2Si-B-3C-N陶瓷的热压烧结工艺

doi:10.11896/cldb.19040021

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (3391KB)
Export: BibTeX | EndNote (RIS)

Abstract In the current research, nano 2Si-B-3C-N ceramics were prepared by the hot pressing technique. Employing the methods of XRD, SEM and TEM, careful investigation was carried out on the effect of hot pressing parameters on the microstructure and properties of the prepared ceramics. Results show that, the sintering temperature and pressure has important influence on the structure and properties of the 2Si-B-3C-N ceramic, while the holding time and gas pressure has little effect. When the temperature, pressure, holding time and gas pressure are designed as 1 900 ℃and 80 MPa,respectively, the prepared ceramic has larger density and mechanical properties. And the relative density, bending strength, elastic modulus, fracture toughness and Vickers hardness of the prepared ceramic is about 88.7%, 331.1 MPa, 139.4 GPa, 2.8 MPa·m^1/2 and 5.7 GPa, respectively. While the temperature is decreased to 1 800 ℃ or the pressure is reduced to 50 MPa, the density and mechanical properties of the prepared ceramic are significantly decreased. The elevated temperature and pressure will facilitate the deformation, sliding and rearrangement of the ceramic particles, as well as accelerate the atomic diffusion, and hence promote the sintering and property improvement of the ceramic.

Key words： 2Si-B-3C-N ceramic sintering process densification microstructure mechanical property

Published: 31 July 2019

CLC number:

TB32

Fund:This work was financially supported by the National Natural Science Foundation Henan United Fund of China (U1504516).

About author:: Pengfei Zhangreceived his Ph.D. degree in materials science from Harbin Institute of Technology in 2013. He is currently an associate professor in Henan University of Science and Technology and participates in the development of advanced ceramics. His research inte-rests are preparation, characterization and application of silicon based ceramics, non-oxide ceramics and ceramic matrix composites.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Pengfei
	XU Panpan
	YU Renhong
	JIA Dechang
	YANG Zhihua

Cite this article:

ZHANG Pengfei,XU Panpan,YU Renhong, et al. Hot Pressing Sintering Process of 2Si-B-3C-N Ceramic[J]. Materials Reports, 2019, 33(18): 3161-3165.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.19040021 OR http://www.mater-rep.com/EN/Y2019/V33/I18/3161

[1]	Colombo P, Mera G, Riedel R, et al. Journal of the American Ceramic Society, 2010, 93(7), 1805.
[2]	Jia D, Liang B, Yang Z, et al. Progress in Materials Science, 2018, 98, 1.
[3]	Weinmann M, Kamphowe T W, Schuhmacher J, et al. Chemistry of Materials, 2000, 12(8), 2112.
[4]	Schmidt H, Borchardt G, Weber S, et al. Journal of Non-Crystalline So-lids, 2002, 298(2-3), 232.
[5]	Tang Y, Wang J, Li X D, et al. Ceramics International, 2009, 35(7), 2871.
[6]	Tavakoli A H, Gerstel P, Golczewski J A, et al. Journal of Materials Research, 2011, 26(4), 600.
[7]	Kumar R, Cai Y, Gerstel P, et al. Journal of Materials Science, 2006, 41(21), 7088.
[8]	Riedel R, Kienzle A, Dressler W, et al. Nature, 1996, 382(6594), 796.
[9]	Wang Z C, Aldinger F, Riedel R. Journal of the American Ceramic Society, 2001, 84(10), 2179.
[10]	Christ M, Thurn G, Weinmann M, et al. Journal of the American Cera-mic Society, 2000, 83(12), 3025.
[11]	Kumar N V R, Prinz S, Cai Y, et al. Acta Materialia, 2005, 53(17), 4567.
[12]	Riedel R, Ruswisch L M, An L N, et al. Journal of the American Cera-mic Society, 1998, 81(12), 3341.
[13]	Weinmann M, Schuhmacher J, Kummer H, et al. Chemistry of Mate-rials, 2000, 12(3), 623.
[14]	Zhang P, Jia D, Yang Z, et al. Journal of Materials Science, 2012, 47(20), 1.
[15]	Schmidt H. Soft Materials, 2006, 4(2-4), 143.
[16]	Janakiraman N, Zern A, Weinmann M, et al. Journal of the European Ceramic Society, 2005, 25(4), 509.
[17]	Haberecht J, Nesper R, Grutzmacher H. Chemistry of Materials, 2005, 17(9), 2340.
[18]	Muller A, Gerstel P, Weinmann M, et al. Chemistry of Materials, 2002, 14(8), 3398.
[19]	Vlcek J, Potocky T, Cizek J, et al. Journal of Vacuum Science & Technology A, 2005, 23(6), 1513.
[20]	Vijayakumar A, Todi R M, Warren A P, et al. Diamond and Related Materials, 2008, 17(6), 944.
[21]	Shao G, Feng L, Ma C, et al. Journal of the American Ceramic Society, 2017, 100, 842.
[22]	Zhang P, Jia D, Yang Z, et al. Journal of Advanced Ceramics, 2012, 1(3), 157.
[23]	Zhang P, Jia D, Yang Z, et al. Journal of Alloys and Compounds, 2012, 537, 346.
[24]	Yang Z H, Zhou Y, Ha D C, et al. Materials Science and Engineering A, 2008, 489(1-2), 187.
[25]	Yang Z H. Microstructure and high-temperature properties of the Si-B-C-N MA-powders and ceramics. Ph.D. Thesis, Harbin Institute of Techno-logy, China, 2008(in Chinese).杨治华. Si-B-C-N机械合金化粉末及陶瓷的组织结构与高温性能. 博士学位论文,哈尔滨工业大学, 2008.
[26]	Zhang P, Jia D, Yang Z, et al. Ceramics International, 2012, 38(8), 6399.
[27]	Seifert H J, Peng J Q, Golczewski J, et al. Applied Organometallic Che-mistry, 2001, 15(10), 794.