| METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
| Effect of Low Temperature Pre-ageing on Microstructure and Corrosion Resistance of Al-4.5Zn-1.4Mg Alloy |
| WANG Shuai1,4, LUO Binghui2,*, XING Shasha3, YUAN Guanghui4, XIE Ning4, JIANG Gen5
|
1 School of Chemistry and Environment, Ankang University, Ankang 725000, Shaanxi, China
2 School of Material Science and Engineering, Central South University, Changsha 410083, China
3 Medical College of Ankang University, Ankang 725000, Shaanxi, China
4 Innovation Research Institute of Advanced Energy Storage Materials and Battery Technology for Future Industrialization, Ankang University, Ankang 725000, Shaanxi, China
5 Zoomlion Heavy Industry Science and Technology Development Co., Ltd., Changsha 410083, China |
|
|
|
|
Abstract In this work, a new three-stage ageing treatment known as P-T74 for aluminum alloy was designed, that is, a low temperature pre-ageing treatment at 65 ℃/96 h was added before the T74 treatment. The corrosion properties and microstructure evolution of Al-4.5Zn-1.4Mg alloy during P-T74 and T74 ageing treatment were studied by using of optical microscope, transmission electron microscope and three-dimensional atom probe. The results show that in comparison with T74, P-T74 can effectively increase the density of Guinier Preston zones (GP zones) in the early stage, giving rise to more nucleation sites for the subsequent η′ phase and η phase. In comparison with T74 treatment, with P-T74 ageing treatment, the η phase in the grain boundaries exhibits a higher area fraction, a higher degree of intermittent distribution, a higher Cu content and a narrower precipitation free zone (PFZ). As a results, the rate of galvanic corrosion reaction decreases, the corrosive ions indepen-dently or stress synchronously are difficult to expand into the grain boundaries and the corrosion resistance of the alloy increases.
|
|
Published: 10 December 2025
Online: 2025-12-03
|
|
|
|
|
1 Qin C, Gou G Q, Che X L, et al. Materials and Design, 2016, 91, 278.
2 Zhang C Z, Wang N, Lu K L, et al. Materials Today Communications, 2023, 35, 105744.
3 Wang Y C, Cao L F, Wu X D, et al. Materials Reports, 2019, 33(7), 1190 (in Chinese).
王一唱, 曹玲飞, 吴晓东, 等. 材料导报, 2019, 33(7), 1190.
4 Sun X H. Effect of alloy elements on microstructure evolution and corrosion resistance of 7xxx aluminum alloys. Master’s Thesis, Dalian University of Technology, China, 2023 (in Chinese).
武晓辉. 合金元素对7xxx系铝合金组织与腐蚀性能研究. 硕士学位论文, 大连理工大学, 2023.
5 Wang S, Luo B H, Bai Z H, et al. Vacuum, 2020, 176, 109311.
6 Li Bo, Wang X M, Chen H, et al. Journal of Alloys and Compounds, 2016, 678, 160.
7 Cao F H. Stabilizing design of nano-precipitates in 7XXX Al alloys based on interfacial control. Ph. D. Thesis, Central South University, China, 2019 (in Chinese).
曹富华. 基于界面调控的7XXX铝合金η′纳米析出相稳定化设计. 博士学位论文, 中南大学, 2019.
8 Liu Y, Li W, Jiang D, et al. Journal of Materials Research, 2015, 30(24), 3803.
9 Liu Y R, Pan Q L, Li H, et al. Journal of Alloys and Compounds, 2019, 792, 32.
10 Berg L K, Gjonnes J, Hansen V, et al. Acta Materialia, 2001, 49(17), 3443.
11 Mukhopadhyay A K. Philosophical Magazine Letters, 1994, 70(3), 135.
12 Sha G, Cerezo A. Acta Materialia, 2004, 52(15), 4503.
13 Wang S, Luo B H, Bai Z H, et al. Journal of Alloys and Compounds, 2024, 980, 173681.
14 Robinson M J. Corrosion Science, 1982, 22(8), 775.
15 Robinson M J, Jackson N C. Corrosion Science, 1999, 41(5), 1013.
16 Song R G, Dietzel W, Zhang B J, et al. Acta Materialia, 2004, 52(16), 4727. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2025, Vol. 39 