| Dispersibility of Silica-loaded Antioxidant in Natural Rubber and Its Anti-aging Function |
| XIONG Ya1, JIANG Meng1, LI Yihang1, WU Jiangbing1, YANG Hang1, XIONG Yuzhu1,2
|
1 College of Materials and Metallurgy, Guizhou University,Guiyang 550025, China
2 Guizhou Province Engineering Laboratory for Rubber Composites, Guizhou University, Guiyang 550025, China |
|
|
|
|
Abstract Antioxidant 4-[(4,6-dioctyl-1,3,5-triazine-2-yl) amino]-2,6-di-tert-butylphenol (antioxidant 565) was loaded on the surface of SiO2(SiO2-565) or SiO2 modified by NDZ-311w (SiO2-N-565) to prepare silica-loaded antioxidant/natural rubber composites. In addition, the disper-sibility of anti-aging SiO2 in natural rubber matrix and its effect on thermal-oxidative aging resistance of natural rubber composites were also stu-died. The results showed that the silica modified by NDZ-311w was evenly dispersed in the rubber matrix, and the aging resistance of natural rubber increased significantly. When the thermal oxidative aging time was three days, the change rate of elongation at break and tensile strength of SiO2-N-565/NR were 44.36% and 48.26%, respectively, which was much lower than that of unmodified rubber (77.51%, 84.35%).
|
|
Published: 23 March 2021
|
|
|
| Fund:Natural Science Foundation of China (51663003), Science and Technology Project of Guizhou Province (20192166). |
About author:: Ya Xiong, master degree candidate of Guizhou University, the main research direction is the structure and properties of polymer compo-sites.
Yuzhu Xiong, Ph.D, graduated from Sichuan University, professor, doctoral supervisor, the main research direction is structure and properties of polymer compo-sites. |
|
|
1 Zhong X O, Ismail H, Bakar A A. Polymer Testing,2013,32(4),625.
2 Lopez J F, Perez L D, Lopez B L. Journal of Applied Polymer Science,2011,122(3),2130.
3 Liu Q Z, Zhao H G, Hu H H, et al. Synthetic Rubber Industry,2014,37(2),144(in Chinese).
刘全章,赵洪国,胡海华,等.合成橡胶工业,2014,37(2),144.
4 Lu X F, Hao Z, Sheng X, et al. Polymer Materials Science & Enginee-ring,2017(2),72(in Chinese).
鲁学峰,郝智,盛翔,等.高分子材料科学与工程,2017(2),72.
5 Yin Q Y, Wang L T, Cao X J, et al. Polymer Materials Science & Engineering,2017(2),171(in Chinese).
尹启彦,王丽婷,曹喜娟,等.高分子材料科学与工程,2017(2),171.
6 Lei H X, Weng G S, Huang G S. Synthetic Rubber Industry,2012,35(5),366(in Chinese).
雷航鑫,翁更生,黄光速.合成橡胶工业,2012,35(5),366.
7 Gao X W, Meng X F, Wang H T, et al. Polymer Degradation and Stabi-lity,2008,93(8),1467.
8 Li F. Preparation of antioxidant GM immobilized on nanosilica and its application in natural rubber. Master's Thesis, South China University of Technology, China,2014(in Chinese).
李峰.纳米二氧化硅固载抗氧剂GM的制备及其在天然橡胶中的应用研究.硕士学位论文,华南理工大学,2014.
9 Liauw C M, Allen N S, Edge M, et al. Polymer Degradation & Stability,2001,74(1),159.
10 Hu C, Chen W H, Li T, et al. Colloids and Surfaces A,2018,551,65.
11 Cai Y, Li J, Yi L, et al. Applied Surface Science,2018,450,102.
12 He C Z, Peng Z, She X D, et al. Synthetic Rubber Industry,2011,34(2),99(in Chinese).
何灿忠,彭政,佘晓东,等.合成橡胶工业,2011,34(2),99.
13 Lyu M Z, Yang Z M, Luo Y Y, et al. Synthetic Materials Aging and Application,2014,43(6),1(in Chinese).
吕明哲,杨子明,罗勇悦,等.合成材料老化与应用,2014,43(6),1. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2021, Vol. 35 