常温制备赤泥-低钙粉煤灰基地聚物的试验和微观研究

doi:10.11896/cldb.201906013

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2680KB)
Export: BibTeX | EndNote (RIS)

Abstract Class F fly ash has the low reaction degree and low strength problems in geopolymer synthesis at ambient temperature. In this study, 20% red mud was added to Class F fly ash to synthesize geopolymer, of which the mechanical properties were investigated. In addition, microstructural change of the geopolymer was explored with SEM, EDS and FT-IR. Furthermore, the effect of n(Si)/n(Al) = 1.8—2.5 and n(Na)/n(Al) = 0.8—1.1, and curing period at 100% relative humidity for 0—7 days on the red mud-fly ash based geopolymer was investigated. It found that the mechanical properties of the ambient temperature cured red mud-fly ash based geopolymer were significantly improved compared to the Class F fly ash based geopolymer. In addition, n(Si)/n(Al)=2.0—2.2 and n(Na)/n(Al)l=1.0 were the optimum chemical composition for the synthesis of red mud-fly ash based geopolymer, and higher curing humidity was beneficial for its early strength. The improving effect of red mud on the ambient condition cured fly ash based geopolymer was found. It also revealed that the more compact microstructure, the more geopolymer gels formed and higher reaction degree of red mud-fly ash based geopolymer than fly ash based geopolymer were the main reasons for the better mechanical properties of the former one.

Key words： red mud-fly ash based geopolymer curing condition chemical composition mechanical properties microstructure

Published: 03 April 2019

CLC number:

TQ170.9

Fund:This work was financially supported by the Liaoning Natural Science Foundation Key Project (20170520406), the China Postdoctoral Science Foundation Funded Project (2017M621125).

About author:: Mo Zhangreceived her Ph.D. degree in civil engineering from Worcester Polytechnic Institute, USA, in 2015. Shiyu Wangreceived her Bachalor degree in safety engineering from Dalian Jiaotong University in 2018.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Mo
	WANG Shiyu

Cite this article:

ZHANG Mo,WANG Shiyu. Experimental Investigation and Microstructural Analysis of Ambient Temperature Cured Red Mud-Class F Fly Ash Based Geopolymer[J]. Materials Reports, 2019, 33(6): 980-985.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.201906013 OR http://www.mater-rep.com/EN/Y2019/V33/I6/980

1 Davidovits J. Journal of Thermal Analysis,1991,37,1633.
2 Zhang G, He J, Gambrell P R. Transportation Research Record,2010,2167(1),1.
3 Kovalchuk G, Fernández-Jiménez A, Palomo A. Fuel,2007,86(3),315.
4 Fernández-Jiménez A, Palomo A. Cement and Concrete Research,2005,35(10),1984.
5 Zhang Y, Sun W, Li Z. Applied Clay Science,2010,47(3-4),271.
6 Komljenovic M, Bascarevic Z, Bradic V. Journal of Hazardous Mate-rials,2010,181(1-3),35.
7 Pacheco-Torgal F, Moura D, Ding Y, et al. Construction and Building Materials,2011,25(9),3732.
8 Chindaprasirt P, Chareerat T, Hatanaka S, et al. Journal of Materials in Civil Engineering,2011,23(3),264.
9 de Vargas S A, Dal Molin C C D, Vilela F C A, et al. Cement and Concrete Composites,2011,33(6),653.
10 Zhang Y, Sun W, Chen Q, et al. Journal of Hazardous Materials,2007,143(1),206.
11 Luo X, Wang C. Journal of the Chinese Ceramic Society,2016,44(3),450(in Chinese).
罗新春,汪长安. 硅酸盐学报,2016,44(3),450.
12 Ma S, Chen P. Concrete,2008(10),80(in Chinese).
马帅, 陈平.混凝土,2008(10),80.
13 Puertas F, MartõÂnez-RamõÂrez S, Alonso S, et al. Cement and Concrete Research,2000,30,1625.
14 Puertas F, Martínez-Ramírez S, Alonso S, et al. Cement and Concrete Research,2003,25(3),287.
15 Sun Q, Ma C, Zhang X. Non-Metallic Mines, 2017(1),26(in Chinese).
孙庆巍, 马驰伟, 张旭冉. 非金属矿,2017(1),26.
16 Zhao J, Wang C, Liu J, et al. Heilongjiang Environmental Journal,2013,37(1),63(in Chinese).
赵家林, 王超会, 刘剑虹, 等.黑龙江环境通报,2013,37(1),63.
17 Liu Z, Zhou Y, Kong F, et al. New Building Materials,2017(12),12(in Chinese).
刘泽, 周瑜, 孔凡龙, 等. 新型建筑材料,2017(12),12.
18 Rao S, Wang K. Materials Review,2011(s1),477(in Chinese).
饶绍建,王克俭.材料导报,2011(s1),477.
19 Hamada T. In: International Conference on Bauxite Tailings. Jamaica,1986.
20 Power G, Gräfe M, Klauber C, Hydrometallurgy,2011,108(1-2),33.
21 Xiao Q. Mechanical properties of red mud-fly ash geopolymer and application to earth walls. Master’s Thesis, Chang’an University, China,2016(in Chinese).
肖强. 赤泥-粉煤灰地质聚合物力学性能及挡土墙应用研究. 硕士学位论文, 长安大学,2016.
22 Duxson P, Provis L J, Lukey C G, et al. Colloids and Surfaces A-Physicochemical and Engineering Aspects,2005,269(1-3),47.
23 Kuenzel C, Vandeperre J L, Donatello S, et al. Journal of the American Ceramic Society,2012,95(10),3270.
24 Davidovits J. In: First International Conference on Alkaline Cements and Concretes.Ukraine,1994,pp. 131.
25 Criado M, Palomo A, Fernandezjimenez A. Fuel,2005,84(16),2048.
26 White E C, Page K, Henson J N, et al. Applied Clay Science,2013,73,17.
27 Steveson M, Sagoe-Crentsil K. Journal of Materials Science,2005,40(8),2023.