CSW/POE-g-MA/PA6三元复合材料的结构和性能

doi:10.11896/j.issn.1005-023X.2017.02.022

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1319KB)
Export: BibTeX | EndNote (RIS)

Abstract Maleic anhydride grafted polyethylene-octene copolymer (POE-g-MA) was used to toughen calcium sulfate whis-ker/nylon 6 (CSW/PA6) composites, and mechanical, thermal, morphological properties and processing performance of CSW/PA6 and CSW/POE-g-MA/PA6 composites were studied. The results indicated that the addition of appropriate CSW could increase both the stiffness and toughness of PA6. Compared with those of pure PA6, tensile strength, flexural strength, flexural modulus and notched impact strength of 10%CSW/PA6 composites increased by 7.5%,9.1%,21.1% and 11.6%, respectively. However, when CSW content increased to 30%, the impact strength of PA6 decreased significantly. The presence of POE-g-MA promoted the homogeneous distribution of CSW in PA6 matrix, also enhanced the interfacial adhesion between CSW and PA6, resulting in significant improvement of impact strength of CSW/PA6 (30/70) composites. Due to the synergistic effect of CSW and POE-g-MA, the notched impact strength and flexural modulus of CSW/POE-g-MA/PA6 (30/5/65) composites increased by 36.8% and 22.1% compared with pure PA6, and its tensile and flexural strength were close to those of pure PA6.

Key words： calcium sulfate whisker nylon 6 maleic anhydride grafted polyethylene-octene copolymer properties

Published: 02 May 2018

CLC number:

TQ342+.11

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SUN Wenkui
	ZHOU Song
	MA Junhui
	YAN Kehua
	WANG Jun
	CHEN Hao

Cite this article:

SUN Wenkui,ZHOU Song,MA Junhui, et al. Structure and Properties of CSW/POE-g-MA/PA6 Ternary Composites[J]. Materials Reports, 2017, 31(2): 101-104.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.02.022 OR http://www.mater-rep.com/EN/Y2017/V31/I2/101

1 Courtney T H. Mechanical behavior of materials [M].New York: McGraw-Hill Science,1999:83.
2 Yang M, Luo S K, Deng Z P,et al.Applications of whiskers in poly-mer composites [J].Mater Rev:Rev,2014,28(2):51(in Chinese).
杨萌,罗世凯,邓昭平,等.晶须在聚合物复合材料中的应用[J].材料导报:综述篇,2014,28(2):5.
3 Tjong S C, Meng Y Z. Performance of potassium titanate whisker reinforced polyamide-6 composites [J]. Polymer,1998,39(22):5461.
4 Liu J Y, Reni L, Wu J L, et al. Fabrication and characterization of polycaprolactone/calcium sulfate whisker composites [J]. Express Polym Lett,2011,5(8):742.
5 He M, Wang L E, Lu S J, et al. Properties of calcium sulfate whisker-modified low melting point nylon6 composite [J]. Plastics,2010,39(4):24(in Chinese).
何敏,王丽娥,鲁圣军,等.硫酸钙晶须改性低熔点PA6复合材料的性能[J].塑料,2010,39(4):24.
6 Shao H J, Qin S H, Yu J, et al. Influence of grafting degree on the morphology and mechanical properties of PA6/POE-g-GMA blends [J].Polym-Plast Technol Eng,2012,51(1):28.
7 Wang K, Wang C, Li J, et al. Effects of clay on phase morphology and mechanical properties in polyamide 6/EPDM-g-MA/organoclay ternary nanocomposites [J].Polymer,2007,48(7):2144.
8 Lim S H, Dasari A, Yu Z Z, et al. Fracture toughness of nylon 6/organoclay/elastomer nanocomposites [J]. Compos Sci Technol,2007,67(14):2914.
9 Ning N Y, Deng H, Luo F, et al. Effect of whiskers nucleation abi-lity and shearing function on the interfacial crystal morphology of polyethylene (PE)/raw whiskers composites [J]. Composites Part B,2011,42(4):631.
10 Feng X, Wang H Y, Shi Y J, et al. The effects of the size and content of potassium titanate whiskers on the properties of PTW/PTFE composites [J].Mater Sci Eng A,2007,448(1-2):253.
11 Qiu L, Tsai F C, Zhou Q, et al. Influence of CaCl₂ on the structure and mechanical properties of PA6/CaSO₄ whisker composites [J]. Colloid Polym,2010,28(2):81(in Chinese).
邱亮,蔡芳昌,周勤,等.氯化钙对尼龙6/硫酸钙晶须增强材料结构与力学性能的影响研究[J].胶体与聚合物,2010,28(2):81.
12 Tjong S C, Meng Y Z. Properties and morphology of polyamide 6 hybrid composites containing potassium titanate whisker and liquid crystalline copolyester [J].Polymer,1999,40(5):1109.
13 Dweiri R, Azhari C H. Thermal and flow property-morphology relationship of sugarcane bagasse fiber-filled polyamide 6 blends [J].J Appl Polym Sci,2004,92(6):3744.
14 Cao M L, Zhang C, Wei J Q. Microscopic reinforcement for cement based composite materials [J]. Constr Build Mater,2013,40:14.
15 Abdulkadir Güllü, Ahmet zdemir, Emin zdemir. Experimental investigation of the effect of glass fibres on the mechanical properties of polypropylene (PP) and polyamide 6 (PA6) plastics [J].Mater Des,2006,27(4):316.
16 Chow W S, Mohd Ishak Z A, Apostolov A A, et al. Compatibilizing effect of maleated polypropylene on the mechanical properties and morphology of injection molded polyamide 6/polypropylene/organoclay nanocomposites [J]. Polymer,2003,44(23):7427.
17 王贵恒.高分子材料成型加工原理[M].北京:化学工业出版社,2011:6.
18 Shiao M L, Nair S V, Garrett P D, et al. Effect of glass-fiber reinforcement and annealing on microstructure and mechanical behaviour of nylon 6,6:Part Ⅱ Mechanical behaviour [J]. Mater Sci,1994,29(7):1739.
19 Zhang X J, Zhang X Y, et al. Mechanical and thermal properties of denture PMMA reinforced with silanized aluminum borate whiskers [J]. Dental Mater J,2012,31(6):903.
20 顾宜,赵长生.材料科学与工程基础[M].北京:化学工业出版社,2011:3.
21 Sachin N Sathe, Rao K V, Surekha Devi, et al. The effect of composition on morphological, thermal, and mechanical properties of polypropylene/nylon-6/polypropylene-g-butyl acrylate blends [J]. Polym Eng Sci,1996,36(19):2443.