集装箱用高强度耐候钢的开发及研究现状

doi:10.11896/cldb.20090318

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (3996KB)
Export: BibTeX | EndNote (RIS)

Abstract Weathering steel reacted with air and rainwater in natural environment, and then an anticorrosion protective layer was formed on its surface. Thus the weathering steel had higher corrosion resistance than ordinary carbon steel. Therefore, it has been widely used on oil drilling, containers, railway vehicles and other structures with adverse and corrosive working condition. In recent years, with the China-Europe train, China-Asian train and other lines rapidly developing, and the support of state policies such as One belt, One road strategy and Expressway Entrance Control, railway container transport has been expanding in China. Light weight and thinning of container will be the main development direction in the future. As a railway container material, weathering steel, especially high strength weathering steel with yield strength of 700 MPa, can reduce the weight of container and realize the thinning of container, so it will be widely used. The development of weathering steel in foreign countries started earlier and had been widely applied. Although the weathering steel in China has been applied in some places, the application progress is still slow. It is necessary to carry out the research and development of weathering steel with high strength and high corrosion resistance to meet the application requirements of railway containers.
At present, domestic and foreign scholars have mainly focused on the corrosion resistance and strengthening and toughening mechanism of weathering steel with different chemical compositions. In this paper, the corrosion resistance mechanism, the mechanism of strength and plasticity and the weldability of weathering steel were reviewed. Considering the strength, toughness, weldability, weather resistance of steel and the research and development experiences of weathering steel, the chemical composition design and the control strategies of deformation, temperature and cooling schedules of ultra-high strength weathering steel were put forward. It was determined that the microstructure of high strength weathering steel below 700 MPa was mainly ferrite+pearlite or granular bainite, while the microstructure of 700 MPa grade high strength weathering steel was fine acicular ferrite or granular bainite. The performance requirements can be met by combining multiple strengthening mechanism such as solution strengthening, fine grain strengthening, precipitation strengthening and phase transformation strengthening. The paper provided refe-rence and basis for the research and design of high strength weathering steel for containers in the future.

Key words： weathering steel corrosion resistance composition design high strength weldability

Published: 25 February 2022 Online: 2022-02-28

CLC number:

TG142.1

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HE Guoning
	JIANG Bo
	HE Bo
	HU Xuewen
	LIU Yazheng

Cite this article:

HE Guoning,JIANG Bo,HE Bo, et al. Development and Research Status of High Strength Weathering Steel for Container[J]. Materials Reports, 2022, 36(4): 20090318-9.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20090318 OR http://www.mater-rep.com/EN/Y2022/V36/I4/20090318

