原位反应在钎焊中的应用

doi:10.11896/cldb.22060183

Abstract
Figure/Table
References
Related Citation (4)

Download:

Full Text ( PDF ) (7910KB)
Export: BibTeX | EndNote (RIS)

Abstract As a new composite material preparation technology, in situ synthesis has become a research hotspot in recent years due to its simple operation, low cost, good compatibility with other processes and easy promotion.The adoption of in situ reaction in brazing technology has also been widely studied, and found to be able to effectively solve the problems such as poor forming performance, large residual stress and difficult wetting of base metal during the preparation and use of brazing filler metal. In this paper, the current application of in situ reaction in brazing filler metal synthesis is reviewed. Firstly, the research on in situ fusion of low melting point and high strength brazing filler metal by changing the forming process is introduced, and the common forming processes, such as layered composite, extrusion composite, adding metal powder core and surface plating, are summarized. After that, the research on effective connection of dissimilar materials by using in situ reaction to generate composite filler metal reinforcement phase is introduced, Finally, the existing problems of in situ synthesis of brazing filler metal at the emerging stage are pointed out, and the future research directions are prospected.

Key words： in situ reaction brazing filler metal reinforcement phase dissimilar material joining

Published: 10 December 2023 Online: 2023-12-08

CLC number:

TG454

Fund:National Key Research and Development Program (2021YFB3401101).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	QIAO Ruilin
	LONG Weimin
	ZHONG Sujuan
	LIAO Zhiqian
	FAN Xigang
	WEI Yongqiang

Cite this article:

QIAO Ruilin,LONG Weimin,ZHONG Sujuan, et al. Application of in Situ Reactions in Brazing[J]. Materials Reports, 2023, 37(23): 22060183-8.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22060183 OR http://www.mater-rep.com/EN/Y2023/V37/I23/22060183

