新型超超临界机组用叶片钢11Cr12Ni3Mo2VN的热变形行为

doi:10.11896/cldb.19020128

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (4860KB)
Export: BibTeX | EndNote (RIS)

Abstract The purpose of this paper was to investigate the thermal deformation behavior of 11Cr12Ni3Mo2VN martensite heat-resistant steel and establish the optimal thermal deformation processing parameters of the material. In this paper, 11Cr12Ni3Mo2VN martensite heat-resistant steel was isothermal heat-compressed by Gleeble-3500 thermal simulation tester at the condition of the temperatures ranging from 900 ℃ to 1 050 ℃ and strain rate in the range of 0.001—10 s^-1. Established a constitutive equation by fitting the peak stress and verified the accuracy of the constitutive equation. It was found that the established constitutive equation have a high prediction precision on the flow stress of the material. By calculating and analysing of the experimental data, the apparent activation energy (Q) was determined to be 450.988 kJ/mol. Drawn the thermal processing maps based on the dynamic material model and Murthy's instability criterion. The optimal processing parameters of 11Cr12Ni3Mo2VN heat-resistant steel was determine by the thermal processing maps and the stress-strain curves. The specific parameters were as follows: the processing temperature from 980 ℃ to 1 050 ℃ and the strain rate of 1 s^-1 or less. The effects of the thermal deformation parameters such as temperature and strain rate on the microstructure evolution of the material were studied through OM.The results show that the temperature and strain rate have a great influence on the generation and degree of dynamic recovery and recrystallization. The processing temperature plays a decisive role in the evolution of the microstructures, the dynamic recovery dominates at low temperatures, and the degree of dynamic recrystallization rose as the temperature increased. In addition,the strain rates have a great influence on the size of dynamically recrystallized grains. The low strain rate is beneficial to the full division of dynamic recrystallization, the grain size is more uniform, and the material has more excellent performance after thermal deformation.

Key words： martensitic heat-resistant steel 11Cr12Ni3Mo2VN high-temperature deformation constitutive equation hot processing map dynamic recrystallization

Published: 15 January 2020

CLC number:

TG142.73

About author:: Peng Lyureceived his Ph.D. degree in materials from Jiangsu University in 2014. He is currently a senior experimentalist in the Institute of Material Science and Engineering at Jiangsu University. His research focuses on microstructure of metal materials, failure analysis and surface modification.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LYU Peng
	CHEN Yanan
	GUAN Qingfeng
	LI Yaojun
	XU Liang
	DING Zuojun

Cite this article:

LYU Peng,CHEN Yanan,GUAN Qingfeng, et al. The High-temperature Deformation Behavior of Novel 11Cr12Ni3Mo2VN Heat Resistant Steel for Ultra-supercritical Units[J]. Materials Reports, 2020, 34(4): 4113-4117.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.19020128 OR http://www.mater-rep.com/EN/Y2020/V34/I4/4113

1 Xie X L, Yang G, Chen J C, et al. Heat Treatment, 2009, 24(5), 35(in Chinese).
谢学林, 杨钢, 陈敬超, 等. 热处理, 2009, 24(5), 35.
2 Liao H J, Yao C G, Wang M, et al. Baosteel Technology, 2009(1), 56(in Chinese).
廖洪军, 姚长贵, 王敏, 等. 宝钢技术, 2009(1), 56.
3 Li J R, Zhou L Y, Gong C, et al. Transactions of Materials and Heat Treatment, 2014, 35(6), 106(in Chinese).
李俊儒, 周乐育, 龚臣, 等. 材料热处理学报,2014, 35(6), 106.
4 Zhu H S, Nie Y H, Bai Y G,et al. Forging Technology, 2016, 41(9), 7(in Chinese).
朱怀沈, 聂义宏, 白亚冠, 等. 锻压技术, 2016, 41(9), 7.
5 Rojas D, Garcia J, Prat O, et al. Materials Science & Engineering A, 2011, 528(3), 1372.
6 Lee K H, Hong S M, Shim J H, et al. Materials Characterization, 2015, 102, 79.
7 Lee K H, Suh J Y, Hong S M, et al. Materials Characterization, 2015, 106, 266.
8 Yin F S, Jung W S, Chung S H. Scripta Materialia, 2007, 57(6), 469.
9 Wang Z, Fu W, Wang B, et al. Materials Characterization, 2010, 61(1), 25.
10 Churyumov A Y, Khomutov M G, Solonin A N, et al. Materials & Design, 2015, 74, 44.
11 Ji H C, Liu J P, Wang B Y, et al. Journal of Alloys & Compounds, 2017, 693, 674.
12 Cai Z M, Ji H C, Pei W H, et al. Vacuum, 2019, 165, 324.
13 Bo Xiao, Lianyong Xu, Lei Zhao et al. Materials Science & Engineering A, 2019, 756, 336.
14 Wang Z M, Wang Y H, Cao W Q, et al. Transactions of Materials and Heat Treatment,2017, 38(1), 191(in Chinese).
王志蒙, 王玉辉, 曹文全, 等. 材料热处理学报, 2017, 38(1), 191.
15 Yagi K, Fujio Abe. Encyclopedia of Materials Science & Technology, 2001, 16(9), 1840.
16 Hamed M. Mechanics of Materials, 2015, 85, 66.
17 Zeng W D, Zhou Y G,Zhou J,et al. Rare Metal Materials and Engi-nering, 2006, 35(5), 673(in Chinese).
曾卫东, 周义刚, 周军, 等. 稀有金属材料与工程, 2006, 35(5), 67.
18 Qin F C, Li Y T. Journal of Mechanical Engineering,2016, 52(4), 45(in Chinese).
秦芳诚, 李永堂. 机械工程学报, 2016, 52(4), 45.
19 Murty S V S N, Rao B N. Materials Science and Engieering A, 1998, 254(1-2), 76.
20 Dipti Samantaray, Sumantra Mandal, et al. Materials Science and Engineering A, 2011, 528(15), 5204