METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
Research Progress on Void Swelling and Radiation-induced Segregation of Austenitic Stainless Steel |
LI Lianqi, YANG Zhanbing
|
School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract As society’s demand for energy increases, nuclear energy has become the focus of recent studies. China is strongly promoting the development of fourth generation nuclear reactor, which puts higher requirements on the performance of reactor structural materials. Austenitic stainless steel, as the core structure material,will undergo radiation damage under long-term service due to the intense radiation in the reactor core, especially the void swelling and radiation-induced segregation, which threaten the safety of the reactor operation. Void swelling and radiation-induced segregation of austenitic stainless steel are closely related to irradiation dose, irradiation temperature and alloy composition.Cold working and alloy elements are usually used to control void swelling. The 15-15Ti austenitic stainless steel shows potential for cladding of fast breeder reactor due to withstanding radiation doses over 100 dpa. However, the austenitic stainless steels developed by these two methods have not fully satisfied the requirement for service. Point defects govern the radiation damage effects; therefore, a more in-depth syste-matic and experimental analysis on the diffusion behavior of point defects is essential to understand the void swelling. Two controversial views were proposed on the mechanism of radiation-induced segregation, that is, vacancy mechanism and interstitial atomic mechanism. However, the radiation-induced segregation of austenitic stainless steel may be governed by both; subsequently, a more optimized kinetic model needs to be established for further study. In addition, recent studies show that the one dimension motion of radiation defects is related to radiation damage, but further research is essential to explore some experimental details. In the present paper, we review the influence factors of void swelling and radiation-induced segregation of austenitic stainless steel, the shortcomings of the existing controlling methods of void swelling, and the progress on the mechanism of radiation-induced segregation. Finally, we prospect the future research directions according to the existing problems of study on the anti-irradiation property of austenitic stainless steel.
|
Published: 12 March 2021
|
|
Fund:National Natural Science Foundation of China (51471027). |
About author:: Lianqi Li received his B.E. degree in University of Science and Technology Beijing in 2018. He is currently pursuing his master’s degree at the School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing under the supervision of asso-ciate professor Zhanbing Yang. His research has focused on radiation damage of austenitic stainless steel. Zhanbing Yang received his B.E. degree in University of Science and Technology Beijing in 2001 and received his Ph.D. degree in metallurgical engineering from the School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, in 2008. After six-year postdoctoral research at Hokkaido University, he is currently a associate professor in University of Science and Technology Beijing. His research interests are non-equilibrium phenomena and dynamic process in metal crystals under irradiation of high-energy particles and control of inclusions in steel. |
|
|
1 Yan S M. Foreign Nuclear News,2004(4),31(in Chinese). 闫淑敏.国外核新闻,2004(4),31. 2 Abram T, Ion S. Energy Policy,2008,36(12),4323. 3 Azevedo C R F. Engineering Failure Analysis,2011,18(8),1943. 4 Yang C, Fang C, Tong J J. Nuclear Power Engineering,2014,35(supplement 1),200(in Chinese). 杨辰,房超,童节娟.核动力工程,2014,35(增刊1),200. 5 Ye Q Z. Southern Energy Construction,2015,2(4),18(in Chinese). 叶奇蓁.南方能源建设,2015,2(4),18. 6 Yvon P, Carré F. Journal of Nuclear Materials,2009,385(2),217. 7 Deng P, Peng Q J, Han E H, et al. Acta Metallurgica Sinica,2017,53(12),1588(in Chinese). 邓平,彭群家,韩恩厚,等.金属学报,2017,53(12),1588. 8 Surh M P, Sturgeon J B, Wolfer W G. Journal of Nuclear Materials,2005,336(2-3),217. 9 Malaplate J, Michaut B, Renault-Laborne A, et al. Journal of Nuclear Materials,2019,517,201. 10 McMurtrey M D, Was G S, Patrick L, et al. Materials Science and Engineering: A,2011,528(10-11),3730. 11 Jiao Z, Was G S. Journal of Nuclear Materials,2011,408(3),246. 12 Wang M, Song M, Lear C R, et al. Journal of Nuclear Materials,2019,515,52. 13 Strafella A, Coglitore A, Fabbri P, et al. Frattura ed Integrità Strutturale,2017,11(42),352. 14 Yu B, Han W, Tong Z, et al. Materials,2019,12(16),2541. 