METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
Effect of Brazing Parameters on Microstructure and Properties of Al2O3 Ceramic/304 Stainless Steel Brazed Joints |
XUE Haitao, LI Tao, GUO Weibing*, CHEN Cuixin, ZHAO Jianglong, DING Zhijie
|
School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300401, China |
|
|
Abstract Al2O3 ceramic and 304 stainless steel were brazed by Ag-Cu-Ti filler alloy. The effects of brazing temperature and holding time on the microstructure and mechanical properties of Al2O3 ceramic/304 stainless steel joint were investigated. The results indicate that the microstructure of the joint was Al2O3/Cu3Ti3O+TiCu/Ag(s,s)+Cu(s,s)+TiCu/Cu0.8Fe0.2Ti/Fe-Cr/304. The shear strength of the joint reached 130.54 MPa when brazed at 900 ℃ and holding time of 10 min. Thickness of the Cu3Ti3O was 2.5 μm. When the temperature is low and the holding time is short, the Cu3Ti3O reaction layer is thin, resulting in weak bonding between Al2O3 ceramic and filler layer. With increase of temperature and holding time, the thickness of the Cu3Ti3O reaction layer is too thick, which weakens the plastic deformation ability of the joint. The thickness of Cu3Ti3O reaction layer is the key to affecting quality of the joint.
|
Published: 10 January 2023
Online: 2023-01-31
|
|
Fund:Natural Science Foundation of Hebei Province (E2021202177). |
|
|
1 Friant J R, Meier A, Darsell J T, et al.Journal of the American Ceramic Society, 2012, 95(5),1549. 2 Lu Y, Zhu M, Zhang Q, et al.Journal of the European Ceramic Society, 2020,40(4),1469. 3 Ali M, Knowles K M, Mallinson P M, et al. Acta Materlalia, 2015, 96,143. 4 Chen Y K, Zhou J P, Zhang Y, et al.Materials Letters, 2021, 291, 129357. 5 Yang J, Wang Y, Huang J, et al.Journal of Alloys and Compounds, 2018, 772,438. 6 Xiao H Z, Xiao B, Wu H H. Journal of Alloys and Compounds, 2019, 781,226. 7 Paidar M, Ravikumar M M, Ojo O O, et al. Materials Letters, 2021, 297, 129919. 8 Dong H G, Zhang R Z, Xia Y Q, et al.Transactions of Nonferrous Metals Society of China, 2021, 31(6),1680. 9 Sun H D, Yu G Y, Chen S H, et al.Journal of Manufacturing Processes, 2021, 68,961. 10 Lu Y, Wang J, Zheng K H. Journal of Manufacturing Processes, 2021, 68,1303. 11 Yan Z, Chen Y K, Zhou J P, et al. Journal of Materials Research and Technology, 2020, 9(1),465. 12 Yang Z, Lin J, Wang Y, et al. Vacuum, 2017, 143,294. 13 Xin C L, Li N, Yan J Z, et al. Rare Metal Materials and Engineering, 2018, 47(4),1031. 14 Mohammed Jasim K, Hashim F A, Yousif R H, et al. Ceramics International, 2010, 36(8),2287. 15 Niu G B, Wang D P, Yang Z W, et al.Ceramics International, 2016, 42(6),6924. 16 Ye X F, Wang Y, Zhang H Q, et al.Rare Metal Materials and Engineering, 2018, 47(11), 3564(in Chinese). 叶晓凤,王宇,张恒泉,等. 稀有金属材料与工程, 2018, 47(11),3564. 17 Zhao Y T, Wang Y, Yang Z W, et al. Archives of Civil and Mechanical Engineering, 2019, 19(1),1. 18 Wang W X. Study on interfacial wettability and mechanical properties of Al2O3/Cu composites. Master’s Thesis, Xi'an University of Technology, China, 2019(in Chinese). 王文祥. Al2O3/Cu复合材料的界面润湿性及其力学性能研究. 硕士学位论文, 西安理工大学,2019. 19 Yang M X, Lin T S, He P. Ceramics International, 2012, 38,289. 20 Wu L Z, Jiang C, Nie M M, et al. Hot Working Technology, 2018, 47(9),70(in Chinese). 吴立舟,江畅,聂明明,等. 热加工工艺, 2018, 47(9),70. 21 Yang Z W, Yang J H, Han Y J, et al. Vacuum, 2020, 181,109604. 22 Michael S L, Horton J A, Pak J J. Journal of the American Ceramic Society, 2005, 73(6),1785. 23 Zhou Q,Thomas R B, Nicholas J D.Acta Materialia, 2018, 148,156. |
|
|
|