Abstract To provide reference for the selection of disinfectant types, dosage, and hazard avoidance in practical applications, we compared and analyzed the corrosiveness of vaporized hydrogen peroxide and chlorine dioxide gas which are commonly used fumigation disinfectants in the field of biosafety. Under the same temperature and humidity conditions, the metal and non-metal materials in the field of biosafety were selected as disinfection objects. They were placed in a 1 m³ sealed chamber with the relative humidity of 50% and the temperature of 20 ℃, and exposed to 6.5 g/m³ of vaporized hydrogen peroxide and 3.3 g/m³ of chlorine dioxide gas for 1.5 h. This experiment was repeated 20 times. The corrosion and changes in properties of the materials were analyzed through weighing, apparent observation, and transmittance testing. Vaporized hydrogen peroxide has mild corrosion on most stainless steel, copper, aluminum alloys, and chromium coatings. Chlorine dioxide gas shows mo-derate corrosion on copper and aluminum, and mild corrosion on stainless steel and chromium coatings. These two fumigation disinfectants have no obvious corrosion to non-metallic materials, and slight corrosion to materials such as PP, PMMA, and color coated steel plates. Chlorine dio-xide gas can change the appearance of TPU and ABS. Vaporized hydrogen peroxide and chlorine dioxide gas fumigation disinfections have good compatibility with metal materials, and neither cause severe corrosion or significant changes in material properties. Chlorine dioxide gas can cause color changes in certain non-metallic materials. Comparatively speaking, the impact of vaporized hydrogen peroxide on materials is smaller than that of chlorine dioxide gas. In the practical application of the two fumigation disinfectants, their material compatibility should be fully considered to simultaneously ensure disinfection effectiveness and minimize the impact on material properties.

Key words： vaporized hydrogen peroxide chlorine dioxide gas fumigation disinfection material compatibility

Published: 25 July 2025 Online: 2025-07-29

CLC number:

O647

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SHANG Yiran
	LIU Qiang
	LI Haiyun
	ZHAO Jie
	DENG Cheng
	WANG Xinmiao
	WU Jinhui
	YI Ying

Cite this article:

SHANG Yiran,LIU Qiang,LI Haiyun, et al. Study on the Material Compatibility of Vaporized Hydrogen Peroxide and Chlorine Dioxide Gas for Fumigation Disinfection[J]. Materials Reports, 2025, 39(14): 24030141-6.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.24030141 OR https://www.mater-rep.com/EN/Y2025/V39/I14/24030141

1 Hao L M, Yi Y, Li S, et al. Chinese Medical Equipment Journal, 2018, 39(2), 92 (in Chinese).
郝丽梅, 衣颖, 林松, 等. 医疗卫生装备, 2018, 39(2), 92.
2 Zhang Q H, Ji S X, Hu J H, et al. Journal of Henan Institute of Science and Technology (Natural Science Edition), 2014, 42(4), 62 (in Chinese).
张庆华, 姬素霞, 胡金花, 等. 河南科技学院学报(自然科学版), 2014, 42(4), 62.
3 Cao W L, Xu Z, World Notes on Antibiotics, 2020, 41(5), 398 (in Chinese).
曹伟龙, 徐志. 国外医药(抗生素分册), 2020, 41(5), 398.
4 Lyu Y J, Cheng J S, Fu Y Q, et al. Chinese Journal of Disinfection, 2018, 35(4), 245 (in Chinese).
吕玉姣, 程锦生, 傅元清, 等. 中国消毒学杂志, 2018, 35(4), 245.
5 Lyu X D, Miao X L, Ye G X, et al. Chemical Engineer, 2023, 37(11), 63 (in Chinese).
吕晓冬, 苗笑亮, 叶更新, 等. 化学工程师, 2023, 37(11), 63.
6 Liu Y H. Study on the preparation of chlorine dioxide and the corrosion characteristics of steel materials during the disinfection process. Master's Thesis, Northeastern University, China, 2021 (in Chinese).
刘宇鹤. 二氧化氯的制备及消毒过程中对钢材料的腐蚀特性研究. 硕士学位论文, 东北大学, 2021.
7 Shunji I, Taishi H, Tomoe S, et al. Heliyon, 2023, 9(2), e13360.
8 Hu J, Li Y M, Cai H L, et al. Chinese Journal of Disinfection, 2020, 37(4), 241 (in Chinese).
胡佳, 李裕明, 蔡慧玲, 等. 中国消毒学杂志, 2020, 37(4), 241.
9 U. S. Environmental Protection Agency. New Caledonia, EPA/600/R-10/037, 2010.
10 吴金辉, 邓橙, 郝丽梅, 等. 中国专利, CN113735064B, 2023.
11 中华人民共和国国家卫生健康委员会. GB/T 38498-2020消毒剂金属腐蚀性评价方法. 中国标准出版社, 2020.
12 全国橡胶与橡胶制品标准化技术委员会软管分技术委员会. GB/T 24134-2009橡胶和塑料软管静态条件下耐臭氧性能的评价. 中国标准出版社, 2009.
13 Yang D H, Wang K, Yang B Y, et al. Chemical Engineering Management, 2022(16), 80 (in Chinese).
杨德红, 王坤, 杨本勇, 等. 化工管理, 2022(16), 80.
14 Jia L H. Modern Chemical Research, 2024(3), 80 (in Chinese).
贾凌寒. 当代化工研究, 2024(3), 80.
15 Liu Y H, Wu M S, Wang X S, et al. Inorganic Chemicals Industry, 2021, 53(3), 18 (in Chinese).
刘宇鹤, 吴明松, 王欣舒, 等. 无机盐工业, 2021, 53(3), 18.
16 Mcevoy B, Eveland R. Biomedical Instrumentation and Technology, 2020, 54(S3), 74.
17 Trinh V M, Yuan M H, Chen Y H, et al. Journal of Cleaner Production, 2021, 320, 128885.