Fe-18Cr-9Mn-1.1Ni-1.1Mo-0.2N节Ni型双相不锈钢高温热变形行为

doi:10.11896/cldb.18030175

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (4246KB)
Export: BibTeX | EndNote (RIS)

Abstract Using Gleeble-3800 thermal simulation machine, the hot compression experiment was conducted to investigate the deformation mechanism and microstructure evolution of Fe-18Cr-9Mn-1.1Ni-1.1Mo-0.2N duplex stainless steel (DSS) in the temperature of 1 123—1 423 K, and the strain rate of 0.01—10 s^-1. According to the hyperbolic sine equation, the peak flow stress constitutive equation of the Z parameter was established after determining the value of stress level constant α, meanwhile, the thermal processing drawings under different strain have been drawn. In the dynamic recrystallization (DRX) region of low deformation strain rate 0.01—0.1 s^-1and high deformation temperature 1 323—1 423 K, the smaller value of strain corresponding to the peak stress, the easier occurring of austenite DRX. At the same strain rate, the auste-nite phases change from dynamic recovery to DRX with the increase of deformation temperature. The ferrite DRX mainly occurred in the middle deformation temperature region of 1 123—1 223 K. The deformation apparent activation energy Q was calculated as 578.46 kJ/mol based on thermal deformation equation, which is higher than that of 2205 DSS (451 kJ/mol), and the apparent stress exponent n was calculated as 8.439 8, indicated that the deformation mechanism is structure stability model based on lattice self-diffusion controlled. The analysis of hot processing maps shows that the instable regions gradually increase with the increase of strain on the condition of high strain rates. The optimized thermal processing area was determined to be in the strain rate of 0.01—0.08 s^-1, in the deformation temperature of 1 323—1 423 K, and the corresponding high values of power dissipation coefficients are between 0.30—0.52, thus, the austenite DRX occurred under this deformation conditions for tested steels.

Key words： duplex stainless steel hot deformation dynamic recrystallization constitutive equation hot working drawing

Published: 31 May 2019

CLC number:

TG142

Fund:This work was financially supported by the National Natural Science Foundation of China (51461024).

About author:: Hao Qian,grade 2016, master of engineering, School of Materials Science and Engineering, Kunming University of Technology, focusing on the research of hot deformation direction of duplex stainless steel.Yinhui Yangreceived his Ph.D. degree in materials from School of Material Science and Technology of Tongji University (TJU) in 2011. He is currently an associate professor in Kunming University of Science and Technology (KMUST), focusing on the research fields of material design, strengthening and toughening of stainless steel, corrosion resistance of metal mate-rials.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	QIAN Hao
	YANG Yinhui
	CAO Jianchun
	SU Yusen

Cite this article:

QIAN Hao,YANG Yinhui,CAO Jianchun, et al. High Temperature Deformation Behavior of Fe-18Cr-9Mn-1.1Ni-1.1Mo-0.2NLow-nickel Type Duplex Stainless Steel[J]. Materials Reports, 2019, 33(12): 2040-2046.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18030175 OR http://www.mater-rep.com/EN/Y2019/V33/I12/2040

1 Charles J,Chemelle P, Hu J C,et al. Word Iron ＆ Steel, 2011, 11(6),1(in Chinese).
Charles J,Chemelle P, 胡锦程,et al. 世界钢铁, 2011, 11(6),1.
2 Gao W, Luo J M, Yang J J. Ordnance Material Science and Engineering, 2005(3),61(in Chinese).
高娃, 罗建民, 杨建君. 兵器材料科学与工程, 2005(3),61.
3 Zhang Guoxin, Li Shuangquan. Petrochemical Equipment Technology,2007, 28(4),55(in Chinese).
张国信, 李双权. 石油化工设备技术, 2007, 28(4),55.
4 Du C F, Zhan F, Yang Y H, et al. Metallic Functional Materials, 2010(5),63(in Chinese).
杜春风, 詹凤, 杨银辉, 等. 金属功能材料, 2010(5),63.
5 Yamamoto Y, Santella M L, Liu C T, et al. Materials Science & Engineering: A, 2009, 524(1-2),176.
6 Huang Y L, Wang J B, Ling X S, et al. Materials Review, 2008, 22(s3),173(in Chinese).
黄有林, 王建波, 凌学士, 等. 材料导报, 2008, 22(s3),173.
7 Li L F, Yang W Y, Sun Z Q. Acta Metallurgica Sinica, 2004(12),1257(in Chinese).
李龙飞, 杨王玥, 孙祖庆.金属学报,2004(12),1257.
8 Zeng J S, Xiong J, Shi W, et al. Materials Science and Technology. 2013,21(2),72(in Chinese).
曾敬山, 熊杰, 史文, 等. 材料科学与工艺, 2013, 21(2), 72.
9 Wu R H, Zhu H T, Zhang H B, et al. Journal of Shanghai Jiaotong University, 2001(3), 339(in Chinese).
吴瑞恒, 朱洪涛, 张鸿冰, 等. 上海交通大学学报, 2001(3), 339.
10Su Yusen,Yang Yinhui, Cao Jianchun, et al. Acta Metallurgica Sinica, 2018, 54(4), 485(in Chinese).
苏煜森, 杨银辉, 曹建春, 等. 金属学报, 2018, 54(4), 485.
11Du S W, Chen S M. Transactions of Materials and Heat Treatment, 2016(3), 223(in Chinese).
杜诗文,陈双梅. 材料热处理学报,2016(3),223.
12Zahiri S H, Davies C H J, Hodgson P D. Scripta Materialia, 2005, 52(4),299.
13Zou D N, Wu K, Han Y, et al. Materials & Design, 2013, 51,975.
14Chen Lei, Wang Longmei, Du Xiaojian, et al. Acta Metallurgica Sinica,2010,46(1),52(in Chinese).
陈雷,王龙妹,杜晓建,等. 金属学报,2010,46(1),52.
15Gironès A, Llanes L, Anglada M, et al. Materials Science & Engineering A, 2004, 367(1-2),322.
16Prasad Y V R K, Gegel H L, Doraivelu S M, et al. Metallurgical Tran-sactions A, 1984, 15, 1883.
17Huang F X, Yin P, Li S S, et al. Journal of Chongqing Institute of Technology(Natural Science), 2010,24(1),92(in Chinese).
黄福祥,尹平,李司山,等.重庆理工大学学报(自然科学),2010,24(1),92.
18Li Dongfeng, Zhang Duanzheng, Liu Shengdan, et al. Transactionsof Nonferrous Metals Society of China, 2016, 26(6),1491.
19Cabrera J M, Mateo A, Llanes L, et al. Journal of Materials Processing Technology, 2003, 143-144, 321.
20Guo J F, Zhou X D, Li H. Transactions of Materials and Heat Treatment,2014, 35(12),128(in Chinese).
郭俊锋, 周旭东, 李汉. 材料热处理学报, 2014, 35(12),128.
21He A, Yang X Y, Xie G L, et al. Journal of Iron and Steel Research, 2015(8),34(in Chinese).
何岸, 杨晓雅, 谢甘霖,等. 钢铁研究学报, 2015(8),34.
22Chen H Q, Bai J X, Qi H P, et al. Journal of Mechanical Engineering, 2014, 50(16),89(in Chinese).
陈慧琴, 柏金鑫, 齐会萍,等. 机械工程学报, 2014, 50(16),89.