Abstract Copper slag (CS) is the by-product of the smelting and refining process of copper. It has been estimated that the production of 1 t blister copper generates 2.2 t slag, and the global copper slag emissions reached 51.7 million tonnes in 2017. As the most common treatment for CS, the landfill not only occupies a great quantity of soils, but also lead to severe ecological environment pollution all around due to the heavy metals in CS. CS, especially the water-quenched one, contains large vitreous fraction, which can be used as the concrete admixture instead of fly ash, slag and other mineral admixtures to relieve the shortage of admixture in some areas. This review summarizes the influence of CS powder on the workability, mechanical properties and durability of concrete, analyzes the environmental safety of copper slag as admixture, and points out several issues that should be paid attention to in the use of copper slag as admixture. It provides a reference for large scale application of copper slag powder in concrete industry.
Recent researches revealed that there is high vitreous fraction in water-quenched CS with favorable activity. The vitreous content in cooling CS is low, nevertheless, it presents acceptable activity. Owing to the high heavy metal composition and low activity, the impact of CS on the workability, mechanical properties and durability of concrete is much more complicated than that of common admixtures like slag and fly ash, which hinders the application of copper slag powder as admixture in concrete.
Although there are different opinions about the effect of CS, it is generally believed that the utilization of CS powder as admixtures can reduce heat release, water consumption and improve workability, while increase the bleeding rate. Thanks to the low activity and high heavy metal content, the CS powder shows notable retarding effect, yet the extension of setting time caused by using large amount of CS powder can be controlled in most cases. The insufficient early strength of concrete resultes from CS powder can be alleviated by adding activators, improving fineness, and reducing W/B ratio. The negative effect of the CS powder on the strength can gradually ease with age, and even it is beneficial to concrete strength after a certain period of time. Besides, CS powder can also improve the elastic modulus of concrete and reduce shrinkage, and has no obvious adverse effect on the fracture resistance of concrete. However, the role of CS powder on the brittleness of concrete is still controversial. CS powder is helpful to reduce harmful pores like capillary pores and further reduce the water absorption rate and amount, which result in a improved durability of concrete. In the hydration reaction of CS powder, owing to the increment of C-S-H gel formation, the interfacial transition zone is optimized, and the anti-carbonation, sulfate resistance and chloride ion penetration resistance of concrete are improved.

Key words： copper slag concrete mineral admixture

Published: 20 December 2018

CLC number:

TU528.041

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HE Wei
	ZHOU Yuqi
	WANG Qiang

Cite this article:

HE Wei,ZHOU Yuqi,WANG Qiang. Advances in Copper Slag as Concrete Admixture[J]. Materials Reports, 2018, 32(23): 4125-4134.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.23.014 OR http://www.mater-rep.com/EN/Y2018/V32/I23/4125

