水灰比对镁系无机轻质材料性能的影响规律

doi:10.11896/j.issn.1005-023X.2018.14.009

Abstract
Figure/Table
References
Related Citation (12)

Download:

Full Text ( PDF ) (4063KB)
Export: BibTeX | EndNote (RIS)

Abstract Magnesium inorganic light material containing a large number of closed pores inside were prepared by chemical foaming process, in which magnesium based cementing material as raw material, hydrogen peroxide as foaming agent, manganese dioxide as activator, calcium stearate as stabilizer and polyacrylamide as thickener. The effect of water cement ratio (the ratio of magnesium salt and magnesium oxide) on the apparent density, compression strength, bending strength, pore structure and water resistance of magnesium inorganic light materials were studied. The experimental results showed that the water cement ratio not only affects the pore structure and foaming formation of magnesium inorganic light materials, but also has a great influence on the crystal structure. With the increasing of water cement ratio, the paste consistency decreased, the apparent density of magnesium inorganic light material decreased, the pore structure shape gradually improved, the mechanical strength and water resistance increased first and then decreased. When the water cement ratio was 1.4, the peak of the intensity phase was the largest, the magnesium inorganic light material had the largest compressive strength, flexural strength and best water resistance. At the same time, the average pore size was smaller, the porosity and the roundness value are close to the Kepler ideal model value, and the apparent density was only 0.41 g/cm³, which is suitable for the use of energy-saving lightweight wall materials.

Key words： magnesium based cementing material chemical foaming inorganic light materials water cement ratio pore structure

Published: 31 July 2018

CLC number:

TU55

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZUO Yingfeng
	XIAO Junhua
	LI Ping
	WANG Jian
	LI Xianjun
	WU Yiqiang

Cite this article:

ZUO Yingfeng,XIAO Junhua,LI Ping, et al. Effect of Water Cement Ratio on Properties of Magnesium Inorganic Light Materials[J]. Materials Reports, 2018, 32(14): 2370-2375.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.14.009 OR http://www.mater-rep.com/EN/Y2018/V32/I14/2370

1 Zhou Xiaoyan, Li Jian, Zhou Dingguo. Simulation evaluation of the heat-conducting property of wheat straw-based sandwich wallboard[J]. Scientia Silvae Sinicae,2007,43(2):24(in Chinese).
周晓燕,李键,周定国.轻质秸秆复合墙体传热特性模拟评价[J].林业科学,2007,43(2):24.
2 Zhang Meng, Tian Qingbo, Xu Lina, et al. Status and prospects of research on foamed cement[J]. Bulletin of the Chinese Ceramic Society,2014,33(10):2547(in Chinese).
张萌,田清波,徐丽娜,等.发泡水泥的研究现状及展望[J].硅酸盐通报,2014,33(10):2547.
3 Papadopoulos A M. State of the art in thermal insulation materials and aims for future developments[J]. Energy and Buildings,2005,37:78.
4 Gyoung-Seok Choi, Jae-Sik Kang, Young-Sun Jeong, ea al. An experimental study on thermal properties of composite insulation[J]. Thermochimica Acta,2007,455:75.
5 Wang F, Yang L, Guan L, et al. Microstructure and properties of cement foams prepared by magnesium oxychloride cement[J]. Journal of Wuhan University of Technology(Materials Science Edition),2015,30(2):331.
6 Xi X, Shui A, Li Y, et al. Effects of magnesium oxychloride and silicon carbide additives on the foaming property during firing for porcelain ceramics and their microstructure[J]. Journal of the European Ceramic Society,2012,32(12):3035.
7 Sglavo V M, De Genua F, Conci A, et al. Influence of curing temperature on the evolution of magnesium oxychloride cement[J]. Journal of Materials Science,2011,46(20):6726.
8 Chau C K, Chan J, Li Z. Influences of fly ash on magnesium oxychloride mortar[J]. Cement and Concrete Composites,2009,31(4):250.
9 Shuiping W, Rui W, Yingdan Z, et al. Effects of EVA latex on the properties of glass-fiber/magnesium-oxychloride cement composites[J]. Journal of Wuhan University of Technology(Materials Science Edition),2006,21(1):138.
10 Li Y, Li Z J, Pei H F, et al.The influence of FeSO₄ and KH₂PO₄ on the performance of magnesium oxychloride cement[J].Construction and Building Materials,2016,102:233.
11 Chen Xuefei, Wang Luming. Research on water resistance of magnesium oxychloride cement with sodium phosphate and styrene-acrylate emulsion[J]. Concrete,2017(6):76(in Chinese).
陈雪霏,王路明.磷酸钠/苯丙乳液改善氯氧镁水泥耐水性的研究[J].混凝土,2017(6):76.
12 Xu Wen, Liu Xingya, Zhu Qinghua. Experimental research on foam concrete panel prepared with chemical method used in external wall external insulation system[J]. Concrete,2012(3):131(in Chinese).
徐文,刘兴亚,朱清华.外墙外保温用化学发泡泡沫混凝土板的试验研究[J].混凝土,2012(3):131.
13 Kearsley E P, Wainwright P J. The effect of high fly ash content on the compressive strength of foamed concrete[J]. Cement and Concrete Research,2001,31(1):105.
14 Peng Junzhi, Peng Xiaoqin. A review on structure and properties of aerated concrete[J]. Materials Review A: Review Papers,2011,25(1):89(in Chinese).
彭军芝,彭小芹.加气混凝土的结构与性能研究进展[J].材料导报: 综述篇,2011,25(1):89.
15 Guan Hui, Ba Hengjing. A study on the stability of magnesium oxychloride cement[J]. Journal of Harbin Engineering University,2009(11):1213(in Chinese).
关辉,巴恒静.氯氧镁水泥相稳定性的研究[J].哈尔滨工程大学学报,2009(11):1213.