| CHINESE MATERIALS CONFERENCE — ENVIRONMENTAL ENGNEERING MATERIALS |
|
|
|
|
|
| Preparation of Low Grade Attapulgite Clay Porous Supports for Ceramic Membranes |
| FAN Zhaoru1,2, ZHOU Shouyong2, LI Meisheng2, ZHAO Yijiang2, XING Weihong1
|
1 National Engineering Research Center for Special Separation Membrane, State Key Laboratory of Materials-oriented Chemical Engineering, College of Chemical Engineering, Nanjing Tech University, Nanjing 210009;
2 Jiangsu Engineering Laboratory for Environment Functional Materials, Jiangsu Key Laboratory for Chemistry of Low-dimensional Materials, School of Chemistry and Chemical Engineering, Huaiyin Normal University, Huai’an 223300; |
|
|
|
|
Abstract Porous ceramic membrane support is the basis of ceramic membrane preparation and application, which is the key factor of supporting membrane layer. It provides certain mechanical strength and corrosion resistance for ceramic membrane. Preparation of the ceramic membrane with inexpensive raw materials, such as diatomite, kaolin and fly ash instead of alumina and lower sintering temperature would be beneficial to reduce the cost of the ceramic membranes and consolidate their applications in industrial processes. This work aimed to develop low-cost ceramic membrane supports from low-grade attapulgite clay (ATP). The effects of raw material ratio, pressing pressure, sintering temperature, pore forming agent and sintering additives on the microstructure and performance of the support were systematically studied. The results showed that the addition of appropriate amount of alumina in attapulgite clay can effectively prevent the excessive shrinkage of the support during sintering, and reduce its shrinkage rate from (30±0.12)% to (3.1±0.05)%, which greatly increased the mechanical strength and porosity of the support. The porosity of the support increased with the increase of the amount of pore-forming agent, while the mechanical strength decreased. The mechanical strength increased with the increase of pressing pressure and the porosity decreased. The mechanical strength increased with the increase of sintering temperature. When the sintering temperature exceeded 750 ℃, the attapulgite structure began to collapse, support began to form densification, and the porosity decreased significantly. When the content of attapulgite clay was 63%, alumina was 29%, pore-forming agent was 6%, the pressing pressure was 10 MPa, and the sintering temperature was 700 ℃, the perfor-mance of the support was optimal, the average mechanical strength was (18.11±1.83) MPa, and the porosity was (45.94±0.49)%.
|
|
Published: 22 November 2018
|
|
|
|
|
1 Anderson L L, Armstrong P A, Broekhuis R R, et al. Advances in ion transport membrane technology for oxygen and syngas production[J]. Solid State Ionics,2016,288:331.
2 Lorente-Ayza M M, Mestre S, Menéndez M, et al. Comparison of extruded and pressed low cost ceramic supports for microfiltration membranes[J]. Journal of the European Ceramic Society,2015,35(13):3681.
3 Zhu J, Fan Y, Xu N. Modified dip-coating method for preparation of pinhole-free ceramic membranes[J]. Journal of Membrane Science,2011,367(1):14.
4 Wu L J, Zhou S Y, Li M S, et al. Research progress of new ceramic membrane material[J]. New Chemical Materials,2016,44(6):43(in Chinese).
吴立剑,周守勇,李梅生,等.新型陶瓷膜材料的研究进展[J].化工新型材料,2016,44(6):43.
5 Mouiya M, Abourriche A, Bouazizi A, et al. Flat ceramic microfiltration membrane based on natural clay and Moroccan phosphate for desalination and industrial wastewater treatment[J]. Desalination,2018,427:42.
6 Fan Y Q, Qi H, Xu N P. Advance in preparation techniques of po-rous ceramic membranes[J]. Ciesc Journal,2013,64(1):107(in Chinese).
范益群,漆虹,徐南平.多孔陶瓷膜制备技术研究进展[J].化工学报,2013,64(1):107.
7 Kouras N, Harabi A, Bouzerara F, et al. Macro-porous ceramic supports for membranes prepared from quartz sand and calcite mixtures[J]. Journal of the European Ceramic Society,2017,37:3159.
8 Ali M B, Hamdi N, Rodriguez M A, et al. Macroporous ceramic supports from natural clays. Improvement by the use of activated clays[J]. Ceramics International,2017,43(1):1242.
9 Guo H, Li W, Ye F. Low-cost porous mullite ceramic membrane supports fabricated from kyanite by casting and reaction sintering[J]. Ceramics International,2016,42(4):4819.
10 Jiang Q, Rentschler J, Perrone R. Application of ceramic membrane and ion-exchange for the treatment of the flowback water from Marcellus shale gas production[J]. Journal of Membrane Science,2013,431(431):55.
11 Zou D, Qiu M H, Chen X F, et al. One-step preparation of high-performance bilayer α-alumina ultrafiltration membranes via co-sintering process[J]. Journal of Membrane Science,2017,524:141.