1 International Energy Agency.Cement technology roadmap 2009-carbon emssions reductions up to 2050[R].Paris: International Energy Agency,2009.
2 Hoenig V, Hoppe H, Emberger B.Carbon capture technology-options and potentials for the cement industry[R].Duesseldorf: European Cement Research Academy,2007.
3 U.S.Geological Survey. Mineral commodity summaries-2018[R].U.S.: Geological Survey,2018.
4 Schneider M.Developments in the global cement market[J].Cement International,2014,12:35.
5 Von B, Siddique R, Khan M I.Supplementary cementing materials[M].Heidelberg: Springer,2011.
6 Boakye D M.Durability and strength assessment of copper slag concrete[D].Johannesburg: University of the Witwatersrand,2014.
7 Gorai B, Jana R K, Premchand. Characteristics and utilisation of copper slag—A review[J].Resources Conservation and Recycling,2003,39(4):299.
8 Das B M, Tarquin A J, Jones A D, et al.Geotechnical properties of copper slag[R].Washington, D.C.: Transportation Research Record,1983.
9 Ayano T, Sakata K.Durability of concrete with copper slag fine aggregate[C]∥5th CANMET/ACI International Conference on Durability of Concrete. Tokyo, Japan,2000:141.
10 Khanzadi M, Behnood A.Mechanical properties of high-strength concrete incorporating copper slag as coarse aggregate[J].Construction and Building Materials,2009,23(6):2183.
11 Moura W, Masuero A, Molin D, et al.Concrete performance with admixtures of electrical steel slag and copper concerning mechanical properties[C]∥2nd CANMET/ACI International Conference on High-Performance. Pairs,1999:81.
12 宋军伟,陈俊.铜矿渣掺合料对混凝土力学性能影响试验研究[J].混凝土与水泥制品,2013(8):81.
13 Al-Jabri K S, Taha R A, Al-Hashmi A, et al. Effect of copper slag and cement by-pass dust addition on mechanical properties of concrete[J].Construction and Building Materials,2006,20(5):322.
14 Alnuaimi A.Effects of copper slag as a replacement for fine aggregate on the behavior and ultimate strength of reinforced concrete slender columns[J].Journal of Engineering Research,2012,9(2):90.
15 Wu W, Zhang W, Ma G.Optimum content of copper slag as a fine aggregate in high strength concrete[J].Materials and Design,2010,31(6):2878.
16 Elshkaki A, Graedel T E, Ciacci L, et al.Copper demand, supply, and associated energy use to 2050[J].Global Environmental Change,2016,39:305.
17 Li F.The pozzolanic activity of granulated copper slay[J].Journal of Fuzhou University (Natural Sciener),1999(2):87(in Chinese).
李锋. 水淬铜渣的火山灰活性[J].福州大学学报(自然科学版),1999(2):87.
18 Douglas E, Mainwaring P R.Hydration and pozzolanic activity of nonferrous slags[J].American Ceramic Society Bulletin,1985,64(5):700.
19 Baragano J R, Rey P.The study of a non-traditional pozzolan: Copper slags[C]∥7th International Congress on the Chemistry of Cement. Paris,1980:37.
20 Pan W C, Wang T D.A study on the components and cementitious properties of activated copper slag[J].Journal of South China University of Technology (Natural Science),1993(1):91(in Chinese).
潘伟才,王天頔.活化铜矿渣的组成及胶凝特性的研究[J].华南理工大学学报(自然科学版),1993(1):91.
21 Najimi M, Pourkhorshidi A R.Properties of concrete containing copper-slag-waste[J].Magazine of Concrete Research,2011,63(8):605.
22 Rojas M I S D, Rivera J, Frías M, et al. Use of recycled copper slag for blended cements[J].Journal of Chemical Technology and Biotechnology,2008,83(3):209.
23 Shi C, Meyer C, Behnood A, et al.Utilization of copper slag in cement and concrete[J].Resources Conservation and Recycling,2008,52(10):1115.
24 Zhao K, Cheng X L, Qi Y H, et al.Characteristics of water quenched copper-containing slag and separation of iron and silicon from it[J].The Chinese Journal of Process Engineering,2012,12(1):38(in Chinese).
赵凯,程相利,齐渊洪,等.水淬铜渣的矿物学特征及其铁硅分离[J].过程工程学报,2012,12(1):38.
25 Alp I, Deveci H, Süngün H.Utilization of flotation wastes of copper slag as raw material in cement production[J].Journal of Hazardous Materials,2008,159(2-3):390.
26 Zhang L N.Study on selective precipitation valuable constituent in copper smelting slags[D].Shenyang: Northeastern University,2005(in Chinese).
张林楠. 铜渣中有价组分的选择性析出研究[D].沈阳:东北大学,2005.
27 Liu G, Zhu R.Study of China’s current copper slag on the use of resources[J]. Mining and Metallurgy,2008,17(3):59(in Chinese).
刘纲,朱荣.当前我国铜渣资源利用现状研究[J].矿冶,2008,17(3):59.
28 Zhang L N, Zhang L, Wang M Y, et al.Treatment and resourceful disposal of copper slag[J].Multipurpose Utilization of Mineral Resources,2005(5):22(in Chinese).
张林楠,张力,王明玉,等.铜渣的处理与资源化[J].矿产综合利用,2005(5):22.
29 Murari K, Siddique R, Jain K K.Use of waste copper slag, a sustainable material[J].Journal of Material Cycles and Waste Management,2015,17(1):13.