1 Li Y X, Chen C, Yi R X, et al. Journal of Manufacturing Processes, 2020, 60, 608.
2 Matthew W, Jack W, Russell G. International Materials Reviews, 2020, 65(5), 257.
3 Ahn B. Metals, 2021, 11(7), 1037.
4 Zhang Y, Wang X M, Ge Y X, et al. Hot Working Technology, 2014, 43(24), 23 (in Chinese).
张宇, 王小美, 葛禹锡, 等. 热加工工艺, 2014, 43(24), 23.
5 Wang Z Y, Ba J, Ma Q, et al. Journal of Netshape Forming Engineering, 2018, 10(1), 82 (in Chinese).
王泽宇, 霸金, 马蔷, 等. 精密成形工程, 2018, 10(1), 82.
6 Chen B M, Zhang Z Y, Wang M X, et al. Advanced Materials Research, 2010, 160, 35.
7 Lin K Y, Wang W H, Jing R S, et al. Chemicals & Chemistry, 2017, 88, 887.
8 Zhang H, Zhu H G. In: 2nd Annual International Conference on Advanced Material Engineering (AME 2016). Wuhan, 2016,pp. 131.
9 Popov V A, Burghammer M, Rosenthal M, et al. Composites Part B, 2018, 145, 57.
10 Long W M, Zhang G X, Zhang Q K, et al. Welding & Joining, 2015(7), 6 (in Chinese).
龙伟民, 张冠星, 张青科, 等. 焊接, 2015(7), 6.
11 Long W M, Zhang G X, Zhang Q K. Scripta Materialia, 2015, 110, 41.
12 Long W M, Zhang G X, Zhang Q K, et al. Transactions of the China Welding Institution, 2015, 36(11), 1 (in Chinese).
龙伟民, 张冠星, 张青科, 等. 焊接学报, 2015, 36(11), 1.
13 Long W M, Dong B W, Zhang Q K, et al. Transactions of the China Welding Institution, 2017, 38(1), 1 (in Chinese).
龙伟民, 董博文, 张青科, 等. 焊接学报, 2017, 38(1), 1.
14 Long W M, Lu Q B, He P, et al. Journal of Materials Engineering, 2016, 44(6), 17 (in Chinese).
龙伟民, 路全彬, 何鹏, 等.材料工程, 2016, 44(6), 17.
15 Wang M, Zhang G X, Zhong S J, et al. Rare Metal Materials and Engineering, 2021, 50(8), 2859 (in Chinese).
王蒙, 张冠星, 钟素娟, 等. 稀有金属材料与工程, 2021, 50(8), 2859.
16 Wang M. Study on the brazing process and brazing seam performance of CuSn and Ni powder to flux-cored silver solder.Master's Thesis, Academy of Machinery Science and Technology, China, 2021 (in Chinese).
王蒙. CuSn、Ni粉对药芯银钎料钎焊工艺及钎缝性能研究. 硕士学位论文, 机械科学研究总院, 2021.
17 Dong B W, Deng X J, He P. Welding & Joining, 2015(7), 34 (in Chinese).
董博文, 邓小君, 何鹏. 焊接, 2015(7), 34.
18 Dong B W, Zhong S J, Pei Y Y, et al. Rare Metal Materials and Engineering, 2021, 50(10), 3527.
19 Peng F. Inner Mongolia Petrochemical Industry, 2011, 37(2), 112 (in Chinese).
彭芳. 内蒙古石油化工, 2011, 37(2), 112.
20 Song Y Y. Research on the process and mechanism of GNPs-enhanced composite brazing filler metals for brazing SiC ceramics and GH99.Master's Thesis, Harbin Institute of Technology, China, 2018 (in Chinese).
宋延宇. GNPs增强复合钎料钎焊SiC陶瓷与GH99的工艺及机理研究. 硕士学位论文, 哈尔滨工业大学, 2018.
21 Yi R X, Chen C, Shi C, et al. Ceramics International, 2021, 47(15), 20807.
22 Li J, Wang F C, Shi C S, et al. Materials Science & Engineering A, 2021, 799, 140127.
23 Li C. Study on self-whisker connection of Al₂O₃ ceramics and its brazing with TC4 titanium alloy. Master's Thesis, Harbin Institute of Technology, China, 2013 (in Chinese).
李淳. Al₂O₃陶瓷的自身晶须连接及其与TC4钛合金的钎焊研究. 硕士学位论文, 哈尔滨工业大学, 2013.
24 Yang M X, Lin T S, He P, et al. Materials Science & Engineering A, 2011, 528(9), 3520.
25 Yang M X, He P, Lin T S. Journal of Materials Science & Technology, 2013, 29(10), 961.
26 Yang M X, Lin T S, He P, et al. Ceramics International, 2011, 37(8), 3029.
27 Yang M X. Microstructure and properties of in-situ TiB whiskers reinforced Al₂O₃/TC4 brazed joints. Ph.D. Thesis, Harbin Institute of Technology, China, 2012 (in Chinese).
杨敏旋. 原位自生TiB晶须增强Al₂O₃/TC4钎焊接头组织结构及性能研究. 博士学位论文, 哈尔滨工业大学, 2012.
28 Yang M X, Lin T S, He P. Journal of Alloys and Compounds, 2012, 512(1), 282.
29 Niu G B, Wang D P, Yang Z W,et al. Journal of Technology & Science, 2017, 43(1), 439.
30 Niu G B.Al₂O₃ Study on vacuum active brazing process and mechanism of ceramics and TiAl alloy. Master's Thesis, Tianjin University, China, 2017 (in Chinese).
牛国宾. Al₂O₃陶瓷与TiAl合金真空活性钎焊工艺与机理研究. 硕士学位论文, 天津大学, 2017.
31 Wang Y, Yang Z W, Zhang L X, et al. Materials & Design, 2015, 86, 328.
32 Bai D, Yan J Z, Li N, et al. Hot Working Technology, DOI: 10.14158/j.cnki.1001-3814.20211604 (in Chinese).
白冬, 颜家振, 李宁, 等. 热加工工艺, DOI: 10.14158/j.cnki.1001-3814.20211604.