15 Allen T R, Cole J I, Gan J, et al. Journal of Nuclear Materials,2005,342(1-3),90. 16 Horiki M, Yoshiie T, Huang S S, et al. Journal of Nuclear Materials,2013,442(1-3),S813. 17 Barcellini C, Harrison R W, Dumbill S, et al. Journal of Nuclear Mate-rials,2019,518,95. 18 Wan F R. Radiation damage of metal materials, Science Press, China,1993(in Chinese). 万发荣.金属材料的辐照损伤,科学出版社,1993. 19 Nordlund K. Journal of Nuclear Materials,2019,520,273. 20 Allen T R, Busby J T, Klueh R L, et al. JOM,2008,60(1),15. 21 Zinkle S J, Was G S. Acta Materialia,2013,61(3),735. 22 Cawthorne C, Fulton E J. Nature,1967,216(5115),575. 23 Was G S. Fundamentals of Radiation Materials Science: Metals and Alloys, Berlin, Heidelberg:Springer, 2007,pp.545. 24 Bellefon G M, Bertsch K M, Chancey M R, et al. Journal of Nuclear Materials,2019,523,291. 25 Kim H, Gigax J G, Fan J, et al. Journal of Nuclear Materials,2019,527,1. 26 Bae D S, Kim S K, Lee S P, et al. Fusion Engineering and Design,2006,81(8-14),969. 27 Kato T, Takahashi H, Izumiya M. Materials Transactions, JIM,1991,32(10),921. 28 Sekio Y, Yamashita S, Sakaguchi N, et al. Materials Transactions,2014,55(3),438. 29 David C, Panigrahi B K, Balaji S, et al. Journal of Nuclear Materials,2008,383(1-2),132. 30 Sekio Y, Sakaguchi N. Materials Transactions,2019,60(5),678. 31 Allen T R, Cole J I, Gan J, et al. Journal of Nuclear Materials,2005,342(1-3),90. 32 Yamashita S, Tachi Y, Akasaka N, et al. Journal of Nuclear Materials,2011,417(1-3),953. 33 Yang S B, Yang Z B, Wnag H, et al. Nonferrous Metals Science and Engineering,2017,8(2),24(in Chinese). 杨苏冰,杨占兵,王会,等.有色金属科学与工程,2017,8(2),24. 34 Yang Z B, Yang S g, Li L Q. China Metallurgy,2020,30(3),35(in Chinsese). 杨占兵,杨苏冰,李连奇.中国冶金,2020,30(3),35. 35 Yoshiie T, Cao X Z, Sato K, et al. Journal of Nuclear Materials,2011,417(1-3),968. 36 Yoshiie T, Sato K, Cao X, et al. Journal of Nuclear Materials,2012,429(1-3),185. 37 Garner F A, Black C A, Edwards D J. Journal of Nuclear Materials,1997,245(2-3),124. 38 Rouxel B, Bisor C, De Carlan Y, et al. EPJ Nuclear Sciences & Techno-logies,2016,30(2),1. 39 Wan F R. Chinese Journal of Engineering, DOI: 10.13374/j.issn2095-9389.2020.02.05.001(in Chinese). 万发荣.工程科学学报, DOI: 10.13374/j.issn2095-9389.2020.02.05.001. 40 Schibli R, Schäublin R. Journal of Nuclear Materials,2013,442(1-3),S761. 41 Etienne A, Radiguet B, Cunningham N J, et al. Journal of Nuclear Materials,2010,406(2),244. 42 Kaur N, Deng C, Ojo O A. Computational Materials Science,2020,179,109685. 43 Takahashi H, Hashimoto N. Materials Transactions, JIM,1993,34(11),1027. 44 Watanabe S, Sakaguchi N, Hashimoto N, et al. Journal of Nuclear Materials,1995,224(2),158. 45 Takahashi H, Sakaguchi N, Hashimoto N, et al. Materials Science Forum,1996,207-209,561. 46 Fukuya K, Nakano M, Fujii K, et al. Journal of Nuclear Science and Technology,2004,41(6),673. 47 Jin H H, Hwang S S, Choi M J, et al. Journal of Nuclear Materials,2019,513,271. 48 Was G S, Wharry J P, Frisbie B, et al. Journal of Nuclear Materials,2011,411(1-3),41. 49 Simonen E P, Bruemmer S M. JOM,1998,50(12),52. 50 Allen T R, Busby J T, Was G S, et al. Journal of Nuclear Materials,1998,255(1),44. 51 Allen T R, Was G S. Acta Materialia,1998,46(10),3679. 52 Fournier L, Sencer B H, Was G S, et al. Journal of Nuclear Materials,2003,321(2-3),192. 53 Sekio Y, Yamashita S, Sakaguchi N, et al. Journal of Nuclear Materials,2015,458,355. 54 Watanabe S, Sakaguchi N, Kurome K, et al. Journal of Nuclear Mate-rials,1997,240(3),251. 55 Stepanov I A, Pechenkin V A, Konobeev Y V. Journal of Nuclear Mate-rials,2004,329-333,1214. 56 Tucker J D, Allen T R, Najafabadi R, et al. In: Conference Record of the International Conference on Mathematics, Computational Methods & Reactor Physics. New York,2009,pp.891. 57 Sakaguchi N, Takahashi H, Ichinose H. Materials Transactions,2005,46(3),440. 58 Yang Z, Sakaguchi N, Watanabe S, et al. Scientific Reports,2011,1,190. 59 Yang Z, Watanabe S. Acta Materialia,2013,61(8),2966. 60 Yang Z, Watanabe S, Kato T. Scientific Reports,2013,3,1201. 61 Yang S B, Yang Z B, Wang H. Chinese Journal of Engineering,2017,39(6),903(in Chinese). 杨苏冰,杨占兵,王会.工程科学学报,2017,39(6),903. 62 Yang S, Yang Z B, Wang H, et al. Journal of Nuclear Materials,2017,488,215. 63 Watanabe S, Takamatsu Y, Sakaguchi N, et al. Journal of Nuclear Materials,2000,283-287,152. 64 Sekine M, Sakaguchi N, Endo M, et al. Journal of Nuclear Materials,2011,414(2),232. 65 Sakaguchi N, Endo M, Watanabe S, et al. Journal of Nuclear Materials,2013,434(1-3),65. 66 Qu X J, Yang Z B, Yang S B. Surface Technology,2019,48(5),201(in Chinese). 曲晓健,杨占兵,杨苏冰.表面技术,2019,48(5),201. 67 Kawai M, Kurishita H, Kokawa H, et al. Journal of Nuclear Materials,2012,431(1-3),16. |
|
|
|