12 Munirasu S, Haija M A, Banat F. Use of membrane technology for oil field and refinery produced water treatment—A review[J]. Process Safety and Environmental Protection,2016,100:183.
13 Zheng X, Zhang Z, Yu D, et al. Overview of membrane technology applications for industrial wastewater treatment in China to increase water supply[J]. Resources Conservation and Recycling,2015,105:1.
14 Zhu M M, Han J Q, Wang F, et al. Electrospun nanofibers membranes for effective air filtration[J]. Macromolecular Materials and Engineering,2017,302:1.
15 Jeong Y, Lee S, Hong S, et al. Preparation, characterization and application of low-cost pyrophyllite-alumina composite ceramic membranes for treating low-strength domestic wastewater[J]. Journal of Membrane Science,2017,536:108.
16 Aust U, Benfer S, Dietze M, et al. Development of microporous ceramic membranes in the system TiO2/ZrO2[J]. Journal of Membrane Science,2006,281(1):463.
17 Babaluo A, Kokabi M, Manteghian M, et al. A modified model for alumina membranes formed by gel-casting followed by dip-coating[J]. Journal of the European Ceramic Society,2004,24(15):3779.
18 Chen X F, Zhang Y, Tang J X, et al. Novel pore size tuning method for the fabrication of ceramic multi-channel nanofiltration membrane[J]. Journal of Membrane Science,2018,552:77.
19 Shqau K, Mottern M L, Di Y, et al. Preparation and properties of porous α-Al2O3 membrane supports[J]. Journal of the American Ceramic Society,2010,89(6):1790.
20 Biesheuvel P M, Verweij H. Design of ceramic membrane supports: Permeability, tensile strength and stress[J]. Journal of Membrane Science,1999,156(1):141.
21 Kwon S, Messing G L. Design of ceramic membrane supports: Permeability, tensile strength and stress[J]. Journal of Membrane Scie-nce,1998,33(4):913.
22 Guo H L, Zhao S F, Qi H, et al. Fabrication and characterization of TiO2/ZrO2 ceramic membranes for nanofiltration[J]. Microporous and Mesoporous Materials,2018,260:125.
23 Zhu Y K, Chen D J. Preparation and characterization of attapulgite-based nanofibrous membranes[J]. Materials and Design,2017,113:60.
24 Liu Z J, Chen Z H, Yuan H J, et al. Effects of attapulgite clay on soil aggregate and wheat growth[J]. Chinese Journal of Soil Science,2010,41(1):142(in Chinese).
刘左军,陈正宏,袁惠君,等.凹凸棒石粘土对土壤团粒结构及小麦生长的影响[J].土壤通报,2010,41(1):142.
25 Brindley W F. The structural scheme of attapulgite [J]. american Mineralogist,1940,25:405.
26 Guo H, Zhang H, Peng F, et al. Effects of Cu/Fe ratio on structure and performance of attapulgite supported CuFeCo-based catalyst for mixed alcohols synthesis from syngas[J]. Applied Catalysis A: Ge-neral,2015,503:511.
27 国家技术监督局.GB/T1965-1996多孔陶瓷膜抗弯强度试验方法[S].北京:中国标准出版社,1997.
28 国家技术监督局.GB/T1966-1996多孔陶瓷显气孔率、容重试验方法[S].北京:中国标准出版社,1997.
29 Yang Y L, Zhou J E, Wang Y Q, et al. Effect of nano-TiO2 on sintering process of alumina porous ceramic membrane support[J]. Journal of Synthetic Crystals,2015,44(10):2841(in Chinese).
杨玉龙,周健儿,汪永清,等.纳米TiO2对氧化铝质多孔陶瓷膜支撑体烧结过程的影响[J].人工晶体学报,2015,44(10):2841.30 Xie J J, Chen T H, Qing C S, et al. Structure evolution of palygorskite after heat-treatment[J]. Earth Science Frontiers,2014,21(5):338(in Chinese).
谢晶晶,陈天虎,庆承松,等.热处理凹凸棒石的结构演化[J].地学前缘,2014,21(5):338.
31 Arzani M, Mahdavi H R, Sheikhi M, et al. Ceramic monolith as microfiltration membrane: Preparation, characterization and perfor-mance evaluation[J]. Applied Clay Science,2018,161:456.
32 Cheng K K, Chang Q B, Wang Y Q, et al. Preparation of α-Al2O3 ceramic membrane support used nano-alumina as sintering-aid[J]. China Ceramics,2013,49(10):9(in Chinese).
程科恺,常启兵,汪永清,等.以纳米氧化铝为助烧结剂制备α-Al2O3陶瓷膜支撑体[J].中国陶瓷,2013,49(10):9.
33 Shen Y, Qiang B, Hong Q I, et al. Fabrication and characterization of porous SiC support and Al2O3/SiC composite membrane[J]. Membrane Science and Technology,2013,33(1):22. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2018, Vol. 32 