| POLYMERS AND POLYMER MATRIX COMPOSITES |
|
|
|
|
|
| Prediction of Elastic Constants of Short Flax Fiber Reinforced Composites Considering the Interfacial Property |
| XIONG Xiaoshuang1,2,3, ZHANG Zihao2, LI Qiaomin2, YU Lianqing2,3
|
1 Hubei Key Laboratory of Digital Textile Equipment, Wuhan Textile University, Wuhan 430200, China
2 School of Mechanical Engineering & Automation, Wuhan Textile University, Wuhan 430200, China
3 Hubei Engineering Technology Research Center of Functional Fiber Processing and Testing, Wuhan Textile University, Wuhan 430200, China |
|
|
|
|
Abstract The interfacial properties between fiber and matrix in natural fiber reinforced composites are poor and fluctuate greatly, which will have a signi-ficant influence on the final mechanical properties of the composites. In the paper, finite element models of unidirectional short flax fiber reinforced composites (SFFRC) using cohesive zone model were established to calculate the elastic constants of the unidirectional SFFRC with different interfacial stiffness. And then, the elastic constants of SFFRC with fiber random distribution were calculated by using the laminate plate theory, which are in good agreement with the tensile test results. On this basis, the effects of the interfacial stiffness (K0), the aspect ratio of fiber (ζ) and the factor of fiber distribution (λ) on the elastic constants of SFFRC were studied, and then a modified “rule-of-mixtures” (ROM) model for predicting the tensile modulus of SFFRC with randomly distributed fibers were proposed. The results show that the longitudinal tensile modulus (E1), transverse tensile modulus (E2) and longitudinal shear modulus (G12) of the composites decrease significantly with the decrease of K0 and increase gradually with the increase of ζ. The change of λ results in the change of fiber orientation angle and has different influence on the E1, E2 and G12 of the composites. The results of tensile modulus from the modified ROM model show good agreements with that from the tensile experiment when K0≤10 GPa/mm, indicating that the modified ROM model can effectively predict the tensile modulus of SFFRC with poor interface stiffness.
|
|
Published: 13 January 2022
Online: 2022-01-13
|
|
|
| Fund:This work was financially supported by the National Natural Science Foundation of China (51805181) and the Natural Science Foundation of Hubei Province (2020CFB389). |
|
|
[1] Zeng J C, Lu B, Zhang L W. Natural fiber composites. Chemical Industrial Press, China, 2005(in Chinese).
曾竟成, 鲁博, 张林文. 天然纤维复合材料. 化学工业出版社, 2005.
[2] Faruk O, Bledzki A K, Fink H, et al. Macromolecular Materials and Engineering, 2014, 299(1), 9.
[3] Xiong X S, Shen S Z, Hua L, et al. Journal of Reinforced Plastics and Composites, 2018, 37(9), 617.
[4] Kern W T, Kim W, Argento A, et al. Materials & Design, 2016, 106, 285.
[5] Sliseris J, Yan L B, Kasal B. Composites Part B: Engineering, 2016, 89, 143.
[6] Modniks J, Andersons J. Computational Materials Science,2010,50(2), 595.
[7] Modniks J, Andersons J. Composites Part B: Engineering, 2013, 54, 188.
[8] Hine P J, Lusti H R, Gusev A A. Composites Science and Technology, 2002, 62, 1445.
[9] Yan L B, Chouw N, Jayaraman K. Composites Part B: Engineering, 2014, 56, 296.
[10] Espinach F X, Granda L A, Tarrés Q, et al. Composites Part B: Engineering, 2014, 56, 296.
[11] Zhang D H, Milanovic N R, Zhang Y H, et al. Composites Part B: Engineering, 2014, 60, 186.
[12] Chen Z R, Yan W Y. Mechanics of Materials, 2015, 91, 119.
[13] Xiong X S, Shen Z S, Hua L, et al. Journal of Composite Materials, 2018, 52(27), 3701.
[14] Cox H L. British Journal of Applied Physics, 1952, 3(3), 72.
[15] Gu H B, Miao M H. Journal of Composite Materials, 2013, 48(24), 2993. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2022, Vol. 36 