13Cr11Ni2W2MoV马氏体热强不锈钢的韧-脆转变及脆化机理

doi:10.11896/cldb.20120015

Abstract
Figure/Table
References
Related Citation (7)

Download:

Full Text ( PDF ) (4546KB)
Export: BibTeX | EndNote (RIS)

Abstract 13Cr11Ni2W2MoV martensitic heat-strength stainless steel can be used to produce the components of spaceflight igniter, whose working temperature is as low as -196 ℃, so it is rather important to investigate the low-temperature impact toughness of the steel. Therefore, Charpy impact properties of 13Cr11Ni2W2MoV steel were measured in the temperature range of -150 ℃ and 100 ℃. The microstructure and fracture morphology were observed by optical microscope(OM),scanning electron microscope(SEM) and transmission electron microscope(TEM). The ductile-brittle transition temperature (DBTT) was obtained according to the impact energy and the rate of brittle fracture. The results show that the DBTT of 13Cr11Ni2W2MoV is -35.5 ℃. The impact energy of 13Cr11Ni2W2MoV steel decreases from 180 J to 30 J when the temperature decreases from 100 ℃ to -150 ℃. The fracture mode of radiation zones is quasi-cleavage, and there are tearing edges and clea-vage facts on the fracture surface. The height of the cleavage steps and the width of the tearing edge are reduced with the decrease of temperature. The fracture mode of fiber zones and shear lip zones is ductile fracture. Dimples are visible on the fracture surfaces. The number and depth of the dimples decrease with the decrease of temperature. The energy for the crack initiation and stable crack propagation are significantly reduced with the decrease of temperature, and the cracks are easy to grow, so the ductile-brittle transition occurs. The ductile-brittle transition might be caused by difficulties of the dislocation generation and slip at low temperatures.

Key words： 13Cr11Ni2W2MoV martensitic heat-resistant stainless steel ductile-brittle transition impact toughness embrittlement mechanism

Published: 25 February 2022 Online: 2022-02-28

CLC number:

TG115.5

Fund:National Defense Basic Scientific Research Program (WDYX19614260201).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SONG Jie
	CHANG Yingke
	WU Ruide
	LI Lin
	ZHANG Chengyu

Cite this article:

SONG Jie,CHANG Yingke,WU Ruide, et al. Ductile-Brittle Transition and Embrittlement Mechanism of 13Cr11Ni2W2MoV Martensitic Heat-resistant Stainless Steel[J]. Materials Reports, 2022, 36(4): 20120015-5.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20120015 OR http://www.mater-rep.com/EN/Y2022/V36/I4/20120015

1 Li J R, Zhang C L, Liu Y Z. Materials Science & Engineering A, 2016, 670, 256.
2 Lu H G, Wang Z Z, Yin F S, et al. Transactions of Materials and Heat Treatment, 2018, 39(4),100(in Chinese).
逯红果, 王壮壮, 殷凤仕, 等. 材料热处理学报,2018,39(4),100.
3 Song Y Y, Ping D H, Yin F X, et al. Materials Science & Engineering A, 2010, 527(3), 618.
4 Kang J, Wang C, Wang G D.Materials Science & Engineering A, 2012, 553(4), 103.
5 Srivatsa K, Srinivas P, Balachandran G, et al. Materials Science & Engineering A, 2016,677, 250.
6 Gustafson A, Agren J.ISIJ International, 2001, 41(4), 359.
7 Li J, Zhang C, Jiang B, et al. Journal of Alloys & Compounds, 2016, 685, 253.
8 Yang G, Liu Z D, Cheng S C, et al. Key Engineering Materials, 2011, 479, 11.
9 Pandey C, Mahapatra M M. Journal of Materials Engineering and Performance, 2016, 25(6), 2202.
10 Zhao Y H, Zhao Z C,Wang J N, et al. Iron and Steel, 2013, 48(4), 75(in Chinese).
赵义翰, 赵成志, 王健楠, 等.钢铁, 2013,48(4), 75.
11 Liu Y, Li A, Cheng X, et al. Materials Science & Engineering A, 2016, 666(1), 32.
12 Morris J W. ISIJ International, 2011, 51(10), 1573.
13 Wang C F, Wang M Q, Shi J, et al. Scripta Materialia,2008,58(6),492.
14 Zhi J H, Wang Y, Li J H, et al. Heat Treatment of Metals, 2018, 43(3), 68(in Chinese).
支金花, 王裕, 李继红, 等.金属热处理, 2018, 43(3), 68.
15 Calliari I, Zanesco M, Dabala K.Materials and Design, 2008,29(1), 246.
16 Jafari M, Kimura Y, Tsuzaki K.Metallurgical & Materials Transactions A,2012, 43 (7), 2462.
17 Hwang B, Kim Y M, Lee S, et al. Metallurgical & Materials Transactions A, 2005, 36(7), 1804.
18 Carrouge D, Bhadeshia H, Woollin P.Science & Technology of Welding & Joining, 2013, 9(5), 380.
19 Dudko V, Fedoseeva A, Kaibyshey R.Materials Science & Engineering A, 2017, 682(13),75.
20 Anoop C R, Adity P, Narayana M, et al. Metallography Microstructure & Analysis, 2018, 7(4), 381.
21 Chatterjee A, Moitra A, Bhaduri A K, et al. Procedia Engineering, 2014, 86, 290.
22 Tomita Y, Okabayashi K.Metallurgical & Materials Transactions A, 1986(10),1203.
23 Stroh A N.Advances in Physics,1957,6(24),419.
24 Haušild P, Nedbal I, Berdin C.Materials Science & Engineering A, 2002, 335(1),172.
25 Zhou G H, Wang D L, Huang Y Z, et al. Journal of Beijing University of Technology, 1997(6), 606(in Chinese).
周国辉, 王东雷, 黄一中, 等. 北京科技大学学报,1997(6),606.
26 Li C J, Li S H, Weng Y Q, et al. Iron and Steel, 1998, 33(10), 53(in Chinese).
李存剑, 李少华, 翁宇庆, 等. 钢铁, 1998, 33(10), 53.