Effects of Process Parameters on Weld Formation and Tensile Properties of Hybrid Laser-Arc Welding |
LUO Ziyi, HAN Shanguo, CHEN Yongcheng, CAI Detao, KHASKIN Vladyslav Yu
|
Guangdong Provincial Key Laboratory of Advanced Welding Technology, Guangdong Welding Institute (China-Ukraine E.O. Paton Institute of Welding),Guangzhou 510650 |
|
|
Abstract Full penetration welding process experiments had been carried out on 8 mm 304 stainless steel by hybrid laser-arc welding using high power disk laser and MIG arc. The effects on the weld formation and tensile property (tensile strength, elongation) of wire feeding speed, laser power, welding speed, distance between laser and arc were studied. The results show that it can decrease back hump and eliminate undercut leading weld formation improvement with increasing wire feeding speed. And it can improve tensile strength and elongation, but if the wire feeding speed is too big, the tensile strength would decrease. It can decrease back hump and eliminate undercut by enhancing laser power but the tensile strength and elongation would decrease. When the distance between laser and arc is 1 mm, it can obtain a good weld formation and the tensile strength and elongation are better. The tensile strength and elongation can be up to 695 MPa and 41.5%, which reach 97.89% and 76.85% of the base material, respectively.
|
Published: 14 June 2019
|
|
Fund:This work was financially supported by the GDAS' Project of Science and Technology Development (2017GDASCX-0113,2018GDASCX-0803), the Science and Technology Planning Project of Guangdong Province of China (2017A010102008,2018A050506058). |
|
|
1 |
Xiao Rongshi, Wu Shikai.Chinese Journal of Lasers, 2008,35(11),1680 (in Chinese).肖荣诗,吴世凯.中国激光,2008,35(11),1680.2 Wang Xiaonan, Chen Changjun, Zhu Guangjiang, et al. Laser & Optoelectronics Progress, 2014,51(3),030008 (in Chinese).王晓南,陈长军,朱广江,等.激光与光电子学进展,2014,51(3),030008.3 Gao Zhiguo, Huang Jian, Li Yaling, et al.Transactions of the China Welding Institution, 2008,29 (12),69 (in Chinese).高志国,黄坚,李亚玲,等.焊接学报,2008,29(12),69.4 Zhao Lin, Tsukamoto Susumu, Arakane Goro, et al.Chinese Journal of Lasers,2015,42(4),0406006 (in Chinese).赵琳,塚本进,荒金吾郎,等.中国激光,2015,42(4),0406006.5 Cui Li, He Dingyong, Li Xiaoyan, et al.Chinese Journal of Lasers, 2011,38(1),0103002 (in Chinese).崔丽,贺定勇,李晓延,等.中国激光,2011,38(1),0103002.6 Chen Yanbin, Feng Jiecai, Li Liqun.Journal of Mechanical Enginee-ring, 2016,52(6),47 (in Chinese).陈彦宾,冯杰才,李俐群.机械工程学报,2016,52(6),47.7 Shi Pengfei,Huang Jian,Tantai Fanliang,et al.Chinese Journal of Lasers, 2017,44(10),1002001 (in Chinese).史鹏飞,黄坚,姚成武,等.中国激光,2017,44(10),1002001.8 Cai Xiaoyu,Li Huan,Yang Lijun,et al. Chinese Journal of Lasers, 2014,41(5),0503001 (in Chinese).蔡笑宇,李桓,杨立军,等. 中国激光,2014, 41(5), 0503001.9 Wahba M,Mizutani M,Katayama S. Materials and Design, 2016, 97,1.10 Steen Erik Nielsen. Physics Procedia,2015,78,24.
|
No related articles found! |
|
|
|
|