纳米复合粉体分散剂的制备及其分散性能

doi:10.11896/j.issn.1005-023X.2018.22.006

Abstract
Figure/Table
References
Related Citation (1)

Download:

Full Text ( PDF ) (2763KB)
Export: BibTeX | EndNote (RIS)

Abstract Nanomaterials are widely used in the fields of electronics, medicine, polymer materials and cement based materials. In order to solve the problem of dispersing of nanomaterials in cement based materials, a particular molecular structure of nano-particle dispersing agent (NDA) was synthesized by free radical copolymerization of acrylic acid (AA), methacryloxyethyltrimethyl ammonium chloride (DMC) and isopentenol polyoxyethylene ether (IPEG). The molecular structure of NDA was characterized by FTIR, ¹H-NMR and GPC. Effect of the dosage of NDA on the rheological performance was investigated by measurements of the visco-sity of nano composite powder slurry. The results indicated that NDA was prepared successfully by the AA, DMC and IPEG, and the best dispersion properties of NDA was obtained when the molar ratio of AA∶DMC∶IPEG was 4.5∶0.3∶1 and the dosage of initiator was 2%. The viscosity of nano composite powder slurry can reduce to 3 091 MPa·s. Meanwhile, the results of zeta potential and TOC indicated that the better dispersion performance of NDA was attributed to the electrostatic adsorption action of positively groups and negatively groups on the surface of nano composite powder, and then depended on the steric hindrance action of polyoxye-thylene side chains (PEO).

Key words： nano composite powder dispersing agent preparation and characterization degree of dispersion mechanism of action

Published: 21 December 2018

CLC number:

TQ172.4+6

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	GAO Ruijun
	YAO Yan
	WU Hao
	WANG Ling

Cite this article:

GAO Ruijun,YAO Yan,WU Hao, et al. Preparation and Dispersion Properties of Nano Composite Powder Dispersing Agent[J]. Materials Reports, 2018, 32(22): 3868-3874.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.22.006 OR http://www.mater-rep.com/EN/Y2018/V32/I22/3868

1 Blanco E, Shen H, Ferrari M. Principles of nanoparticle design for overcoming biological barriers to drug delivery[J]. Nature Biotechnology,2015,33:941.
2 Yang G F, Ke Y C, Liu W K. Research on the optical properties and crystallization behavior of PET/SiO₂ nanocomposites[J]. Polymer Materials Science and Engineering,2007,23(4):94(in Chinese).
杨光富,柯扬船,刘维康.PET/SiO₂纳米复合材料的光学性能和结晶成核行为[J].高分子材料科学与工程,2007,23(4):94.
3 Cheng S F, Gary S G. Dispersing nanoparticles in a polymer film via solvent evaporation[J]. ACS Macro Letters,2016,5(6):694.
4 Ramezanzadeh B, Haeri Z, Ramezanzadeh M. A facile route of ma-king silica nanoparticles-covered graphene oxide nanohybrids (SiO₂-GO), fabrication of SiO₂-GO/epoxy composite coating with superior barrier and corrosion protection performance[J]. Chemical Enginee-ring Journal,2016,303:511.
5 Gu Y, Ran Q P, Shu X, et al. Synthesis of nanoSiO₂@PCE core-shell nanoparticles and its effect on cement hydration at early age[J]. Construction and Building Materials,2016,114:673.
6 Zapata L E, Portela G, Suárez O M, et al. Rheological performance and compressive strength of superplasticized cementitious mixtures with micro/nano-SiO₂ additions[J]. Construction and Building Materials,2013,41(41):708.
7 Senff L, Hotza D, Wellington L, et al. Mortars with nano-SiO₂ and micro-SiO₂ investigated by experimental design[J]. Construction and Building Materials,2010,24(8):1432.
8 Suzuki T S, Sakka Y, Nakano K, et al. Effect of ultrasonication on the microstructure and tensile elongation of zirconia-dispersed alumina ceramics prepared by colloidal processing[J]. Journal of the American Ceramic Society,2001,84(9):2132.
9 Li L, Zhang Q L, Liu Y Z, et al. Fabrication and factors of stabilization of pickering emulsion based on TiO₂-SA-Arg Nanoparticles[J]. Polymer Materials Science and Engineering,2016,32(8):162(in Chinese).
李磊,张巧玲,刘有智,等.SiO₂-SA-Arg纳米颗粒稳定Pickering乳液的制备及稳定因素[J].高分子材料科学与工程,2016,32(8):162.
10 Yan C, Li J X, Pan Z D. Progress in the surface modification research of nano-TiO₂ particles[J]. Journal of Ceramics,2002,23(1):62(in Chinese).
鄢程,李竟先,潘志东.纳米TiO2颗粒的表面改性研究进展[J].陶瓷学报,2002,23(1):62.
11 Zhao Y Z, Yu Z P, Zhu S H, et al. Surface modification and biomedical application of silica nanoparticles[J]. The Chinese Journal of Nonferrous Metals,2010,20(7):1412(in Chinese).
赵颜忠,余智萍,朱晒红,等.硅纳米颗粒的表面改性及生物应用[J].中国有色金属学报,2010,20(7):1412.
12 Li D, Muller M B, Gilje S, et al. Processable aqueous dispersions of graphene nanosheets[J]. Nature Nanotechnology,2008,3:101.
13 Konsta-Gdoutos M S, Metaxa Z S, Shah S P. Highly dispersed carbon nanotube reinforced cement based materials[J]. Cement and Concrete Research,2010,40(7):1052.
14 Liang W Y. Study on the dispersion of nano-sized CaCO₃ in the aqueous system and its mechanism[D]. Wuxi: Jiangnan University,2008(in Chinese).
梁文玉.纳米CaCO₃在水中的分散及其机理研究[D].无锡:江南大学,2008.
15 Collins F, Lambert J, Duan W H. The influences of admixtures on the dispersion, workability, and strength of carbon nanotube-OPC slurry mixtures[J]. Cement & Concrete Composites,2012,34(2):201.
16 Zou B, Chen S J, Korayem A H, et al. Effect of ultrasonication energy on engineering properties of carbon nanotube reinforced cement pastes[J]. Carbon,2015,85:212.
17 Zou H, Wu S S, Shen J. Polymer/silica nanocomposites: Preparation, characterization, properties, and applications[J]. Chemical Reviews,2008,108(9):3893.
18 潘祖仁.高分子化学[M].第五版.北京:化学工业出版社,2014.