INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
Study on Properties of SiO2 Gel Dry Water Powders |
SHI Yanjuan, FENG Mengmeng, CHEN Guangnan, XIAO Huan, SHI Guibin, CAO Chengran, HE Song
|
School of Safety Science and Emergency Management, Wuhan University of Technology, Wuhan 430070, China |
|
|
Abstract In this paper,a gel dry water was prepared using SiO2 gel as the core and hydrophobic nano SiO2 particle as the shell under high-speed shear. Powder parameters like fluidity, stability, particle size distribution, bulk density and water repellency were studied. The results show that compared with the traditional dry water powder, SiO2 gel dry water powder shows smaller repose angle, larger outflow velocity and better fluidity. The traditional dry water powder can be destroyed at the centrifuge speed of 2 000 r/min, while SiO2 gel dry water powder only agglo-merate when the centrifuge speed reaches 6 000 r/min. The bulk density of SiO2 gel dry water powder is smaller than dry water powder. For the existence of hydrophobic nano SiO2 shell, the as-prepared SiO2 gel dry water powder presents excellent water repellency.
|
Published: 24 July 2020
|
|
About author:: Yanjuan Shi, master of safety engineering, Wuhan University of Technology. Mainly engaged in preparation and characterization of porous gel materials and fire prevention research. Song Hereceived his Ph.D. degree in safety science and engineering from University of Science and Technology of China. Currently, his major locates in the protection mechanism of thermal & respiratory protection materials, as well as their preparation, characte-rization and application. |
|
|
1 Brünner H, Schutte D, Schmitz F T, et al. U.S. patent application, US 33931555, 1968. 2 Allan B D. U.S. patent application, US 4008170, 1977. 3 Binks B P, Murakami R. Nature Materials, 2006, 5(11), 865. 4 Saleh K, Forny L, Guigon P, et al. Chemical Engineering Research and Design, 2011, 89(5), 537. 5 Forny L, Saleh K, Pezron I, et al. Powder Technology, 2009, 189(2), 263. 6 Zhang Qiang, Wu Qiang, Zhang Baoyong, et al. Journal of China University of Mining & Technology, 2014(4), 593(in Chinese). 张强, 吴强, 张保勇, 等.中国矿业大学学报, 2014(4), 593. 7 Liang Huajie. Study on the properties and gas hydrate of dry water. Mater’s Thesis, South China University of Technology, China, 2010(in Chinese). 梁华杰. 干水的性能及水合物储气研究. 硕士学位论文, 华南理工大学, 2010. 8 Qiu Chuanbao. Guangdong Chemical Industry, 2012, 39(12), 77(in Chinese). 邱传宝.广东化工, 2012, 39(12),77. 9 Zhang Diwei, Ma Xinxu, Su Kunsheng, et al. Guangzhou Chemical Industry, 2014, 42(18),6(in Chinese). 张地伟, 马欣旭, 苏坤胜, 等.广州化工, 2014, 42(18), 6. 10 Wu Qiang, Zhang Baoyong. Journal of China University of Mining & Technology, 2010, 26(4),18(in Chinese). 吴强, 张保勇.中国矿业大学学报, 2010, 26(4),18. 11 Zhang Qiang, Wu Qiang, Zhang Baoyong, et al. Journal of China University of Mining & Technology, 2016, 45(5),907(in Chinese). 张强, 吴强, 张保勇, 等.中国矿业大学学报, 2016, 45(5),907. 12 Cater B O, Wang W, Adams D J, et al. Langmuir, 2010, 26(5), 3186. 13 He Juan. Research on new dry water extinguishing agent. Mater’s Thesis, Xi’an University of Science and Technology, 2014,China(in Chinese). 贺娟. 新型干水灭火剂的研究.硕士学位论文,西安科技大学, 2014. 14 Bian Jianfeng, He Yongjun, Mou Guodong. Journal of Chinese People’s Armed Police Force Academy, 2015, 31(4), 41(in Chinese). 卞建峰, 贺拥军, 牟国栋.武警学院学报, 2015, 31(4), 41. 15 Han Z Y, Zhang Y P, Du Z M. Journal of Cleaner Production, 2017, 166, 590. 16 Taylan O, Berberoglu H. Journal of Quantitative Spectroscopy and Radiative Transfer, 2013, 120, 104. 17 Zhang Zumin, Chen Xianfeng, Yuan Bihe. Journal of Functional Mate-rials, 2018, 49(6), 107(in Chinese). 张祖忞, 陈先锋, 袁必和.功能材料, 2018, 49(6),107. 18 Lu Yichun, Li Zaigeng. Refractories, 1995(6), 326(in Chinese). 芦贻春, 李再耕.耐火材料, 1995(6), 326. 19 Geldart D, Abdullah E C, Verlinden A. Powder Technology, 2009, 190(1-2), 70. |
|
|
|