30 Li F.Study on the theory and application of water-quenched copper slag as concrete component[D].Xi’an: Xi’an University of Architecture and Technology,1990(in Chinese).
李锋. 水淬铜渣作为混凝土组分的理论和应用研究[D].西安:西安建筑科技大学,1990.
31 Emery J J.Manitoba slags, deposits, characterization, modifications, potential utilization[R].Toronto: Geotechnical Engineering Limited,1986.
32 Hughes M L, Haliburton T A.Use of zinc smelter waste as highway construction material[C]∥52nd Annual Meeting of the Highway Research Board. Washington, USA,1973:16.
33 Tixier R.Microstructural development and sulfate attack modeling in blended cement-based materials[D].Phoenix: Arizona State University,2000.
34 Nie Q, Cheng L, Niu W G.Effect of different admixtures on cement hydration heat[J].Coal Ash,2007,19(3):3(in Chinese).
聂强,陈磊,牛文阁.不同掺和料对水泥水化热的影响[J].粉煤灰,2007,19(3):3.
35 侯贵华,沈晓冬,许仲梓.掺杂氧化铜的硅酸三钙早期水化过程的研究[C]∥第九届全国水泥和混凝土化学及应用技术会议.广州,2005:282.
36 Wang X, Yan B L, Wang L, et al.The research on the mechanism of solidification and stability of ettringite doped Cr⁶+ and Cu²+[J].Bulletin of the Chinese Ceramic Society,2013,32(2):12(in Chinese).
王昕,颜碧兰,汪澜,等.钙矾石对Cr⁶+和Cr²+的固化及稳定性[J].硅酸盐通报,2013,32(2):12.
37 Afshoon I, Sharifi Y.Ground copper slag as a supplementary cementing material and its influence on the fresh properties of self-consolidating concrete[J].The IES Journal Part A: Civil and Structural Engineering,2014,7(4):229.
38 Kolovos K G, Barafaka S, Kakali G, et al.CuO and ZnO addition in the cement raw mix: Effect on clinkering process and cement hydration and properties[J].Ceramics Silikaty,2005,49(3):205.
39 Najimi M, Sobhani J, Pourkhorshidi A R.Durability of copper slag contained concrete exposed to sulfate attack[J].Construction and Building Materials,2011,25(4):1895.
40 Arliguie G, Grandet J.Etude de l’hydratation du ciment en presence de zinc influence de la teneur en gypse[J].Cement and Concrete Research,1990,20(3):346.
41 Yousuf M, Mollah A, Hess T R, et al.An FTIR and XPS investigations of the effects of carbonation on the solidification/stabilization of cement based systems—Portland type V with zinc[J].Cement and Concrete Research,1993,23(4):773.
42 Ma B G, Wu B, Li X G, et al.Influence of Zn²+ on the hydration properties of the sulphoaluminate and ordinary Portland cement[J].Journal of Wuhan University of Technology,2010(14):30(in Chinese).
马保国,吴贝,李相国,等.Zn²+对硫铝酸盐和硅酸盐水泥水化性能的影响[J].武汉理工大学学报,2010(14):30.
43 施惠生,施慧聪.硫化物对水泥基材料中锌的控制研究[J].水泥,2006(2):15.
44 Ouki S K, Hills C D.Microstructure of Portland cement pastes containing metal nitrate salts[J].Waste Management,2002,22(2):147.
45 Sahu R M, Sadangi M, Kuchya S P, et al.Use of copper slag[J].International Cement Review,2011(2011):58.
46 Onuaguluchi O, Eren Ö.Some properties of cement-copper tailings pastes and mortars[C]∥International Conference on Solid Waste-Moving Towards Sustainable Resource Management. Hong Kong, China,2011:276.
47 Onuaguluchi O, Gharagozloo A, Iravanian A.Utilization of copper processing waste as partial replacement of cement in concrete[C]∥9th International Congress on Advances in Civil Engineering. Trabzon, Turkey,2010:1.
48 Onuaguluchi O, Eren Ö.Copper tailings as a potential additive in concrete: Consistency, strength and toxic metal immobilization properties[J].Indian Journal of Engineering and Materials Sciences,2012,19(2):79.
49 Douglas E, Mainwaring P R, Hemmings R T.Pozzolanic properties of Canadian non-ferrous slags[J].Journal of the American Concrete Institute,1986,83(2):342.
50 Taeb A, Faghihi S.Utilization of copper slag in the cement industry[J].ZKG International,2002,55(4):98.
51 Ravindrarajah R S, Tam C T.Properties of concrete containing low-calcium fly ash under hot and humid climate[C]∥3rd International Conference Proceedings. Fly Ash, Silica Fume, Slag, and Natural Pozzolans in Concrete. Trondheim, Norway,1989:139.
52 Zain M F M, Islam M N, Radin S S, et al. Cement-based solidification for the safe disposal of blasted copper slag[J].Cement and Concrete Composites,2004,26(7):845.
53 Moura W A, Gonçalves J P, Lima M B L. Copper slag waste as a supplementary cementing material to concrete[J].Journal of Mate-rials Science,2007,42(7):2226.
54 Al-Jabri K, Shoukry H.Use of nano-structured waste materials for improving mechanical, physical and structural properties of cement mortar[J].Construction and Building Materials,2014,73:636.
55 Brindha D, Sureshkumar P.Buckling strength of RCC column incorporating copper lag as partial replacement for cement[C]∥ National Conference on Emerging Trends in Civil Engineering (NCETCE-10). Tiruchengod, India,2010:146.