33 Lin G B, Huang J H, Zhang J G, et al. The Chinses Journal of Nonferrous Metals, 2005, 15(9), 1327 (in Chinese).
林国标, 黄继华, 张建纲, 等. 中国有色金属学报, 2005, 15(9), 1327.
34 Song Y Y, Liu D, Song X G, et al. Journal of the American Ceramic So-ciety, 2019, 102(11), 6529.
35 Song Y Y, Liu D, Hu S P, et al. Ceramics International, 2019, 45(7), 8962.
36 Chen Z. Research on the process and mechanism of composite brazing of SiC and Nb.Master's Thesis, Harbin Institute of Technology, China, 2015 (in Chinese).
陈哲. 复合钎料钎焊SiC与Nb的工艺和机理研究. 硕士学位论文, 哈尔滨工业大学, 2015.
37 Song Y Y, Liu D, Hu S P, et al. Journal of the European Ceramic Society, 2018, 39(4), 696.
38 Yang Z W, Zhang L X, He P, et al. Materials Science & Engineering A, 2011, 532, 471.
39 Yang Z W, Zhang L X, Tian X Y, et al. Materials Characterization, 2013, 79, 52.
40 Lin G B, Huang J H. Powder Metallurgy, 2006, 49(4), 345.
41 Lin G B, Huang J H, Zhang H, et al. Materials Transactions, 2006, 47(4), 1261.
42 Xiong J H, Huang J H, Wang Z P, et al. Materials Science and Technology, 2010, 26(3), 356.
43 Ban Y H, Huang J H, Zhang H, et al. Rare Metal Materials and Engineering, 2009, 38(4), 713 (in Chinese).
班永华, 黄继华, 张华, 等. 稀有金属材料与工程, 2009, 38(4), 713.
44 Wang Z P, Huang J H, Ban Y H, et al. Journal of Materials Enginee-ring, 2008(9), 36 (in Chinese).
王志平, 黄继华, 班永华, 等. 材料工程, 2008(9), 36.
45 Xue X Y, Xiong J H, Huang J H, et al. Journal of Materials Enginee-ring, 2010(5), 68 (in Chinese).
薛行雁, 熊进辉, 黄继华, 等. 材料工程, 2010(5), 68.
46 Gao L L, Cai C, Xiong J H, et al. Transactions of the China Welding Institution, 2011, 32(7), 35 (in Chinese).
高玲玲, 蔡创, 熊进辉, 等. 焊接学报, 2011, 32(7), 35.
47 Ba J, Zhang X H, Ning R, et al. Journal of Technology & Science, 2018, 44(9), 10210.
48 Ba J. Study on surface structure control assisted brazing of SiO₂-BN Ceramics and TC4 titanium alloy. Master's Thesis, Harbin Institute of Technology, China, 2018 (in Chinese).
霸金. 表面结构调控辅助钎焊SiO₂-BN陶瓷与TC4钛合金工艺研究. 硕士学位论文, 哈尔滨工业大学, 2018.
49 Ba J, Li H, Ren B X, et al. Journal of Technology & Science, 2019, 45(6), 8054.
50 Qi J L, Lin J H, Wan Y H, et al. RSC Advances, 2014, 4(109), 64238.
51 Wan Y H. Study on the mechanism of brazing SiO₂-BN ceramics and Nb with CNTs reinforced TiNi composite solder. Master's Thesis, Harbin Institute of Technology, China, 2014 (in Chinese).
万禹含. CNTs增强TiNi复合钎料钎焊SiO₂-BN陶瓷与Nb的机理研究. 硕士学位论文, 哈尔滨工业大学, 2014.
52 Yang Z W. Design of SiO₂-BN ceramic and Invar alloy brazing interlayer and formation mechanism of interface structure. Master's Thesis, Harbin Institute of Technology, China, 2013 (in Chinese).
杨振文. SiO₂-BN陶瓷与Invar合金钎焊中间层设计及界面结构形成机理. 硕士学位论文, 哈尔滨工业大学, 2013.
53 Mao Y W, Yu S, Zhang Y Z, et al. Fusion Engineering and Design, 2015, 100, 152.
54 Mao Y W, Wang S, Peng L X, et al. Journal of Materials Science, 2016, 51(4),1671.
55 Guo B B. In situ reaction to generate a reinforcing phase for carbon/copper bonding.Master's Thesis, Wuhan Institute of Technology, China, 2015 (in Chinese).
郭贝贝. 原位反应生成增强相用于碳/铜连接的研究. 硕士学位论文, 武汉工程大学, 2015.
56 Wang S. Study on the role of reinforcing phase in C/Cu connection in composite solder.Master's Thesis, Wuhan Institute of Technology, China, 2017 (in Chinese).
汪盛. 复合钎料中增强相在C/Cu连接中的作用研究. 硕士学位论文, 武汉工程大学, 2017.
57 Mao Y W, Peng L X, Wang S, et al. Journal of Alloys and Compounds, 2017, 716, 81.
58 Mao Y W, Yu S, Deng Q R, et al. Journal of Materials Engineering, 2016, 25(12), 5262.
59 Long W M, Li S N, Shen Y X, et al. Rare Metal Materials and Enginee-ring, 2020, 49(8), 2683.
60 Li K Z, Shen X T, Li H J, et al. Carbon, 2010, 49(4), 1208.
61 Wang Y L, Wang W L, Huang J H, et al. Materials Science & Enginee-ring A, 2019, 759, 303.
62 Wang Y L, Wang W L, Huang J H, et al. Journal of Materials Processing Technology, 2021, 288, 116886.
63 Lin T S, Yang M X, He P, et al. Materials & Design, 2011, 32(8-9), 4553.
64 Shi S F, Cho S H, Goto T, et al. Journal of the American Ceramic Society, 2021, 104(6), 2753.
65 Song X R, Li H J, Zeng X R. Journal of Alloys and Compounds, 2016, 664, 175.