| Study on Mechanical Properties and Thermal Stability of Thermoset Poly(Lactic Acid) Prepared by Polycondensation Method |
| XIE Pengfei, CHEN Xie, DING Feng, ZHANG Naiwen, LI Jianbo, REN Jie
|
| College of Materials Science and Engineering, Tongji University, Shanghai 201804 |
|
|
|
|
Abstract This work presents the preparation of thermoset poly(lactic acid) (PLA) through polycondensation and cross-linking reactions. Firstly, four-armed star-shaped poly(lactic acid) (4sPLA) with short chains was synthesized by polycondensation using L-lactic acid as monomer and pentaerythritol as initiator, and was hydroxyl-terminated using methacrylic anhydride to obtain the unsaturated-group-terminated star-shaped oligomer precursor (M4sPLA) capable of cross-linking and solidification. Then, the thermoset PLA samples were obtained by a free-radical-initiated cross-linking reaction, and the effects of polycondensation duration on mechanical properties and thermal stability of the thermoset PLA product were studied. The results showed that the reaction initiation efficiency can be obviously enhanced by increasing the polycondensation duration, which lead to low inpurity content, high molecular weight and low polydispersity of 4sPLA. Moreover, the prolonged polycondensation duration is conducive to higher cross-linking density of the thermally cured PLA product. The most satisfactory mechanical properties, thermal stability and microstructure of the thermoset PLA could be achieved when the polycondensation reaction duration was 20 h.
|
|
Published: 03 April 2019
|
|
|
| Fund:This work was financially supported by the Shanghai Automotive Industry Science and Technology Development Foundation (1006), the National High Technology Research and Development Program of China (2013AA032202), the National Natural Science Foundation of China (51203118). |
| About author:: Pengfei Xie received his bachelor degree in June 2017 from Donghua University in polymer materials. Jianbo Li associate professor and doctoral supervisor of Tongji University, received his Ph.D. degree in materials of Tongji University in 2010. |
|
|
1 Jie Ren. Biodegradable poly(lactic acid): synthesis, modification, processing and applications, Springer, Germany,2011.
2 Anders S, Mikael S. Progress in Polymer Science,2002,27(6),1123.
3 Ren J, Li J B, A series of new natural polymer materials—Polylactic acid, Chemical Industry Press, China,2014(in Chinese).
任杰,李建波. 天然高分子基新材料丛书——聚乳酸, 化学工业出版社,2014.
4 Zou H T, Yi C H, Wang L X, et al. Journal of Thermal Analysis and Calorimetry,2009,97(3),929.
5 Carrasco F, Pages P, Gamez-Perez J. Polymer Degradation and Stability,2010,95(12),2508.
6 Ahmad N, Alam M, Al-Otaibi, et al.Progress in Reaction Kinetics,2015,40(1),86.
7 Yin H Y, Wei X F, Bao R Y, et al. CrystEngComm,2015, 17(11), 2310.
8 Albano C, Rodríguez B, Karam A, et al. Polymers Bulletin,2012,68(7),1935.
9 Su Z Z, Guo W H, Liu Y J, et al. Polymers Bulletin,2009,62(5),629.
10 Zhang J, Sato H, Tsuji H, et al. Macromolecules,2005,38(5),1822.
11 Sakamoto Y, Tsuji H S.Macromolecular Chemistry and Physics,2013,214(7),776.
12 Brizzolara D, Cantow H J, Diederichs K.Macromolecules,1996,29(1),191.
13 Sun J R, Shao J, Huang S Y. Materials Letters,2012,89(15),169.
14 Chen X, Zhang N W, Gu S Y, et al. Journal of Reinforced Plastics and Composites,2014,33(10),953. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2019, Vol. 33 