硝酸活化时间对煤基电极材料结构及性能的影响

doi:10.11896/j.issn.1005-023X.2018.04.004

Abstract
Figure/Table
References
Related Citation (14)

Download:

Full Text ( PDF ) (1667KB)
Export: BibTeX | EndNote (RIS)

Abstract Nitric acid was used to activate the coal-based electrode, the effect of activation time on the surface properties and adsorption properties of the electrode materials was studied. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR) were used to characterize the microstructure and surface chemical properties of the electrodes. The study showed that the iodine adsorption value of coal-based electrode material increased at first and then decreased while the activation rate and compressive strength gradually decreased with the increasing activation time of nitric acid, the content of carboxyl group, hydroxyl group, phenolic hydroxyl group and other oxygen functional groups increased gradually. When the activation time was 8 h, the total oxygen functional groups could be increased by 144%, the iodine adsorption value reached 301.72 mg·g^-1, and the compressive strength was 0.234 MPa, the yield was 67.64%. The electrochemical test results showed that the coal-based electrode had good capacitance characteristics and formed a stable double layer structure. The removal rate of each ion in the process of cyanide wastewater after electro adsorption was increased with the increasing activation time, copper and total cyanide ion removal rates could reach 90% and 68% after activating for 8 h.

Key words： electrode material activation time pore size adsorption capacit

Published: 25 February 2018

CLC number:	TQ536.9
	TM242

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SU Ting
	SONG Yonghui
	ZHANG Shan
	TIAN Yuhong
	LAN Xinzhe

Cite this article:

SU Ting,SONG Yonghui,ZHANG Shan, et al. Influence of Nitric Acid Activation Time on the Structure and Property of Coal-based Electrode Materials[J]. Materials Reports, 2018, 32(4): 528-532.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.04.004 OR http://www.mater-rep.com/EN/Y2018/V32/I4/528

