Effect of Chemical Composition and Structure of Blast Furnace Slag on Its Early hydration Characteristics in Alkaline Environment
WANG Yali1,2, YAO Yuhan1,2, CUI Suping1,2, WANG Hui1,2, WANG Wei1
1 College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124; 2 National Engineering Laboratory for Industrial Big-data Application Technology, Beijing 100124
摘要 以不同组成和结构的高炉矿渣作为研究对象,借助XRD、ICP-MS以及29Si MAS NMR等微观测试手段,探究了高炉矿渣在碱性环境中的离子溶出特性、硅氧四面体聚合状态随水化龄期变化的影响规律。研究表明:高炉矿渣中玻璃体的活性受其化学组成和结晶相含量影响,结晶相及铝氧结构单元的存在和增多降低了玻璃体结构的聚合度;网络改性剂在玻璃体结构中表现为不均匀分布,不同网络形成体结构单元的水解会伴随不同的水化特性;在碱性环境下,高炉矿渣玻璃体结构中硅氧四面体含量较大时,其硅氧结构更易被破坏,溶液中硅离子的浓度较高,溶液pH值维持在较低水平,生成的水化产物中高聚态硅氧四面体较多;高炉矿渣玻璃体结构中铝氧四面体含量较大时,其铝氧结构更易被破坏,溶液中铝离子及钙离子的浓度较高,液相pH值维持在较高水平,生成的水化产物中高聚态硅氧四面体较少。
Abstract: The composition and structure of blast furnace slag have influence on its early hydration characteristics. In this paper, various blast furnace slag with different chemical composition and structure were studied by means of X-ray diffraction, ICP-MS spectroscopy and 29Si MAS NMR to research the relationship among glass phase polymerization state with the ion dissolution characteristic in alkaline environment, and the change of silicate tetrahedron polymerization state with hydration age. The results showed that the structure of glass phase was affected by chemical composition and content of crystalline phase in which the existence and increase of crystalline phase and Al-O structure unit could reduce the degree of polymerization. In the glass phase network structure, the network modifier was inhomogeneously distributed among the networks, and the hydrolysis of the different structural units would be accompanied by different hydration characteristics. In alkaline environment, the more Si-O structure units in glass phase, the structure of Si-O was more easily hydrated, resulting in higher concentration of silicon ions in the solution, and more exist of polymeric silicate tetrahedrons in the gel products, and the pH value of environment was obviously decreased. With the more exist of more Al-O structure units, the structure of Al-O was more easily hydrated, resulting in higher concentration of aluminum ion and calcium ion in the environment, which corresponding to only a small amount of highly polymeric Si-O tetrahedron could be distinguished in the gels, and the hydration process could keep at a high pH value.
王亚丽, 姚羽涵, 崔素萍, 王卉, 王为. 高炉矿渣的组成和结构对其在碱性环境中早期水化特性的影响[J]. 材料导报, 2018, 32(22): 3989-3994.
WANG Yali, YAO Yuhan, CUI Suping, WANG Hui, WANG Wei. Effect of Chemical Composition and Structure of Blast Furnace Slag on Its Early hydration Characteristics in Alkaline Environment. Materials Reports, 2018, 32(22): 3989-3994.
1 张临峰,黄导.钢铁工业大宗固体废物综合利用综述[J].冶金管理,2017(4):27. 2 Zhou Shengbo.Research overview of slag microstructure[J].Shandong Metallurgy,2008,30(6):12(in Chinese). 周胜波.矿渣微观结构的研究进展[J].山东冶金,2008,30(6):12. 3 Zachariasen W H. The atomic arrangement in glass[J]. Journal of the American Chemical Society,1932,44(10):3841. 4 Poulsen S L, Kocaba V, Le S G, et al. Improved quantification of alite and belite in anhydrous Portland cements by 29Si MAS NMR: Effects of paramagnetic ions[J]. Solid State Nuclear Magnetic Resonance,2009,36(1):32. 5 He Y J, Hu Z G. Application of 29 Si nuclear magnetic resonance (NMR) in research of cement chemistry[J]. Journal of Materials Science and Engineering,2007,25(1):147(in Chinese). 何永佳,胡曙光.29Si固体核磁共振技术在水泥化学研究中的应用[J].材料科学与工程学报,2007,25(1):147. 6 钟白茜. 用29Si-NMR和TMS-GC研究由水热合成CSH脱水形成β-C2S[J]. 硅酸盐学报,1994(6):566. 7 Joo Hyun Park. Structure-property relationship of CaO-MgO-SiO2, slag: Quantitative; analysis of Raman spectra[J]. Metallurgical & Materials Transactions B,2013,44(4):938. 8 Chen J J, Thomas J J, Taylor H F W, et al. Solubility and structure of calcium silicate hydrate[J]. Cement & Concrete Research,2004,34(9):1499. 9 Haha M B, Lothenbach B, Saout G L, et al. Influence of slag che-mistry on the hydration of alkali-activated blast-furnace slag—Part Ⅱ: Effect of Al2O3[J]. Cement & Concrete Research,2011,42(1):74. 10 Puertas F, Palacios M, Manzano H, et al. C-A-S-H gels formed in alkali-activated slag cement pastes. Structure and effect on cement properties and durability[C]∥Conference Record of the Internatio-nal Congress on Materials & Structural Stability. Rabat, Morocco,2014:01002.
渝公网安备50019002502923号 版权所有：《材料导报》编辑部
2018, Vol. 32 