INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
Photoelectrochemical Properties of Hydrogen Reduced TiO2 Film by HF Corrosion |
YU Lianqing1, YANG Qianlong1, ZHU Haifeng2, DUAN Lijie1, ZHAO Xingyu1, WANG Yankun1
|
1 College of Material Science and Engineering, China University of Petroleum (East China), Qingdao 266580, China 2 College of Science,China University of Petroleum (East China), Qingdao 266580, China |
|
|
Abstract TiO2 is a low cost and stable semiconductor. It is widely studied in photocatalytic water splitting, waste-water treatment and so on. However, it can only absorb ultraviolet light limiting its practical application. HF solution was used to etch titanium sheet. Afterwards, TiO2 nano-film were reduced in H2 atmosphere under high temperature. The TiO2 nano-film were tested by XRD, SEM and electrochemical workstation to obtain phase composition, microstructures and photo-response current, linear sweep voltammetry curve, electrochemical impedance spectra, respectively. The results show that TiO2 nano-film exposes more rutile (101) facet through HF treatment. And the photoelectrochemical properties apparently promote after H2 treatment, the photocurrent density is up to 1.04 mA/cm2. It is 11.5 times higher than that of pure nano-film, and 2.97 times higher than that of without H2 reduction. Meanwhile, the maximum photoconversion efficiency reached 70% improvement.
|
Published: 12 November 2021
|
|
Fund:Natural Science Foundation of Shandong Province (ZR2020ME010). |
Corresponding Authors:
iyy2000@163.com
|
About author:: Lianqing Yu received his doctor’s degree in 2007 from Zhejiang University. He is a professor of China University of Petroleum (East China). His focus is on the research of permanent magnets, and photo(electro) cata-lysis hydrogen production. |
|
|
1 David P, Rodrigue G, Wang T, et al. BioScience,1994,44(8),536. 2 Mathews Nripan, Varghese Binni, Sun Cheng, et al. Nanoscale,2010,2(10),1984. 3 Guo Honghui, Zhou Jianzhang, Lin Zhonghua. Electrochemistry Communications,2008,10(1),146. 4 Liao L, Lu H B, Li J C, et al. The Journal of Physical Chemistry C,2007,111(5),1900. 5 Liu Jinping, Li Yuanyuan, Fan Hongjin, et al. Chemistry of Materials,2010,22(1),212. 6 Fujishima Akira, Honda Kenichi. Nature,1972,238(5358),37. 7 Wang Gongming, Wang Hanyu, Ling Yichuan, et al. Nano Letters,2011,11(7),3026. 8 Liu Lei, Chen Xiaobo. Chemical Reviews,2014,114(19),9890. 9 Li Sheng, Qiu Jingxia, Ling Min, et al. ACS Applied Materials & Interfaces,2013,5(21),11129. 10 Lee J, Christopher O M, Warren S C, et al. Nature Materials,2008,7,222. 11 Yu Lianqing, Zhi Qianqian, Huang Chengxing, et al. Journal of Nanoscience and Nanotechnology,2015,15(9),6576. 12 Martra Gianmario. Applied Catalysis A: General,2000,200(1),275. 13 Li Guisheng, Wu Ling, Li Fang, et al. Nanoscale,2013,5(5),2118. 14 Zhang Yaping, Zhu Haifeng, Yu Lianqing,et al. Materials Research Express,2018,5(4),045014. 15 Yu Lianqing, He Jiandong, Huang Chengxing, et al. RSC Advances,2017,7(86),54485. 16 Yu Lianqing, Li Ming, Huang Chengxing,et al. Materials Letters,2018,216,239. 17 Chen Xiaobo, Liu Lei, Yu Peter, et al. Science,2011,331(6018),746. 18 Gong D, Grimes C A, Varghese O K, et al. Journal of Materials Research,2001,16(12),3331. 19 Paulose M, Shankar K, Yoriya S, et al. Journal of Physical Chemistry B,2006,110(33),16179. 20 Tae Woo Kim, Kyoung-Shin Choi. Science,2014,343(6174),990. 21 Zhang Wenhua, Yang Jinlong, Luo Yi, et al. Journal of Chemical Phy-sics,2008,129(6),064703. 22 Schladt T D, Graf T, Aetukuri N B,et al. ACS Nano,2013,7(9),8074. |
|
|
|