Metals and Metal Matrix Composites |
|
|
|
|
|
Research Progress on Surface Coating of Metal/Ceramic Powder Suitable for 3D Printing |
WANG Hang1, GUO Zi'ao1, YI Denghao1, FENG Yinghao1, ZHANG Jingfang1, LI Xiaofeng1,2,*, LIU Bin1,*, BAI Peikang1
|
1 School of Materials Science and Engineering, North University of China, Taiyuan 030051, China 2 Henan Huanghe Whirlwind Co., Ltd., Changge 461500, China |
|
|
Abstract Since its appearance, 3D printing technology has received widespread attention. The molding material is mainly powder, and the properties of the powder material have a great influence on the formed parts. In the process of powder 3D printing, due to problems such as poor fluidity of the powder and large shrinkage coefficient, it is easy to cause defects such as uneven microstructure, cracking, holes, etc. in the process of 3D printing, which are related to 3D printed powder materials. The performance is very closely related. Since the powder material required for 3D printing has the characteristics of large specific surface area, stong adsorption agglomeration effect, and large surface activity, many printing powder materials are prone to dispersion unevenness in 3D printing if they are not pretreated, which is suitable for printing. The quality of the parts will cause a significant deterioration. Modification of the surface of the printed powder can effectively improve the printing process performance of the 3D printed material, and also has a good overall performance improvement for the 3D printed structural parts. There are many methods for common powder modification methods, The surface coating of the powder makes the material have good wettability, fluidity, corrosion resistance, etc., and can also make the material “shell” and “core” performance to better play the material potential. For the surface of the metal or ceramic powder used in 3D printing technology, the surface of the powder can be coated as needed during the preparation of the powder material, so that the excellent performance of the material can be better exhibited. This paper combines the main metal/ceramic powder coating methods, and makes an inductive analysis of the current metal/ceramic-based powder coating conventional methods for 3D printing, summarizing the ceramic/metal/polymer surface materials in the 3D printing process. Coa-ting metal or ceramic-based powder materials provides reference and inspiration for further exploration of metal/ceramic powder preparation and development for 3D printing.
|
Published: 17 November 2020
|
|
Fund:This work was financially supported by the National Natural Science Foundation of China (51804280), the Natural Science Foundation of Shanxi Province, China(201701D221086,201801D221146),the Major Science and Technology Projects of Shanxi Province, China (20181101009),Department of Scientific and Technologial Innovation Programs of Higher Education Institutions in Shanxi(201802076),Returned Overseas Students Research Funding Project of Shanxi Pro-vince (2017-095),International Cooperation Project of Shanxi Province(201603D421024), the Support Program for Young Academic Leaders of North University of China (QX201802). |
About author:: Hang Wang received his B.E. degree in material for-ming and control engineering from Zhengzhou Institute of Science and Technology for the Nationalities in 2018. He is currently pursuing master degree at the School of Material Science and Engineering, North University of China under the supervision of A/Prof. Li Xiaofeng. His research has focused on the preparation of cemented carbide material by selective laser melting (SLM). Xiaofeng Li received his B.E. degree in material from Central South University in 2009 and received his Ph.D. degree in state key laboratory for powder metallurgy from Central South University, in 2016. He is currently a associate professor and master's supervisor in North University of China. His research interests are powder me-tallurgy, additive manufacturing, design and development of metal matrix composites. |
|
|
[1] |
Liu Wen, Xu Shuqiong. In: Proceedings of the International Conference on Advanced Material Engineering. Guangzhou, China, 2015, pp. 506.
|
[2] |
Ma W L, Tao F H, Jia C Z, et al. Applied Mechanics & Materials, 2014, 644(60), 650.
|
[3] |
Duda T, Raghavan L V. IFAC-Papers on Line, 2016, 49(29), 103.
|
[4] |
Xin W, Man J, Zhou Z, et al. Composites Part B Engineering, 2017, 110(442), 58.
|
[5] |
Ngo T D, Kashani A, Imbalzano G, et al. Composites Part B Enginee-ring, 2018, 143, 347.
|
[6] |
Chen Y H, Zhou K G, Li X B. China's Manganese Industry, 2006, 24(3),36 (in Chinese).
|
|
陈一恒, 周康根, 李晓波.中国锰业, 2006, 24(3), 36.
|
[7] |
Liu Z, Huang H, Deng S, et al. Inorganic Chemicals Industry, 2006,38(1),13.