1 Wang Z K.Shanxi Architecture, 2018, 44(10), 98(in Chinese).
王志坤. 山西建筑, 2018, 44(10), 98.
2 Ye Y J, Chen S W. In: Conference Record of the 2015 Steel Construction Industry Conference. Jinan, 2015, pp. 422(in Chinese).
叶永健, 陈素文. 2015中国钢结构行业大会. 济南, 2015, pp. 422.
3 Chen M Q, Chen Y, Lu Y Q. Geographical Research, 2018, 37(2), 404(in Chinese).
陆梦秋, 陈娱, 陆玉麒.地理研究, 2018, 37(2), 404.
4 Xu Q, He T J, Mao B H.Journal of Transportation Systems Engineering and Information Technology, 2018, 18(6), 198(in Chinese).
许奇, 何天健, 毛保华.交通运输系统工程与信息, 2018, 18(6), 198.
5 Larrabee C P.Corrosion Engineering, 2014, 3(8), 259.
6 Wang Z B. High strength low alloy steel, Atomic Energy Press, China, 1996(in Chinese).
王祖滨. 低合金高强度钢, 原子能出版社, 1996.
7 Concli F, Maccioni L. Procedia Structural Integrity, 2019, 24, 738.
8 Hu X Y. The effect of alloying and hot-rolling process on the microstructures and mechanical properties of low-carbon bainitic weathering steels. Master's Thesis, Northeastern University, China, 2011(in Chinese).
胡霄雨. 合金元素和轧制工艺对低碳贝氏体耐候钢组织和力学性能影响. 硕士学位论文,东北大学, 2011.
9 Borko K, Hadzima B, Jacková M N. Procedia Engineering, 2017, 192, 58.
10 Kurc-Lisiecka A, Lisiecki A. Materiali in Tehnologije, 2017, 51(2), 199.
11 Cvetkovski S T. Key Engineering Materials, 2017, 750, 45.
12 Chen F H, Gao Z F, Huang W, et al. Shanghai Metals, 2017, 39(1), 70(in Chinese).
陈付红, 高真凤, 黄维, 等.上海金属, 2017, 39(1), 70.
13 Wang D C, Guo L. Science Technology of Baotou Steel Group Corporation, 1993(3), 59(in Chinese).
王栋材, 郭亮.包钢科技, 1993(3), 59.
14 Lu J X, Li A B, Li Z G, et al. China Metallurgy, 2004(12), 23(in Chinese).
陆匠心, 李爱柏, 李自刚, 等.中国冶金, 2004(12), 23.
15 Chen K L. World Bridges, 2020, 48(1), 47(in Chinese).
陈开利.世界桥梁, 2020, 48(1), 47.
16 Song R B, Wen X L, Zhang Y K. Materials Science and Technology, 2011, 19(3), 106(in Chinese).
宋仁伯, 文新理, 张永坤.材料科学与工艺, 2011, 19(3), 106.
17 Chen Q J, Kang Y L, Su S H, et al. Iron Steel, 2005, 40(7), 60(in Chinese).
陈庆军, 康永林, 苏世怀, 等.钢铁, 2005, 40(7), 60.
18 Li H Y, Kang Y L, Wang J J, et al. Journal of Wuhan University of Science and Technology, 2010, 33(1), 47(in Chinese).
李慧远, 康永林, 王建景, 等.武汉科技大学学报, 2010, 33(1), 47.
19 Zhao P L, Sun X J, Tang H S, et al. Special Steel, 2012, 33(1), 46(in Chinese).
赵培林, 孙新军, 汤化胜, 等.特殊钢, 2012, 33(1), 46.
20 Gao J X. Study on microstructure and properties of ultra-high strength weathering steel produced by TSCR. Ph.D. Thesis, South China University of Technology, China, 2012(in Chinese).
高吉祥. 薄板坯连铸连轧超高强耐候钢的组织性能研究. 博士学位论文, 华南理工大学, 2012.
21 Wang B. Effects and mechanism of Mn, Cr and V-N alloying in low carbon weathering steel. Ph.D. Thesis, Northeastern University, China, 2008(in Chinese).
王博. 锰铬及钒氮合金化在低碳耐候钢中的作用机理. 博士学位论文, 东北大学, 2008.
22 Qu P. China Metallurgy, 2009, 19(6), 19(in Chinese).
曲鹏.中国冶金, 2009, 19(6), 19.
24 Chen S G, Wang L, Li X L, et al. China Metallurgy, 2016, 26(3), 17(in Chinese).
陈守关, 王莉, 李晓林, 等.中国冶金, 2016, 26(3), 17.
25 Liu X C, Zhang Z Z, Li W Y, et al. Steel Rolling, 2019, 36(4), 31(in Chinese).
