Materials Reports 2021, Vol. 35 Issue (Z1): 279-283 |
INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
Effect of Particle Size of Si-Mn Slag on Hydraulic Mechanism and Mechanical Property in Composite Cementitious System |
ZHOU Xiang1,2, ZHAO Huatang2,3, LI Liang1,2, DU Lang1,2, ZHOU Shuangfu1,2, SHAO Zhao1,2, ZHANG Xiaomin1,2
|
1 Chengdu Institute of Products Quality Inspection Co.,Ltd., Chengdu 610100, China 2 National Center for Building Material Quality Supervision and Inspection(Sichuan), Chengdu 610100, China 3 Sichuan Institute of Product Quality Supervision and Inspection, Chengdu 610100, China |
|
|
Abstract To achieve the high efficient utilization of Si-Mn slag, a Si-Mn slag powder was classified into three fractions by an air classifier, with D50=6.9 μm, 17.9 μm, 56.4 μm, respectively. The effect of size fraction of Si-Mn slag on hydraulic activity and physical property in composite cementitious system were investigated by isothermal calorimeter(TAM air), X-ray diffraction (XRD), mercury intrusion porosimeter(MIP), scanning electron micorscope and energy dispersive X-ray spectrometer(SEM-EDS). The test results indicated that the early hydration reaction(30 min) of free lime, aluminate and C3S phase were promoted by all size fractions of Si-Mn slag from nucleation induction. The intensity peaks of Ca(OH)2 and clinker decreased dramatically with the decrease of particle size in the late hydration. The blended cement paste with finer Si-Mn slag resulted in a decrease in the most probable pore size and total porosity than that of the one with coarser Si-Mn slag. The SEM-EDS results further demonstrated that the hardened blended cement paste containing fine Si-Mn slag powder produced a denser microstructure because more C-S (Al, Mg)-H gels hydration products with low calcium were produced. It was noted that the strength could surpass the technical index of 42.5 grade cement in GB 175 standard when the content of Si-Mn slag powder with D50=6.9 μm and 17.9 μm was reached up to 30%. Thus, these fractions were strongly recommended to serve as mineral admixtures in blended cement production or concrete making.
|
Published: 16 July 2021
|
|
About author:: Xiang Zhou received his master degree in Southwest University of Science and Technology in 2017. He is an engineer in Chengdu Institute of Products Quality Inspection Co., Ltd. His research interests are inspection of building materials products, comprehensive utilization of solid waste and advanced building materials.Huatang Zhao received his master degree in physical chemistry from the Sichuan University in 1989. He is a senior engineer in Sichuan Institute of Product Quality Supervision and Inspection. His research interests are inspection of building materials products, comprehensive utilization of solid waste and energy conservation in building. |
|
|
1 吴中伟. 建筑技术, 1999, 30(3), 161. 2 张同生. 水泥熟料与辅助性胶凝材料的优化匹配. 博士学位论文,华南理工大学, 2012. 3 董方园, 郑山锁, 宋明辰, 等. 材料导报:综述篇, 2018, 32(1), 163. 4 Moisés Frías, Rodríguez C. Cement and Concrete Composites, 2008, 30(3), 212. 5 Péra J, Ambroise J, Chabannet M. Cement and Concrete Research, 1999, 29(2), 177. 6 陈平, 王一靓, 刘婷, 等. 材料导报, 2010, 24(专辑15), 448. 7 王一靓, 陈平, 刘婷, 等. 混凝土, 2010(5), 64. 8 Frias M, De Rojas M I, Santamaria J, et al. Cement and Concrete Research, 2006, 36(3), 491. 9 Nath S K, Kumar S. Construction and Building Materials, 2016, 125, 127. 10 Allahverdi A, Ahmadnezhad S. Powder Technology, 2014, 251, 42. 11 Patil A V, Pande A M. Advanced Materials Research, 2011, 255-260, 3258. 12 范春平, 倪文, 杨慧芬, 等. 硅酸盐通报, 2007, 26(3), 541. 13 卢忠远. 微纳粉体对水泥物理力学性能的影响及机理研究, 博士学位论文,四川大学, 2005. 14 Chindaprasirt P, Jaturapitakkul C, Sinsiri T. Construction and Building Materials, 2007, 21, 1536. 15 何真, 王磊, 邵一心, 等. 建筑材料学报, 2011, 14(3), 298. 16 牛全林, 冯乃谦, 杨静. 建筑材料学报, 2002, 32(1), 89. 17 周祥, 李玉香, 郑召, 等. 混凝土与水泥制品, 2017(1), 6. 18 苏英, 卢敏, 贺行洋, 等. 混凝土, 2019(8), 105. |
|
|
|