|
[8] |
Zhang S X, Li J B, Zhang B, et al. Chemistry Bulletin, 2001, 64(2),71 (in Chinese).
|
|
张淑霞, 李建保, 张波,等. 化学通报, 2001, 64(2),71.
|
[9] |
Xu B S, Wang H D, Dong S Y, et al. Jiangsu Machine Building & Automation, 2004, 25(5), 8.
|
[10] |
Jin Y Z, Wu W. Chinese Journal of Rare Metals, 2004, 28(1), 262 (in Chinese).
|
|
金永中, 吴卫.稀有金属, 2004, 28(1), 262.
|
[11] |
Liu D F, Zheng Y Y, Huang H M. Journal of Materials Engineering, 2008, 10, 342.
|
[12] |
Meier H, Haberland C. Materialwissenschaft Und Werkstofftechnik, 2010, 39(9), 665.
|
[13] |
Gibsn I, Shi D. Rapid Prototyping Journal, 1997, 3(4), 129.
|
[14] |
Vilar R. Materials Science Forum, 1999, 301(24), 12.
|
[15] |
Lemke J N, Simonelli M, Garibaldi M, et al. Journal of Alloys & Compounds, 2017, 722(293), 301.
|
[16] |
Garibaldi M, Ashcroft I, Simonelli M, et al. Acta Materialia, 2016, 110(207), 16.
|
[17] |
Garibaldi M, Ashcroft I, Lemke J N, et al. Scripta Materialia, 2018, 142(1), 121.
|
[18] |
Kang N, El M M, Guittonneau F, et al. Applied Surface Science, 2018, 455, 736.
|
[19] |
Sun J G. Study on the preparation of nickel-coated copper composite powder by electroless plating. Master's Thesis, Lanzhou University of Technology, China, 2013 (in Chinese).
|
|
孙建国. 化学镀法制备镍包覆铜复合粉末的工艺研究. 硕士学位论文, 兰州理工大学, 2013.
|
[20] |
Révész , Takacs L. Surface & Coatings Technology, 2009, 203(20), 3026.
|
[21] |
Farahbakhsh I, Mashimo T. Surface Engineering, 2018, 1, 13.
|
[22] |
Kuang Y Z, Zhang B, Ma F, et al. Chinese Journal of Rare Metals, 2019(8), 838(in Chinese).
|
|
匡益之, 张彬, 马飞,等. 稀有金属, 2019(8), 838.
|
[23] |
Davydova A, Dmashenkov A, Sova A, et al. Journal of Materials Proce-ssing Technology, 2016, 229(361), 6.
|
[24] |
Yu J. Electroless plating of Cr3C2-Ni powder and its application in laser cladding. Master's Thesis, Zhejiang University, China, 2010 (in Chinese).
|
|
俞佳. Cr3C2-Ni粉末化学镀及其在激光熔覆中的应用. 硕士学位论文, 浙江大学, 2010.
|
[25] |
Wang R, Ma H B, Wei D Q, et al. Special-cast and Non-ferrous Alloys, 2015, 35(11), 1209 (in Chinese).
|
|
王荣, 马海波, 魏德强,等. 特种铸造及有色合金, 2015, 35(11), 1209.
|
[26] |
Gao H J, Wang Y Z, Li F P, et al. Electroplating & Finishing, 2007(12), 18 (in Chinese).
|
|
高海军, 王引真, 李方坡,等. 电镀与涂饰, 2007(12), 18.
|
[27] |
Gao H J, Wang Y Z, Li F B, et al. China Surface Engineering, 2007, 20(4), 47 (in Chinese).
|
|
高海军, 王引真, 李方坡,等. 中国表面工程, 2007, 20(4), 47.
|
[28] |
Zhong H. Preparation of core-shell structure cobalt-coated tungsten carbide composite powder by intermittent electrode position. Master's Thesis, Hunan University, China, 2011 (in Chinese).
|
|
钟欢. 核-壳结构钴包碳化钨复合粉体的间歇电沉积制备研究. 硕士学位论文, 湖南大学, 2016.
|
[29] |
Ren J S, Li B, Wang J, et al. Electronic Components & Materials, 2018, 37(1), 51 (in Chinese).
|
|
任劲松, 李勃, 王进,等. 电子元件与材料, 2018, 37(1), 51.
|
[30] |
Ahn J H, Lee J K, Kim D W, et al. Materials Research Bulletin, 2008, 43(8-9), 2266.
|
[31] |
Matik U. Journal of the Faculty of Engineering and Architecture of Gazi University, 2018, 33(4), 1603.