1 Xing Baolin, Chen Lunjian, Zhang Chuanxiang. Activation mechanism of lignite-based activated carbon prepared by KOH activation[J].Journal of China University of Mining & Technology,2014,43(6):1038(in Chinese).
邢宝林,谌伦建,张传祥.KOH活化法制备褐煤基活性炭的活化机理研究[J].中国矿业大学学报,2014,43(6):1038.
2 Xing Baolin, Chen Lunjian, Zhang Chuanxiang. Research progress of activated carbon electrode material for supercapacitor[J].Materials Review A:Review Papers,2010,24(8):22(in Chinese).
邢宝林,谌伦建,张传祥.超级电容器用活性炭电极材料的研究进展[J].材料导报:综述篇,2010,24(8):22.
3 Zhao Shuhong, Wu Feng, Su Yuefeng. New progress in research on carbon-based electrode in electrochemical capacitor[J].Materials Review,2003,17(4):46(in Chinese).
赵淑红,吴锋,苏岳锋.电化学电容器碳基电极材料研究进展[J].材料导报,2003,17(4):46.
4 Yan Chao, Li Kaixi, Jia Lincai. Research on the preparation of high specific surface area coal-based activated carbon[J].Sci-Tech Information Development & Economy,2010,20(31):162(in Chinese).
阎超,李开喜,贾林才.煤基高比表面积活性炭的制备研究[J].科技情报开发与经济,2010,20(31):162.
5 Shan Mingli, Liu Yujing, Li Xia. KOH-activated carbons used as electrode materials for supercapacitor[J].Materials Review B:Research Papers,2016,30(5):11(in Chinese).
单明礼,刘玉静,李霞.氢氧化钾改性碳材料及其在超级电容器中的应用[J].材料导报:研究篇,2016,30(5):11.
6 Hyun-Chul Lee, Narandalai Byamba-Ochir, et al. High-performance super capacitors based on activated anthracite with controlled porosity[J].Journal of Power Sources,2015,275:668.
7 Ye Yunna, Chen Lunjian, Liu Linqin, et al. Effect of preparation procedure of coal-based activated carbons on iodine adsorption[J].Mate-rials Review,2015,29(S1):327(in Chinese).
叶云娜,谌伦建,刘林勤,等.制备工艺对煤基活性炭碘吸附性能的影响[J].材料导报,2015,29(专辑25):327.
8 Li Lanting. Study on the activation condition of coal-based electrode[J].Coal Processing & Comprehensive Utilization,2009(4):40(in Chinese).
李兰廷.煤基电极炭活化条件的研究[J].煤炭加工与综合利用,2009(4):40.
9 Yang Ying, Li Lei, Sun Zhenya, et al. The research on the surface oxidation modification of activated carbon and its adsorption mechanisms of organic matter and heavy metalions[J].Science Technology and Engineering,2012,12(24):6132(in Chinese).
杨颖,李磊,孙振亚,等.活性炭表面官能团的氧化改性及其吸附机理的研究[J].科学技术与工程,2012,12(24):6132.
10 Zhu Yangjun, Dai Fang, Yu Feng, et al. Study on the Electrochemical performance of activated carbon electrode material modified by nitric acid[J].Journal of Fudan University(Natural Science),2014,53(1):93(in Chinese).
朱杨军,代芳,于峰,等.硝酸改性活性炭电极材料的电化学性能研究[J].复旦学报(自然科学版),2014,53(1):93.
11 Soudani N, Souissi-Najar S, Ouederni A. Influence of nitric acid concentration on characteristics of olive stone based activated carbon[J].Chinese Journal of Chemical Engineering,2013,21(12):1425.
12 Huang Wei, Sun Shengkai, Li Yujie, et al. Influence of nitric acid modification on the properties of activated carbon[J].Biomass Che-mical Engineering,2006(6):17(in Chinese).
黄伟,孙盛凯,李玉杰,等.硝酸改性处理对活性炭性能的影响[J].生物质化学工程,2006(6):17.
13 Wu Kaijin, Guan Xinyu, Guan Jiuhong, et al. Influence of nitric acid modification on the adsorption properties of activated carbon[J].Journal of Fujian Forestry Science and Technology,2009,36(4):35(in Chinese).
吴开金,官新宇,官九红,等.硝酸改性对活性炭吸附性能的影响[J].福建林业科技,2009,36(4):35.
14 Ding Chunsheng, Gong Fei, Chen Shan, et al. Preparation of HNO3-modified activated carbon and its adsorption capability to Cr(Ⅵ)[J].Environmental Protection of Chemical Industry,2013,33(4):344(in Chinese).
丁春生,贡飞,陈姗,等.硝酸改性活性炭的制备及其对Cr(Ⅵ)的吸附性能[J].化工环保,2013,33(4):344.
15 Zhang Shouyu, Lu Junfu, Liu Qing, et al. Influence of activation time on characteristics of active coke[J].Journal of China University of Mining & Technology,2003,32(3):289(in Chinese).
张守玉,吕俊复,刘青,等.活化时间对煤制活性焦性质的影响[J].中国矿业大学学报,2003,32(3):289.
16 Wang Kunping, Xu Qianqian. Effect of several different treatment methods on surface chemical properties of actived carbon[J].Chinese Journal of Environmental Engineering,2012,6(2):373(in Chinese).
汪昆平,徐乾前.几种不同处理方法对活性炭表面化学性质的影响[J].环境工程学报,2012,6(2):373.
17 Langley Laura A, Fairbrother D Howard. Effect of wet chemical treatments on the distribution of surface oxides on carbonaceous materials[J].Carbon,2007,45(1):47.
18 Xing Baolin, Chen Lunjian, Zhang Chuanxiang, et al. Preparation and characterization of activated carbons for supercapacitor under moderate temperature activation condition[J].Journal of China Coal Society,2011(7):1200(in Chinese).
邢宝林,谌伦建,张传祥,等.中低温活化条件下超级电容器用活性炭的制备与表征[J].煤炭学报,2011(7):1200.
19 Chen Lunjian, Xing Baolin, Ma Yafen, et al. Electrochemical performance of coal-based activated carbon electrodes modified by ammoxidation[J].Journal of China University of Mining & Technology,2013,42(3):454(in Chinese).
谌伦建,邢宝林,马亚芬,等.氨解改性煤基活性炭电极材料的电化学性能[J].中国矿业大学学报,2013,42(3):454.