| METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
| C/C-SiC:Preparation and Properties of W/Cu Composite Coatings |
| ZHANG Xizhi1, CUI Hong1,*, ZHANG Jiahao2, HU Yang1, DENG Hongbing1
|
1 Research Institute of Xi'an Aerospace Composites Materials, Xi'an 710025, China
2 Xi'an Institute of Aerospace Dynamics Measurement and Control Technology, Xi'an 710025, China |
|
|
|
|
Abstract In order to improve the ablation resistance of C/C-SiC composites and improve the brittleness of W coatings, W/Cu composite powders were prepared by cladding method, and W coating, W/Cu composite coating were prepared on the surface of C/C-SiC composites by atmosphe-ric plasma spraying technology. The effects of different W/Cu ratios (10∶0.5, 10∶1, 10∶1.5) on the microstructure, microhardness, ablation resistance and erosion resistance of the composite coatings were investigated. The results show that the W/Cu composite coating prepared by atmospheric plasma spraying will form a special Cu/W/Cu/W alternating structure. The microhardness decreased, with a maximum decrease of 45%, but the brittleness of the W coating was significantly improved, and the erosion resistance was significantly enhanced. In the process of oxyacetylene flame test with heat flux density of 4 200 kW/m2 for 60 s, the W/Cu composite coating will absorb a lot of heat due to the characteristics of low melting point and high boiling point of Cu, which can effectively reduce the surface temperature of the coating and delay the ablation. When the mass ratio of W/Cu was 10∶1, the diameter of the ablation center surface of the W/Cu composite coating was reduced by 57.4% compared with that of the W coating, and the line ablation rate and mass ablation rate were reduced by 45.5% and 42%, respectively.
|
|
Published: 10 August 2023
Online: 2023-08-07
|
|
|
| Fund:National Defense Science and Technology Innovation Special Zone Project (19H86303ZD102006). |
|
|
1 Brozek V, Vokac M, Kolisko J, et al. Metalurgija, 2017, 56 (1-2), 79.
2 Chong F, Chen J. Journal of Alloys and Compounds, 2021, 861, 158422.
3 Guo S, Ge C, Feng Y, et al. Rare Metal Materials and Engineering, 2011, 40 (12), 2167.
4 Wang F Q, Zhang L, Chen J. Aerospace Materials & Technology, 2020, 50 (6), 8 (in Chinese).
王富强, 张力, 陈建. 宇航材料工艺, 2020, 50 (6), 8.
5 Zhu Y, Meng X L, Cui H, et al. Journal of Propulsion Technology, 2020, 41 (3), 700 (in Chinese).
朱阳, 孟祥利, 崔红, 等. 推进技术, 2020, 41 (3), 700.
6 Zhang H, Fan J, Liu T, et al. Vacuum, 2021, 194, 110563.
7 Zhang Q, Liang S, Zhuo L. Materials Science and Technology, 2017, 33 (17), 2071.
8 Chen P, Shen Q, Luo G, et al. Surface & Coatings Technology, 2016, 288, 8.
9 Niu Y, Lu D, Huang L, et al. Vacuum, 2015, 117, 98.
10 Matejicek J, Chraska P, Linke J. Journal of Thermal Spray Technology, 2007, 16 (1), 64.
11 Zhang Q, Cui H, Zhu Y, et al. Acta Materiae Compositae Sinica, 2018, 35 (3), 640 (in Chinese).
张强, 崔红, 朱阳, 等. 复合材料学报, 2018, 35 (3), 640.
12 Zhu Y, Hu Y, Cui H, et al. Ceramics International, 2021, 47 (5), 6554.
13 Hu D, Zheng X, Niu Y, et al. Journal of Thermal Spray Technology, 2008, 17 (3), 377.
14 Chen Z, Li Y, Cheng L, et al. Nuclear Fusion, 2021, 61 (12), 126024.
15 Kim H, Lee H J, Kim S H, et al. Fusion Engineering and Design, 2016, 109, 590.
16 Wang P, Jacob W, Gao L, et al. Physica Scripta, 2014, T159, 014046.
17 Deng N, Tang J, Xiong T, et al. Surface & Coatings Technology, 2019, 368, 8.
18 Zhou Z, Niu F, Hu X, et al. Advanced Engineering Materials, DOI:10. 1002/adem. 202001457.
19 Guo L J, Peng J, Guo C, et al. Vacuum, 2017, 143, 262.
20 Guo L J, Peng J, Wang H Q, et al. Journal of Alloys and Compounds, 2017, 703, 560. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2023, Vol. 37 