| Preparation of Manganese Dioxide Ultrathin Nanosheets@Carbon Nanosphere Composites and Their Capacitance Properties |
| WANG Guiling, DU Mengyu, MA Chenchao, NIU Xingyu, ZHANG Weimin, WANG Xinyu
|
| College of Chemistry and Materials Engineering, Anhui Science and Technology University, Fengyang 233100, China |
|
|
|
|
Abstract In this paper, manganese dioxide nanosheets@carbon nanospheres electrode material was prepared by liquid phase precipitation method. XRD analysis showed that the synthesized material was in the form of sodium manganese dioxide. Electrochemical measurements showed that the introduction of appropriate amount of carbon nanospheres significantly improved the electrochemical properties of the materials, and the 100 mol% carbon nanospheres composite material had the best specific volume: the specific capacity was 166.3 F · g-1 at the current density of 1 A · g-1. When the current density increased to 10 A · g-1, the specific volume remained at 135.9 F · g-1, and the capacitance retention rate was 95.1% after 2 000 cycles, which indicated that the material had excellent rate capacity and high stability. Maybe that’s because the elevated conductivity increased active sites number of sodium manganese with the introduction of carbon nanospheres.
|
|
Published: 24 July 2020
|
|
|
| Fund:This work was supported by Anhui Natural Science Foundation Youth Fund Project (1908085QB84), Anhui Science and Technology Major Special Fund (18030901087). |
| About author:: Guiling Wang, lecturership, received her D.E. degrees in Jan. 2016 from Yanshan University and teaching in Anhui Science and Technology University, focusing on the preparation of new energy materials and research on supercapacitors. |
|
|
1 Liu C, Han G, Chang Y et al. Chemical Engineering Journal, 2017, 328,25.
2 Zhang Y, Li L, Zhang L, et al. Nano Energy, 2017,31, 174.
3 Yao B, Wang H, Zhou Q, et al. Advanced Materials, 2017, 29, 1700974.
4 Zhang Q, Zhao B, Wang J,et al. Nano Energy, 2016,28, 475.
5 Simon P,Gogotsi Y,Dunn B, et al.Science, 2014,343,1210.
6 Patake V D,Lokhande C D,Joo O S,et al. Applied Surface Science, 2009,255(7), 4192.
7 Conway B E. Journal of The Electrochemical Society, 1991, 138(6), 1539.
8 Ahn Y R,Song M Y,Jo S M,et al. Nanotechnology, 2006,17(12), 2865.
9 Hu C C,Huang C M,Chang K H. Journal of Power Sources, 2008,185(2), 1594.
10 Kandalkar S G,Gunjakar J L,Lokhande C D et al. Applied Surface Science, 2008,254(17), 5540.
11 Din H, Achour A, Vizirean U S, et al. Nano Energy, 2014, 10, 288.
12 Zhang K, Han X, Hu Z, et al. Chemical Society Reviews, 2015, 44, 699.
13 Xu C, Kang F, Li B,et al. Journal of Materials Research, 2011,25, 1421.
14 Tian Y H, Fu X T, Wu B R. Journal of Power Sources, 2002(6), 466(in Chinese).
田艳红,付旭涛,吴伯荣. 电源技术, 2002(6), 466.
15 Yin J L, Li Y D. Chemical Engineer, 2011, 47(7),42(in Chinese).
殷金玲,李一栋. 化学工程师, 2011, 47(7),42.
16 Zhang X Y, Han L Q, Sun S, et al.Journal of Alloys and Compounds, 2015, 653, 539.
17 Chen S, Zhu J W, Wu X D, et al. ACS Nano, 2010, 4(5),2822.
18 Rakhi R B, Chen J W, Cha D, et al. Advanced Energy Materials, 2012, 2(3), 381.
19 Zhao Y, Meng Y N, Jiang P. Journal of Power Sources, 2014,259, 219.
20 Kanoh H, Tang W, Makita Y, et al. Langmuir, 1997,13, 6845. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2020, Vol. 34 