56 Lee D U, Jung Y J, Kim Y S.A study on the corrosion resistance of concrete containing copper slag[J].Journal of the Korea Institute for Structural Maintenance and Inspection,2007,11(5):189.
57 Song J W, Fang K H, Zhu J L, et al.Experimental study on strength and brittleness of copper slag concrete[J].Journal of Wuhan University of Technology,2013,35(10):33(in Chinese).
宋军伟,方坤河,朱街禄,等.铜矿渣混凝土强度与脆性试验研究[J].武汉理工大学学报,2013,35(10):33.
58 Tixier R, Arino-Moreno A, Mobasher B.Properties of cementitious mixture modified by copper slag[C]∥Symposium: HH, Structure Property Relationships in Hardened Cement Paste and Composites. Tucson, American,1996.
59 邹伟斌,胡新明.铜矿渣、石灰石、矿渣复合硅酸盐水泥[J].江西建材,1998(2):27.
60 Mobasher B, Devaguptapu R, Arino A M.Effect of copper slag on the hydration of blended cementitious mixtures[C]∥Materials for the New Millennium. Washington, American,1996:1677.
61 戴映清,严生,沈晓东.铜渣道路水泥的研究[J].江苏建材,1998(2):29.
62 Singh J, Singh J, Kaur M.Copper slag blended cement: An environmental sustainable approach for cement industry in India[J].Current World Environment,2016,11(1):186.
63 Mohsenian H, Sohrabi M R.Compering the effect of using the copper blast furnace slag and Taftan pozzolan on concrete properties[C]∥3rd International Conference on Concrete and Development. Tehran, Iran,2009:181.
64 Ariño A M, Mobasher B.Effect of ground copper slag on strength and toughness of cementitious mixes[J].ACI Materials Journal,1999,96(1):68.
65 Moosberg H, Lagerblad B, Forssberg E.The use of by-products from metallurgical and mineral industries as filler in cement-based materials[J].Waste Management and Research the Journal of the International Solid Wastes and Public Cleansing Association Iswa,2003,21(1):29.
66 Yin H, Dong B Q, Ding Z, et al.Study of the water absorbtivity and permeability for concrete[J].Low Temperature Architecture Technology,2009,31(2):4(in Chinese).
殷慧,董必钦,丁铸,等.混凝土的渗水、吸水特性研究[J].低温建筑技术,2009,31(2):4.
67 赵铁军. 混凝土渗透性[M].北京:科学出版社,2006.
68 Wu Z W.An approach to the recent trends of concrete science and technology[J].Journal of the Chinese Ceramic Society,1979(3):82(in Chinese).
吴中伟. 混凝土科学技术近期发展方向的探讨[J].硅酸盐学报,1979(3):82.
69 Alexander M G, Jaufeerally H, Mackechnie J R.Structural and durability properties of concrete made with Corex slag[M].Cape Town: University of Cape Town,2003.
70 Brown P W.An evaluation of the sulfate resistance of cements in a controlled environment[J].Cement and Concrete Research,1982,11(5):719.
71 Alter H.The composition and environmental hazard of copper slags in the context of the Basel Convention[J].Resources Conservation and Recycling,2005,43(4):353.
72 Environment Agency of GOV.UK. Guidance on the classification and assessment of waste[R].Bristol: Environment Agency of GOV.UK,2015.
73 Vitkova M, Ettler V, Mihaljevic M, et al.Effect of sample preparation on contaminant leaching from copper smelting slag[J].Journal of Hazardous Materials,2011,197(6):417.
74 Johnson E A, Oden L L, Sanker P E.Results of EPA extraction procedure toxicity test applied to copper reverberatory slags (Report of investigations 8648)[R].Reno: U.S Bureau of Mines,1982.
75 Lim T T, Chu J.Assessment of the use of spent copper slag for land reclamation[J].Waste Management and Research the Journal of the International Solid Wastes and Public Cleansing Association Iswa,2006,24(1):67.
76 Shanmuganathana P, Lakshmipathiraja P, Srikantha S, et al.Toxi-city characterization and long-term stability studies on copper slag from the ISASMELT process[J].Resources Conservation and Recycling,2008,52(4):601.
77 Jarosíková A, Ettler V, Mihaljevič M, et al.The pH-dependent leaching behavior of slags from various stages of a copper smelting process: Environmental implications[J].Journal of Environmental Management,2017,187:178.
78 Karamanov A, Aloisi M, Pelino M.Vitrification of copper flotation waste[J].Journal of Hazardous Materials,2007,140(1-2):333.
79 Gougar M L D, Scheetz B E, Roy D M. Ettringite and C-S-H Portland cement phases for waste ion immobilization: A review[J].Waste Management,1996,16(4):295.
80 Li X D, Poon C S, Sun H, et al.Heavy metal speciation and leaching behaviors in cement based solidified/stabilized waste materials[J].Journal of Hazardous Materials,2001,82(3):215.
81 Batchelor B.Overview of waste stabilization with cement[J].Waste Management,2006,26(7):689.
82 Rojas M I S D, Rivera J, Frías M, et al. Leaching characteristics of blended mortars made of copper slags[C]∥8th International Conference on Fly Ash, Silica Fume, Slag and Natural Pozzolans in Concrete. Las Vegas, USA,2004:925.