刘晓翠, 张转转, 李文远, 等.轧钢, 2019, 36(4), 31.
25 Okada H, Hosoi Y, Yukawa K I, et al. Tetsu-to-Hagane, 2010, 55(5), 355.
26 Kihira H, Ito S, Murata T. Corrosion Science, 1990, 31, 383.
27 Misawa T, Asami K, Hashimoto K, et al. Corrosion Science, 1974, 14(4), 279.
28 Keiser J T, Brown C W, Heidersbach R H.Corrosion Science, 1983, 23(3), 251.
29 Yamashita M, Miyuki H, Matsuda Y, et al. Cheminform, 1994, 25(19), 283.
30 Yamashita M, Nagano H, Misawa T, et al. ISIJ International, 1998, 38(3), 285.
31 Zhang Q C. Materials Review, 2004, 18(Z1), 169(in Chinese).
张全成.材料导报, 2004, 18(专辑3), 169.
32 Stratmann M, Bohnenkamp K, Ramchandran T.Corrosion Science, 1987, 27(9), 905.
33 Cao T H. Copper enrichment behavior of steel with copper addition during oxidation process. Master's Thesis, University of Science and Technology Liaoning, China, 2015(in Chinese).
曹桐赫. 含铜钢氧化过程中铜的富集行为研究. 硕士学位论文,辽宁科技大学,2015.
34 Kihira H, Ito S, Murata T.Corrosion Science, 1990, 31, 383.
35 Zhang Q C, Wu J S, Yang X S, et al. Materials Protection, 2002, 35(3), 21(in Chinese).
张全成, 吴建生, 杨晓芳, 等.材料保护, 2002, 35(3), 21.
36 Hao L, Zhang S, Dong J, et al. Corrosion Science, 2011, 53(12), 4187.
37 Diaz I, Cano H, Fuente D D L, et al. Corrosion Science, 2013, 76(2), 348.
38 Hao X C, Xiao K, Zhang H Q, et al. Materials Protection, 2009, 42(1), 21(in Chinese).
郝献超, 肖葵, 张汉青, 等.材料保护, 2009, 42(1), 21.
39 Tian J, Zhang K, Wang J.Materials Protection, 2019, 52(11), 33(in Chinese).
田骏, 张昆, 王金.材料保护, 2019, 52(11), 33.
40 Wang Y, Zeng J.Surface & Coatings Technology, 2014, 245, 55.
41 Wang Y J.Locomotive Rolling Stock Technology, 1992(1), 11(in Chinese).
王英杰.机车车辆工艺, 1992(1), 11.
42 Liu J R, Zhang W L, Liu Z S.Research on Iron and Steel, 2010, 38(4), 17(in Chinese).
刘建容, 张万灵, 刘正生.钢铁研究, 2010, 38(4), 17.
43 Fajardo S, Llorente I, Jimenez J A, et al. Corrosion Science, 2019, 154, 246.
44 Moon K M, Kim D A, Kim Y H, et al. International Journal of Modern Physics B, 2018, 32(19),1840083.
45 Liu X C, Zhang Z Z, Liu K, et al. Steel Rolling, 2019, 36(6), 17(in Chinese).
刘晓翠, 张转转, 刘锟, 等.轧钢, 2019, 36(6), 17.
46 Li Y, Shao M R, Zhao Z W. Corrosion and Protection, 2019, 40(9), 627(in Chinese).
李岩, 邵明蕊, 赵增武.腐蚀与防护, 2019, 40(9), 627.
47 Liu Q C. Effect of vanadium on the high strength steels used for railway freight cars. Ph.D. Thesis, Kunming University of Science and Techno-logy, China, 2016(in Chinese).
刘庆春. 钒在铁路货车用高强度钢中的作用研究. 博士学位论文, 昆明理工大学, 2016.
48 Chi X B.Bengang Technology, 1995(5), 58(in Chinese).
迟秀斌.本钢技术, 1995(5), 58.
49 Townsend H E.Corrosion, 2001, 57(6), 497.
50 Legault R A, Mori S, Leckie H P.Corrosion, 1973, 29(5), 169.
51 Qing J S, Shen H F, Liu M. Iron Steel, 2017, 52(5), 87(in Chinese).
卿家胜, 沈厚发, 刘明.钢铁, 2017, 52(5), 87.
52 Zhang H M, Liu X H, Wang G D. Journal of Iron and Steel Research, 2001, 13(1), 36(in Chinese).
张红梅, 刘相华, 王国栋.钢铁研究学报, 2001, 13(1), 36.
53 Wang J F, Wang Z G, Wang X D, et al. Scripta Materialia, 2017, 129, 25.