INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
Effects of Quicklime-Sodium Carbonate Content and Slag Activity on Cracking Resistance of Alkali-activated Slag Mortar |
ZHAO Xiaowen1, ZHANG Jianmei1, CHEN Xudong2, JI Tao1,*
|
1 College of Civil Engineering, Fuzhou University, Fuzhou 350108, China 2 College of Civil and Transportation Engineering, Hohai University, Nanjing 210098, China |
|
|
Abstract Alkali-activated slag mortar was prepared using quicklime and sodium carbonate (the molar ratio of 1∶1) as activators. The effect of quicklime and sodium carbonate content (namely Na2O content, 2.5%, 4.5%, 6.5% and 8.5%) and slag activity (depending on the chemical composition and fineness, etc.) on the splitting tensile strength, strain of interior steel ring, circumferential tensile stress and cracking resistance of alkali-activated slag mortars (AM) was investigated. It is found that the cracking resistance of Portland cement mortars is better than that of AM; with the increase of Na2O content, the splitting tensile strength and cracking resistance increase firstly and then decrease. When the Na2O content is 6.5%, the cracking resistance is the best; with the increase of slag activity, the splitting tensile strength of AM increases, but its cracking resistance decreases.
|
Published: 25 August 2022
Online: 2022-08-29
|
|
Fund:National Natural Science Foundation of China (51878179) and Natural Science Foundation of Fujian Province (2021J02021). |
|
|
1 Fernandez J A, Palomo J G, Puertas F. Cement and Concrete Research, 1999, 29(8), 1313. 2 Collins F, Sanjayan J G. Cement and Concrete Research, 2000, 30(5), 791. 3 Palacios M, Puertas F. Cement and Concrete Research, 2007, 37(5), 691. 4 Xin D S. Study on preparation and mechanism of one-part alkali-activated slag cementitious material with quicklime, slaked lime and sodium carbonate. Master's Thesis, Fuzhou University, China, 2018(in Chinese). 辛东升. 单组份生/熟石灰与碳酸钠激发矿渣胶凝材料的制备及其机理研究.硕士学位论文, 福州大学, 2018. 5 Wang J X, Lyu X J, Wang L Y, et al. Journal of Cleaner Production, 2018, 171, 622. 6 Xia J. Study on mix proportion design of alkali slag concrete. Master's Thesis, Chongqing University, China, 2013(in Chinese). 夏婧. 碱矿渣混凝土配合比设计研究. 硕士学位论文, 重庆大学, 2013. 7 Wu P, Lyu X J, Hu S G, et al. Silicate Bulletin, 2014, 33(10), 2572(in Chinese). 吴蓬, 吕宪俊, 胡术刚,等. 硅酸盐通报, 2014, 33(10), 2572. 8 Chen K J. Study on autogenous shrinkage and crack resistance of alkali-activated slag ceramsite concrete. Master's Thesis, Fuzhou University, China, 2016(in Chinese). 程可佳. 碱矿渣陶粒混凝土的自收缩及抗裂性能研究.硕士学位论文, 福州大学, 2016. 9 Ji T, Chen C Y, Chen Y Y, et al. Construction and Building Materials, 2013, 44, 726. 10 Zhang B B. Early age tensile creep and anti-cracking performance evaluation method of steel fiber reinforced ceramsite concrete. Master's Thesis, Fuzhou University, China, 2014(in Chinese). 张彬彬. 钢纤维陶粒混凝土早期拉伸徐变及抗裂性能评价方法. 硕士学位论文, 福州大学, 2014. 11 Zhuang Y Z, Chen C Y, Ji T. Construction and Building Materials, 2013, 46(8), 13. 12 Zhang J, Shi C J, Zhang Z H. Construction and Building Materials, 2021, 269, 121258. 13 Chen W W, Li B, Wang J, et al. Cement and Concrete Research, 2021, 141, 106322. 14 Su Y, Wang Z H, Wang Y B, et al. Journal of Wuhan University of Technology, 2015, 37(11),32(in Chinese). 苏英, 王志虎, 王迎斌,等. 武汉理工大学学报, 2015, 37(11), 32. 15 He X Y, Zhang C, Su Y, et al. Concrete, 2019(9),83(in Chinese). 贺行洋, 张晨, 苏英, 等. 混凝土, 2019(9),83. |
|
|
|