氧化石墨烯作为润滑油添加剂的分散稳定性

doi:10.11896/cldb.18070074

Abstract
Figure/Table
References
Related Citation (2)

Download:

Full Text ( PDF ) (3044KB)
Export: BibTeX | EndNote (RIS)

Abstract he work was based on te laboratory-designed ultrasound-assisted ball milling and microwave-assisted ball milling test equipment, the GO lubricant oil was obtained by dispersing the GO in the base oil PAO6 using different dispersion methods (surface modification and dispersion, dispersant dispersion, surface modification and dispersant dispersion). Examinations of the surface features of the GO were conducted by XRD, SEM, TEM etc. before and after modification. The dispersion stability of the GO in the base oil was measured by ultraviolet-visible spectrophotometer (UV-Vis) and Zeta potential, and the dispersion mechanism was analyzed. The results indicated that, compared with surface modification dispersion and dispersant dispersion, the combination of surface modification and dispersant dispersion improved the stability of the GO by 44.8% and 35.5%, respectively. After surface modification of GO, the oxygen-containing functional groups on the surface were reduced, the wettability was improved, and the surface was grafted with a lipophilic long-chain alkyl group, which penetrated into the base oil to improve the dispersion stability of the GO. The dispersant was adsorbed on the surface of the modified graphene oxide (MGO) to form a stable double-layer effect. The nano-MGO particles could generate electrostatic repulsion and form a steric hindrance layer to prevented the particles from colliding with each other and agglomerates which could help the MGO disperse in the basic lubrication oil stably. The work not only dispersed the GO in the base oil PAO6 successfully, but also concluded that the combination of surface modification and dispersant dispersion had the best effect on improving the dispersion stability of GO in the base oil, and the optimal concentration of the dispersant was 0.6%.

Published: 12 July 2019

CLC number:

TH117.2

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	QIU Lei
	CHEN Ding
	ZHU Lili
	CHEN Yaotong
	WANG Siyuan
	FENG Pengfei

Cite this article:

QIU Lei,CHEN Ding,ZHU Lili, et al. Dispersion Stability of Graphene Oxide as Lubricant Additive[J]. Materials Reports, 2019, 33(16): 2638-2643.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18070074 OR http://www.mater-rep.com/EN/Y2019/V33/I16/2638

[1] Huang B R, Chan H W, Jou S, et al. Applied Surface Science, 2016, 362, 250.
[2] Pu J, Mo Y, Wan S, et al. Chemical Communications, 2013, 50(4), 469.
[3] Yang G, Su J, Gao J, et al. Journal of Supercritical Fluids, 2013, 73(1), 1.
[4] Olle M, Ceballos G, Serrate D, et al. Nano Letters, 2012, 12(9), 4431.
[5] Ramanathan T, Abdala A A, Stankovich S, et al. Nature Nanotechnology, 2008, 3(6), 327.
[6] Park S, Ruoff R S. Nature Nanotechnology, 2009, 4(4), 217.
[7] Liu Xue, Cai Changfeng, Ding Jiawei. Journal of Chongqing University of Technology (Natural Science), 2017, 31(7), 92. (in Chinse).
刘学, 蔡昌凤, 丁佳炜. 重庆理工大学学报(自然科学), 2017, 31(7), 92.
[8] Zhang Y, Tan Y W, Stormer H L, et al. Nature, 2005, 438(7065), 201.
[9] Schedin F, Geim A K, Morozov S V, et al. Nature Materials, 2007, 6(9), 652.
[10] Kim K S, Lee H J, Lee C, et al. ACS Nano, 2011, 5(6), 5107.
[11] Berman D, Erdemir A, Sumant A V. Materials Today, 2014, 17(1), 31.
[12] Ou J, Wang J, Liu S, et al. Langmuir, 2010, 26(20), 15830.
[13] Hou X, Yang C, He J, et al. Industrial & Engineering Chemistry Research, 2015, 54(17), 4773.
[14] Berman D, Erdemir A, Sumant A V. Carbon, 2013, 59(8), 167.
[15] Patil A J, Vickery J L, Scott T B, et al. Advanced Materials, 2009, 21(31), 3159.
[16] Chang H, Wang G, Yang A, et al. Advanced Functional Materials, 2010, 20(17), 2893.
[17] Allen M J, Tung V C, Kaner R B. Chemical Reviews, 2010, 110(1), 132.
[18] Fan X, Wang L. Journal of Colloid & Interface Science, 2015, 452, 98.
[19] Huang H D, Tu J P, Gan L P, et al. Wear, 2006, 261(2), 140.
[20] Lu K. Ceramics International, 2008, 34(6), 1353.
[21] Lin J, Wang L, Chen G. Tribology Letters, 2011, 41(1), 209.
[22] Zhang W, Zhu H W, Di Z C, et al. Nanoscience & Nanotechnology, 2011(1), 5(in Chinse).
张伟, 朱宏伟, 狄泽超, 等.纳米科技, 2011(1), 5.
[23] Lei Z, Cai Z, Zhang Z, et al. Chinese Journal of Materials Research, 2016(1), 57(in Chinse).
赵磊, 蔡振兵, 张祖川, 等. 材料研究学报, 2016(1), 57.
[24] Jia Z, Pang X, Li H, et al. Tribology International, 2015, 90, 240.
[25] Chen C S, Chen X H, Xu L S, et al. Carbon, 2005, 43(8), 1660.
[26] Guo Y, Sun X, Liu Y, et al. Carbon, 2012, 50(7), 2513.
[27] Li P, Xu Z, Liu Z, et al. Nature Communications, 2011, 6, 5716.
[28] Yan Y, Yin Y X, Guo Y G, et al. Advanced Energy Materials, 2014, 4(8), 1079.
[29] Shih C J, Lin S, Sharma R, et al. Langmuir, 2012, 28(1), 235.
[30] Lord R C. Journal of the American Chemical Society, 1990, 87(5), 1155.
[31] Stankovich S, Piner R D, Nguyen S B T, et al. Carbon, 2006, 44(15), 3342.
[32] Naebe M, Wang J, Amini A, et al. Scientific Reports, 2014, 4(3), 4375.
[33] Li D, Müller M B, Gilje S, et al. Nature Nanotechnology, 2008, 3(2), 101.
[34] Liu J F, Chen H H, Xia Z B, et al. Synthetic Materials Aging and Application, 2010, 39(2), 36(in Chinse).
刘景富, 陈海洪, 夏正斌, 等.合成材料老化与应用, 2010, 39(2), 36.
[35] Han G S, Chen D, Li X. Advanced Powder Technology, 2017, 28(4), 1136.
[36] Chen D, Zhang Y Z, Chen B Y et al. Industrial and Engineering Chemistry Research, 2013, 52(39), 14179.