|
[32] |
Lekatou A, Sioulas D, Karantzalis A E, et al. Surface & Coatings Technology, 2015, 276(539), 56.
|
[33] |
Jankovi c' N Z, Slijep c'evic' M Z,C'antrak S, et al. In: Proceedings of the Multidisciplinary Engineering Design Optimization. Belgrade, Serbia, 2016.
|
[34] |
Melchels F P W, Feijen J, Grijpma D W. Biomaterials, 2010, 31(24), 6121.
|
[35] |
Wang Y Q, Shen J X, Wu H Q. Journal of Aeronautical Materials, 2016, 52(10), 1239 (in Chinese).
|
|
王延庆, 沈竞兴, 吴海全. 航空材料学报, 2016, 52(10), 1239.
|
[36] |
Tata K, Fadel G, Bagchi A, et al. Rapid Prototyping Journal, 1998, 4(4), 151.
|
[37] |
Song S Y, Min S P, Lee J W, et al. Materials Chemistry & Physics, 2018, 216, 213.
|
[38] |
Romero-Romero M, Domínguez-Ríos C, Torres-Sánchez R, et al. Surface & Coatings Technology, 2017, 315(Complete), 181.
|
[39] |
Proa-Flores P M, Drew R A L. Advanced Engineering Materials, 2010, 10(9), 830.
|
[40] |
Zhuang Y, Wang S, Jia D, et al. Materials Science & Engineering A, 2015, 626(27), 33.
|
[41] |
Li X, Gao M, Zhang L. Journal of Alloys & Compounds, 2016, 669(55), 9.
|
[42] |
He Y W. Study on microstructure and properties of organic coating alloy powder and its laser formed parts. Master's Thesis, University of South China, China, 2016 (in Chinese).
|
|
贺沅玮. 有机物包覆合金粉末及其激光成形件组织与性能研究. 硕士学位论文, 南华大学, 2016.
|
[43] |
Seong M R, Kwon J, Lee G Y, et al. Applied Surface Science, 2010, 256(8), 2332.
|
[44] |
Liu G P, Guo X D, Duan H Z, et al. The Chinese Journal of Nonferrous Metals, 2007, 17(12), 1999 (in Chinese).
|
|
刘冠鹏, 郭效德, 段红珍, 等. 中国有色金属学报, 2007, 17(12), 1999.
|
[45] |
Chen A N, Ga F, Li M, et al. Ceramics International, 2019, 45(12), 15538.
|
[46] |
Beaman J J, Deckard C R. U.S. patent, US19900547857. 1990.
|
[47] |
Li X, Zhi C, Zhang Z, et al. Applied Surface Science, 2006, 252(22), 7856.
|
[48] |
Shiron H, Amano Y, Kawaguchi M, et al. Journal of Colloid & Interface Science, 2001, 239(2), 555.
|
[49] |
Mallakpour S, Barati A. Progress in Organic Coatings, 2011, 71(4), 391.
|
[50] |
Yun J S, Park T W, Jeong Y H, et al. Applied Physics A, 2016, 122(6), 629.
|
[51] |
Thakur V K, Thakur M K, Gupta R K. Carbohydrate Polymers, 2014, 104(1), 87.
|
[52] |
Thakur M K, Gupta R K, Thakur V K. Carbohydrate Polymers, 2014, 111(1), 849.
|
[53] |
Thakur V K, Thakur M K, Gupta R K. Carbohydrate Polymers, 2013, 98(1), 820.
|
[54] |
Thakur V K, Thakur M K, Gupta R K. International Journal of Biological Macromolecules, 2013, 61(10), 121.
|
[55] |
Thakur V K, Thakur M K, Gupta R K. Carbohydrate Polymers, 2013, 97(1), 18.
|
[56] |
Thakur V K, Thakur M K, Gupta R K. International Journal of Biological Macromolecules, 2013, 62(11), 44.
|
[57] |
Gupta R K, Ying G, Srinivasan M P, et al. Journal of Physical Chemistry B, 2012, 116(32), 9784.
|
[58] |
Gupta R K, Kusuma D Y, Lee P S, et al. ACS Applied Materials & Interfaces, 2011, 3(12), 4619.
|
[59] |
Yecheng He B L, Zou H. In: Proceedings of the ACS Symposium Series. Guangxi, China, 2014, pp.1183.
|
[60] |
Song S Y, Park M S, Lee J W, et al. Materials Chemistry and Physics, 2018, 216(446), 53.
|
|
|
|