Materials Reports 2022, Vol. 36 Issue (Z1): 22010200-6 |
INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
Multi-sheet Preparation and Characterization of Nano-porous Silicon |
JIAN Yan, YANG Wenjing, YANG Lei, SONG Shaoyi, NI Jie, HE Yinfang
|
School of College of Chemistry and Chemical Engineering, Chongqing University, Chongqing 400000, China |
|
|
Abstract Nano-porous silicon(PS) composite energetic material is currently an important emerging material in the military field of various countries. Due to the large specific surface area, high chemical activity and other excellent properties, it can cause rapid combustion and explosion under certain trigger conditions and release high-efficiency energy. In order to realize the mass production of nano-porous silicon, the electrochemical single-cell anodization method was used to prepare porous silicon in small batches, and the structure, morphology and photoluminescence properties of porous silicon were analyzed and studied by scanning electron microscope (SEM) and steady-state fluorescence spectrometer. The results show that the luminescence intensity of porous silicon increases first then decreases with the prolongation of corrosion time, and is neagatively correlated with the increase of current density; its fluorescence peak tends to red-shift with the increase of hydrofluoric acid content in the electrolyte ratio; the increase of current density and etching time benefits the preparation of porous silicon with large porosity and deep longitudinal etching, and with the increase of the concentration ratio of hydrofluoric acid in the etching solution system, better uniformity, compactness and flatness of nano-scale porous silicon can be obtained within the range of controlled experimental conditions, for which the batch controllable production of porous silicon can be effectively realized.
|
Published: 05 June 2022
Online: 2022-06-08
|
|
Fund:Open Project of Chongqing Key Laboratory(KFJJ2004). |
|
|
1 Lu Z, Liu N, Lee H W, et al. ACS Nano, 2015, 9(3), 2540. 2 Tölli M A, Ferreira M, Kinnunen S M. Biomaterials, 2014, 35(29), 8394. 3 Mora M B, Bornacelli J, Nava R, et al. Journal of Luminescence, 2014, 146, 247. 4 Kozak D A, Stievater T H, Pruessner M W, et al. ECS Transactions, 2014, 64(1), 197. 5 Santos H A, Mäkilä E, Airaksinen A J, et al. Nanomedicine, 2014, 9(4),535. 6 Martinpalma R J, Mansosilvan M, Torrescosta V. Journal of Nanophoto-nics, 2010, 4(1),3150. 7 张栋. 周期性硅纳米线和纳米多孔硅的制备及其光电性能研究. 博士学位论文, 上海师范大学, 2016. 8 Costa V T, Martin-Palma R J. Journal of Materials Science, 2010, 45(11), 2823. 9 Diener J, Gross E , Künzer N, et al. patent, US6803244B2, 2004. 10 Kovalev, Timoshenko V Y, Kunzner N, et al. Physical Review Letters,2001,87(6), 11. 11 Clement D, Diener J, Grcss E, et al. Physica Status Solidi (a) , 2005,202(8), 1357. 12 Mccord P, Yau S L, Bard A J. Science, 1992, 257(5066), 68. 13 王晶禹, 张景林, 徐文峥.火炸药学报, 2003, 26(1), 4. 14 许高斌, 卢翌, 陈兴, 等.电子测量与仪器学报, 2014(12),1308. 15 任秀秀, 赵省向, 韩仲熙, 等.材料导报:综述篇, 2019, 33(23), 91. 16 眭俊. 多孔硅的电化学制备及其性能研究.博士学位论文, 南昌航空大学, 2013. 17 张华, 李蛟, 丛日敏.山东理工大学学报: 自然科学版, 2015, 29(3), 20. 18 牟奕轩, 简燕, 陈金, 等.山东化工, 2021,50(4),6. 19 Splinter A, Stürmann J, Benecke W. Sensors and Actuators A: Physical, 2001, 92(1-3), 394. 20 宋晓岚, 喻振兴, 程蕾, 等.中南大学学报(自然科学版), 2010(4),1229. 21 Sujatha L, Bhattachaeya E. Sadhana-Academy Proceeding in Engineering Sciences, 2009, 34(4), 643. |
|
|
|