively low temperature and low strain rate. The peak stress, critical stress, peak strain and critical strain of the experimental steel show an increasing trend, as the deformation temperature decreases and the strain rate increases, and simultaneously, a new relationship model between them is obtained. The recrystallization grain size of the experimental steel increases with the increase of temperature and the decrease of strain rate, and the stacking fault energy (SFE) ranges from 181.1 mJ/m² to 237.4 mJ/m², which exhibits increasing trend with the increase of temperature under the deformation condition. It can be concluded that stacking fault energy is not the only factor affecting the deformation mechanism of the experimental steel because of the presence of the twins after hot deformation of the experimental steel. Dislocation slipping is the main deformation mechanism of the experimental steel.

Key words： lightweight steel isothermal compression work hardening rate dynamic recrystallization deformation mechanism

Published: 10 October 2022 Online: 2022-10-12

CLC number:

TG142.1

Fund:National Natural Science Foundation of China (51674004, 51805002)

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SUN Jian
	HUANG Zhenyi
	LI Jinghui
	WANG Ping
	WU Xuming

Cite this article:

SUN Jian,HUANG Zhenyi,LI Jinghui, et al. Study on the Critical Condition and Deformation Mechanism of Dynamic Recrystallization of Novel Lightweight Steel Based on the Work Hardening Rate[J]. Materials Reports, 2022, 36(19): 21050251-9.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21050251 OR http://www.mater-rep.com/EN/Y2022/V36/I19/21050251

1 Chen S, Rana R, Haldar A, et al. Progress in Materials Science, 2017, 89, 345.
2 Zambrano O A. Journal of Materials Science, 2017, 53(20), 14003.
3 Liu C Q, Peng Q C, Xue Z L,et al. Materials Reports A: Review Papers, 2019, 33(8), 2572(in Chinese).
刘春泉, 彭其春, 薛正良, 等. 材料导报:综述篇, 2019, 33(8), 2572.
4 Pierce D T, Field D M, Limmer K R, et al. Materials Science and Engineering: A, 2021,825,141785.
5 Zhang X F, Wu X J, Tang L Z, et al. Ordnance Material Science and Engineering, 2020, 43(5), 11(in Chinese).
章小峰, 武学俊, 唐立志, 等. 兵器材料科学与工程, 2020, 43(5), 11.
6 Xu C B, Ye C L, Zhao G, et al. Journal of Wuhan University of Science and Technology, 2003, 26(4), 334(in Chinese).
余驰斌, 叶传龙, 赵刚, 等. 武汉科技大学学报, 2003, 26(4), 334.
7 Cao J R, Liu Z D, Cheng S C. Acta Metallurgica Sinica, 2007, 43(1), 35(in Chinese).
曹金荣, 刘正东, 程世长. 金属学报, 2007, 43(1), 35.
8 Kim S I, Lee Y, Byon S M. Journal of Materials Processing Technology, 2003, 140, 84.
9 Li Z, Wang Y, Cheng X, et al. Materials Science and Engineering A, 2019, 772, 138700.
10 Ryan N D, Kocks U F. Solid State Phenomena, 1993, 35(36), 1.
11 Poliak E I, Jonas J J. Acta Materialia, 1996, 44(1), 127.
12 Wang Z T, Huo D, Yu X L. Transactions of Nonferrous Metals Society of China, 2018, 28(10), 1972(in Chinese).
王忠堂, 霍达, 于晓林. 中国有色金属学报, 2018, 28(10), 1972.
13 Ouyang D L, Lu S Q, Cui X, et al. Journal of Aeronautical Materials, 2010,30(2), 17(in Chinese).
欧阳德来, 鲁世强, 崔霞, 等. 航空材料学报, 2010, 30(2), 17.
14 Cai Y, Sun C Y, Wan L, et al. Acta Metallurgica Sinica, 2016, 52(9), 1123(in Chinese).
蔡赟, 孙朝阳, 万李, 等. 金属学报, 2016, 52(9), 1123.
15 Wang Z T, Deng Y G, Zhang S H. Transactions of Materials and Heat Treatment, 2014, 35(7), 193(in Chinese).
王忠堂, 邓永刚, 张士宏. 材料热处理学报, 2014, 35(7), 193.
16 Chen W, Guan Y P, Wang Z H. Materials Reports B:Research Papers, 2016, 30(11), 164(in Chinese).
陈微, 官英平, 王振华. 材料导报:研究篇, 2016, 30(11), 164.
17 Li Y P, Song R B, Wen E D, et al. Acta Metallurgica Sinica (English Letters), 2016, 29(5), 1.
18 Qin X M, Di H S, Chen L Q, et al. In: The 10th International Conference on Steel Rolling. Beijing, China, 2010, pp.154.
19 Pan X Y, Yang Y H, Ni K, et al. Chinese Journal of Materials Research, 2021, 35(5), 381(in Chinese).
潘晓宇, 杨银辉, 倪珂, 等. 材料研究学报, 2021, 35(5), 381.
20 Olson G B, Cohen M. Metallurgical and Materials Transactions A, 1976, 12, 1905.
21 Ma T, Gao J, Li H, et al. Metals, 2021, 11(2), 345.
22 Yoo J D, Park KT. Materials Science and Engineering A, 2008, 496, 417.
23 Saeed A A, Imlau J, Prahl U, et al. Metallurgical and Materials Transactions A, 2009, 40 (13), 3076.
24 Ishida K. Physica Status Solidi (A), 1976, 36 (2), 717.
25 Kaufman L. In: Proceedings of the fourth calphad meeting Workshop on computer-based coupling of thermochemical and phase diagram data. Maryland, 1977, pp. 89.
26 Curtze S, Kuokkala V T, Oikari A, et al. Acta Materialia, 2011, 59 (3), 1068.