镍基高温合金与耐火材料界面特性研究

doi:10.11896/cldb.22100206

Abstract
Figure/Table
References
Related Citation (11)

Download:

Full Text ( PDF ) (50740KB)
Export: BibTeX | EndNote (RIS)

Abstract The interface characteristics of refractory materials and molten alloys have long been studied for the selection of appropriate refractory materials for alloy smelting. Herein, the high-temperature wettability and permeability characteristics of nickel-based superalloys with white fused corundum, sintered magnesia-alumina spinel, and magnesia stabilized zirconia at 1 600 ℃ for 1 h under an Ar atmosphere were studied. The results indicate that the white fused corundum did not exhibit wetting with the nickel-based superalloy, with a contact angle of 92.1°. Furthermore, the surface morphology of the substrate remained unchanged, and the penetration depth was about 1.4 mm. However, wetting of white fused corundum occurred with sintered magnesium aluminium spinel, with a contact angle of 82.6° and substrate penetration depth of about 0.38 mm. In addition, the surface was eroded, depressed, and cracked. For the wetting of white fused corundum with magnesia stabilized zirconia, the contact angle was 52.9°, and the substrate surface remained intact with almost no permeability, but a large amount of contaminated alloy was formed. Based on a comprehensive analysis of performance and cost, white fused corundum and sintered magnesium aluminium spinel were identified as the primary raw materials, with magnesium stabilized zirconium oxide addtion to improve erosion resistance and permeability. The combination is expected to yield optimal refractory crucibles with superior performance and durability for high-temperature alloy smelting.

Key words： nickel-based superalloys refractories high temperature wettability interfacial penetration

Published: 10 February 2025 Online: 2025-02-05

CLC number:

TQ175

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	PAN Yuanshuai
	WANG Gang
	FENG Haixia
	LIU Jun
	YUAN Bo
	TIAN Pengdan
	HAN Yihui

Cite this article:

PAN Yuanshuai,WANG Gang,FENG Haixia, et al. Research on the Interface Properties of Nickel-based Superalloy and Refractories[J]. Materials Reports, 2025, 39(3): 22100206-7.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22100206 OR http://www.mater-rep.com/EN/Y2025/V39/I3/22100206

1 Shi C X, Zhong Z Y. Acta Metallurgica Sinica, 2010, 46(11), 1281 (in Chinese).
师昌绪, 仲增墉. 金属学报, 2010, 46(11), 1281.
2 Wang H Y, An Y Q, Li C Y, et al. Materials Reports, 2011, 25(S2), 482 (in Chinese).
王会阳, 安云岐, 李承宇, 等. 材料导报, 2011, 25(S2), 482.
3 Yang S, Yun J, Moon B, et al. Journal of Mechanical Science and Technology, 2022, 36(1), 127.
4 Liao Z R, Xu D D, Luna Gonzalogarcia, et al. Journal of Materials Processing Technology, 2021, 298(7), 117313.
5 Zhao Y, Wang L, Chen C Y, et al. Ceramics International, 2023, 49(1), 117.
6 Kanyo E J, Schafföner S, Uwanyuze S R, et al. Journal of the European Ceramic Society, 2020, 40(15), 4955.
7 Fan J X. Preparation and properties of Al₂O₃ crucible for smelting superalloy. Master's Thesis, Chang'an University, China, 2023 (in Chinese).
樊嘉显. 高温合金熔炼用氧化铝坩埚制备与性能研究. 硕士学位论文, 长安大学, 2023.
8 Wang G, Wang L W, Yuan B, et al. Refractories, 2023, 57(5), 442 (in Chinese).
王刚, 王来稳, 袁波, 等. 耐火材料, 2023, 57(5), 442.
9 Zhang Y, Li P H, Jia C L, et al. Materials Reports, 2018, 32(9), 1496 (in Chinese).
张勇, 李佩桓, 贾崇林, 等. 材料导报, 2018, 32(9), 1496.
10 Pei Z Y. Study on K465 nickel-base superalloy. Master's Thesis, Northeastern University, China, 2008 (in Chinese).
裴忠治. K465镍基高温合金的研究. 硕士学位论文, 东北大学, 2008.
11 Gao X Y, Zhang L, Qu X H, et al. International Journal of Minerals, Metallurgy and Materials, 2020, 27(11), 1551.
12 Jiang L. Zirconia refractory for melting nickel based superalloy. Master's Thesis, Shanghai University, China, 2017 (in Chinese).
姜兰. 用于镍基高温合金熔炼氧化锆耐火材料的研究. 硕士学位论文, 上海大学, 2017.
13 Wang H W, Yang J X, Meng J, et al. Ceramics International, 2020, 46(14), 22057.
14 Li S J, Liu S, Duan H P, et al. Journal of the Chinese Ceramic Society, 1999, 27(6), 757 (in Chinese).
李树杰, 刘深, 段辉平, 等. 硅酸盐学报, 1999, 27(6), 757.
15 Chen X Y, Jin Z, Bai X F, et al. Acta Metallurgica Sinica, 2015, 51(7), 853 (in Chinese).
陈晓燕, 金喆, 白雪峰, 等. 金属学报, 2015, 51(7), 853.
16 Song Q Z, Qian K, Shu L, et al. Acta Metallurgica Sinica, 2022, 58(7), 868 (in Chinese).
宋庆忠, 潜坤, 舒磊, 等. 金属学报, 2022, 58(7), 868.
17 Zhang Z, Zhu K L, Liu L J, et al. Journal of the Chinese Ceramic Society, 2013(9), 1278 (in Chinese).
张钊, 朱凯亮, 刘岚洁, 等. 硅酸盐学报, 2013(9), 1278.
18 Yin R R. Investigation on interfacial reaction between multicomponent slag and MgO-C refractories. Master's Thesis, University of Science and Technology Liaoning, China, 2020 (in Chinese).
尹冉冉. 多元熔渣与MgO-C耐火材料界面反应研究. 硕士学位论文, 辽宁科技大学, 2020.
19 Mukai K, Tao Z, Goto K, et al. Scandinavian Journal of Metallurgy, 2002, 31(1), 68.
20 Jiang X M, Chen Z Y. Iron and Steel, 1993, 28(7), 21 (in Chinese).
蒋明学, 陈肇友. 钢铁, 1993, 28(7), 21.