水热法合成MoO<sub>3</sub>单晶纳米带及其形成机理<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.02.024

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1594KB)
Export: BibTeX | EndNote (RIS)

Abstract Single crystal orthorhombic phase MoO₃ (α-MoO₃) nanobelts with uniform diameter were successfully prepared through a simple hydrothermal synthesis route at 180 ℃, using solution of sodium molybdate dihydrate as well as hydrochloric acid as raw materials and without template. The products were characterized by X-ray diffraction, field emission scanning electron microscopy and transmission electron microscopy. It can be concluded that the synthesized α-MoO₃ nanobelts were transformed from the metastable phase h-MoO₃ micro rods formed at low temperature (<90 ℃) by dissolution-recrystallization, and grew along the c-axis direction. Surfactant CTAB could increase aspect ratio of the prepared α-MoO₃ nanobelts.

Key words： molybdenum trioxide hydrothermal synthesis nanobelts formation mechanism aspect ratio

Published: 02 May 2018

CLC number:

TQ127

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	GAO Bin
	ZHANG Xiaojun

Cite this article:

GAO Bin,ZHANG Xiaojun. Hydrothermal Synthesis of Single Crystal α-MoO₃ Nanobelts and Their Formation Mechanism[J]. Materials Reports, 2017, 31(2): 112-116.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.02.024 OR http://www.mater-rep.com/EN/Y2017/V31/I2/112

1 Wang X D, Summers C J , Wang Z L. Large-scale hexagonal-patterned growth of aligned ZnO nanorods for nano-optoelectronics and nanosensor arrays[J]. Nano Lett,2004,4(3):423.
2 Huang M H, Mao S, Feick H N, et al. Room-temperature ultraviolet nanowire nanolasers[J]. Science,2001,292(6):1897.
3 Mao S X, Zhao M H, Wang Z L. Nanoscale mechanical behavior of individual semiconducting nanobelts [J]. Appl Phys Lett,2003,83(5):993.
4 Tao T, Glushenkov A M, Zhang C F, et al. MoO₃ nanoparticles dispersed uniformly in carbon matrix: A high capacity composite anode for Li-ion batteries [J]. J Mater Chem,2011,21(25):9350.
5 Li T M,Zeng W,Zhang Y Y, et al. nanobelt-assembled nest-like MoO₃ hierarchical structure hydroth[J].Mater Lett,2015,160(7):476.
6 Wu H H, Yang R, Song B M. Biocompatible inorganic fullerene-like molybdenum disulfide nanoparticles produced by pulsed laser ablation in water[J]. ACS Nano,2011,5(2):1276.
7 Sun Y X,Wang J,Zhao B T, et al. Binder-free α-MoO₃ nanobelt electrode for lithium-ion batteries utilizing van der Waals forces for film formation and connection with current collector [J]. J Mater Chem A,2013,1(15):4736 .
8 Komaba S, Kumagai N, Kumagai R,et al. Molybdenum oxides synthesized by hydrothermal treatment of A₂MoO₄ (A=Li, Na, K) and electrochemical lithium intercalation into the oxide [J]. Solid State Ionics,2002,152-153:319.
9 He T, Yao J. Photochromism of molybdenum oxide [J]. J Photochem Photobiol C: Photochem Rev,2003,4(2):125 .
10 Hsu C S, Chan C C, Huang H T, et al. Electrochromic properties of nanocrystalline MoO₃ thin films [J]. Thin Solid Films,2008,516(15):4839.
11 Liu Y L, Chen K Q, Chen W. Electrochemical performance of new α-MoO₃ nanobelt cathode materials for rechargeable Li-ion batteries[J]. Solid State Sci,2014,34(8):43.
12 Zhuo R F, Xu X Y, Feng H T. Morphology-controlled synthesis, growth mechanism, optical and microwave absorption properties of ZnO nanocombs [J]. Adv Mater Res,2010,97(6):960.
13 Jang S Y, Song Y M, Kim H S,et al. Three synthetic routes to single crystalline PbS nanowires with controlled growth direction and their electrical transport properties[J]. ACS Nano,2010,4(12):2391.
14 Hu Z B , Zhou C G , Zheng M R,et al. K-enriched MoO₃ nanobundles: A layered structure with high electric conductivity[J]. J Phys Chem C,2012,116(6):3962.
15 Zheng L, Xu Y, Jin D,et al. Novel metastable hexagonal MoO₃ nanobelts synthesis, photochromic, and electrochromic properties [J]. Chem Mater,2009,21(2):5681.
16 Lin S Y, Wang C M, Kao K S, et al. Electrochromic properties of MoO₃ thin films derived by a sol-gel process [J]. J Sol-Gel Sci Technol,2010,53(1):51.
17 Cordier A, Resende V G, Weibel A, et al. Catalytic chemical vapor deposition synthesis of double-walled and few-walled carbon nanotubes by using a MoO₃-supported conditioning catalyst to control the formation of iron catalytic particles within an ±-Al_1.8Fe_0.2O₃ self-supported foam [J]. J Phys Chem C,2010,14(2):19188.
18 Li Y B, Bando Y. Quasi-aligned MoO₃ nanotubes grown on Ta substrate [J]. Chem Phys Lett,2002,364(5):484.
19 Zhou J, Xu N S, Deng S Z, et al. Large-area nanowire arrays of molybdenum and molybdenum oxides: Synthesis and field emission properties [J]. Adv Mater,2003,15(21):1835.
20 Niederberger M, Krumeich F, Muhr H J, et al. Synthesis and cha-racterization of novel nanoscopic molybdenum oxide fibers [J]. Mater Chem,2001,11(7):1941.
21 Li X L, Liu J F, Li Y D. Low-temperature synthesis of large-scale single-crystal molybdenum trioxide (MoO₃) nanobelts [J]. Appl Phys Lett,2002,81(25):4832.
22 Lou X W, Zeng H C. Hydrothermal synthesis of α-MoO₃ nanorods via acidification of ammonium heptamolybdate tetrahydrate [J]. Chem Mater,2002,14(11):4781.
23 Gao Y H, Bando Y, Sato T. Nanobelts of the dielectric material Ge₃N₄[J]. Appl Phys Lett,2001,79(27):4565.
24 Sun X M, Chen X, Deng Z X, et al. A CTAB-assisted hydrothermal orientation growth of MoO₃ nanorods [J]. Chem Phys,2002,78(5):99.