METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
The High Frequency Induction Welding Technology of 316 Austenitic Stainless Steel with 0.3 mm Thickness |
WANG Chao1, XIE Zhixiong1, LUO Ping1, CHEN Qi1, XIAO Shuguang1, DONG Shijie1,2, XIE Jianying3
|
1 School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China 2 Hubei University of Economics,Wuhan 430205, China 3 Wuhan Borkin New Materials Technology Co., Ltd, Wuhan 430058, China |
|
|
Abstract Ahigh-speed high-frequency induction welding technology was used to weld a 316 austenitic stainless steel pipe with a wall thickness of 0.3 mm, and themacroscopic morphology, weld structure and mechanical properties of welded pipe joints under different high-frequency induction welding parameters were studied. The results show that in order to ensure the good weld formability of thin-walled 316 austenitic stainless steel under high-frequency induction welding conditions, the burrs formed on both sides of the weld must be continuous and consistent, and the heat input and extrusion must match, when the heat input increases, the amount of extrusion should decrease, and when the amount of extrusion increases, the heat input should decrease. When the welding heat input is 49.5 KJ/m and the extrusion amount is 0.36mm, the macroscopic surface of the joint is well formed and the grains in the weld zone are fine. The microstructure of the weld is dominated by austenite and δ-ferrite, and the weld hardness can reach more than 300HV, which is significantly increased compared with the base metal matrix hardness (236HV), which is the result of the refinement of weld grains.
|
Published: 25 November 2021
Online: 2021-12-13
|
|
Fund:National Natural Science Foundation of China (51771071). |
About author: Chao Wangreceived his B.E. degree from Shenyang University in June 2018. He is currently a postgraduate in the School of Materials and Chemical Engineering,Hubei University of Technology .He is under the supervision of Prof. Shijie Dong and Ph.D. Zhixiong Xie and Ph.D. Ping Luo.His research interest is the high frequency induction welding technology of thick 316 austenitic stainless steel. Zhixiong Xiereceived his Ph.D. degree from Shanghai Jiaotong University in 2012.He is the vice director of Department of Material Forming and Control Enginee-ring,Hubei University of Technology.He is a project leader of National Natural Science Foundation of Hubei Province and participated in several research projects of the National Natural Science Foundation of China.His researches focus on the preparation,microstructure and properties of high strength and high conductivity copper alloys,and the hydrogen generation with Al-water splitting reaction,and the high frequency induction welding of ultra-thin titanium tube and stainless steel tube. |
|
|
1 Kurgan N, Varol R. Powder Technology, 2010, 201(3), 242. 2 Rosso M, Grande M A. Journal of Achievements in Materials & Manufacturing Engineering, 2007, 21(2), 97 3 Wang F, Young B, Gardner L. Journal of Constructional Steel Research, 2020, 170, 105942. 4 Gardner L. Thin-Walled Structures, 2019, 141, 208. 5 Hidiroglu M, Serce O, Karabulut H, et al. The Eurasia Proceedings of Science Technology Engineering and Mathematics, 2018(4), 263. 6 Saha S, Mukherjee M, Pal T K. Journal of Materials Engineering & Performance, 2015, 24(3), 1125. 7 Meng X, Qin G, Bai X, et al. Welding Journal, 2016, 95(9), 331S. 8 Zhang Z S, Ning D J. Welding Technology, 1990(5), 11(in Chinese). 张则甡, 宁道俊. 焊接技术, 1990 (5), 11. 9 T U, E M. Journal of Material Science & Engineering, 2017, 6(2), 1. 10 Shi C h. Welded Pipe and Tube, 2017, 40(12), 40(in Chinese). 施春华. 焊管, 2017, 40(12), 40. 11 Zhang W, Zhao G, Fu Q. Materials Science and Engineering: A, 2018, 736, 276. 12 Hu S L. Steel Pipe, 2016, 45(4), 1(in Chinese). 胡松林. 钢管, 2016, 45(4), 1. 13 Feng D K, Tian D J. Welded Pipe and Tube, 2012, 35(2), 30(in Chinese). 冯大奎, 田道建. 焊管, 2012, 35(2), 30. 14 Bi Z Y, Yan P L, Yu H, et al. Welded Pipe and Tube, 2016, 39(8), 1(in Chinese). 毕宗岳, 严培林, 余晗, 等. 焊管, 2016, 39(8), 1. 15 Menggen B G, Ai B Q, Wang Q Y, et al. Welding & Joining, 2019(8), 57(in Chinese). 孟根巴根, 艾兵权, 王秋雨, 等. 焊接, 2019(8), 57. 16 Li D D, Yu T Y, Zeng Q J, et al. Welded Pipe and Tube, 2002 (5), 12(in Chinese). 李大东, 余腾义, 曾庆江, 等. 焊管, 2002(5), 12. 17 Kim D, Kim T, Park Y, et al. Welding Journal New York, 2007, 86(3), 71. 18 He J Y, Li Z Q, Xie J Y, et al. Welding Technology, 2009, 38(4), 51(in Chinese). 贺继有, 李志强, 解剑英, 等. 焊接技术, 2009, 38(4), 51. 19 Huang Y Y. Steel Pipe, 2000(6), 31(in Chinese). 黄友阳. 钢管, 2000 (6), 31. 20 Liu J F, Liu K W, Chen J, et al. Sichuan Metallurgy, 2013, 35(4), 59(in Chinese). 刘建芳, 刘科伟, 陈建, 等. 四川冶金, 2013, 35(4), 59. 21 Jie S Q. Welded Pipe and Tube, 2003(4), 47(in Chinese). 介升旗. 焊管, 2003(4), 47. 22 He F, Qu J S, Zhang D Y, et al. Hot Working Technology, 2010, 39(23), 179(in Chinese). 何芬, 屈金山, 张德远, 等. 热加工工艺, 2010, 39(23), 179. 23 John C L, Damian J K,Welding metallurgy and weldability of stainless steels, New Jersey: John Wiley & Sons, USA, 2005. 24 Folkhard E. Welding metallurgy of stainless steels, Springer Science & Business Media, GER, 2012. |
|
|
|