相变微胶囊保温砂浆的制备及性能

doi:10.11896/cldb.22110170

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (8954KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to reduce the energy consumption of buildings, the National Phase Change Policy of ‘Carbon Neutralization' and ‘Carbon Peak' is responded. Based on in-situ polymerization method, a phase change microcapsule (MiPCM) suitable for thermal insulation and energy saving cement mortar was prepared by using n-octadecane-n-octadecane mixture as binary phase change core material and methyl methacrylate (PMMA) as outer wall material. MiPCM reduces the influence of external environment on the internal temperature of cement mortar through the heat absorption or heat release characteristics of internal core materials in the phase change process, thereby reducing people's dependence on air conditioners and other electrical appliances, and achieving the purpose of energy conservation and emission reduction. The experimental results showed that the phase transition temperature range and latent heat of MiPCM were 17.8—36.7 ℃ and 74.72 J/g, respectively. MiPCM was graupel-like, without agglomeration and had obvious core-wall structure. TG analysis and thermal cycling test showed that MiPCM had good thermal stability. The temperature rise experiment was carried out by adding MiPCM into cement mortar. The results show that in the infrared heat source irradiation environment, MiPCM significantly slows down the change rate of center temperature of cement mortar, and the peak temperature of cement mortar decreases by 7 ℃. Therefore, the cement mortar with MiPCM as additive conforms to the design concept of heat preservation and energy saving.

Key words： phase change material microencapsulation technology cement mortar heat preservation and energy saving

Published: 10 May 2024 Online: 2024-05-13

CLC number:

TB332

Fund:State Key Laboratory of Bridge Structure Health and Safety Development Research Fund Project(BHSKL21-02-GF), and National Key Research and Development Program of China (2022YFC3004804).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LONG Yong
	WANG Yu
	LIU Tianle
	WANG Yazhou

Cite this article:

LONG Yong,WANG Yu,LIU Tianle, et al. Preparation and Properties of Thermal Insulation Mortar Incorporated with Phase Change Microcapsules[J]. Materials Reports, 2024, 38(9): 22110170-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22110170 OR http://www.mater-rep.com/EN/Y2024/V38/I9/22110170

1 Wang Y M, Tang B T, Zhang S F, et al. Advanced Functional Materials, 2013, 23, 4354.
2 Qian X Q, Zhu Y T. China Civil Engineering Journal, 2010,43(S2),392 (in Chinese).
钱晓倩, 朱耀台. 土木工程学报, 2010, 43(S2), 392.
3 Sun W C. Research on building energy saving effect of active-passive coupling system based on composite phase change materials containing hydrated inorganic salts. Ph.D. Thesis, South China University of Technology, China, 2020 (in Chinese).
孙婉纯. 基于水合无机盐复合相变材料的主动与被动耦合型建筑节能研究. 博士学位论文, 华南理工大学, 2020.
4 Liu J B. Research on energy consumption and thermal comfort of energy-saving wall buildings. Master's Thesis, Changsha University of Science and Technology, China, 2012 (in Chinese).
刘剑波. 节能墙体建筑能耗及热舒适性研究. 硕士学位论文, 长沙理工大学, 2012.
5 Liu M T, Ye X J, Hou Z J, et al. Contamination Control & Air-Conditioning. 2018(3), 58 (in Chinese).
刘明炀, 叶晓江, 侯志坚, 等. 洁净与空调技术, 2018(3), 58.
6 Wang T Y, Wang S F, Luo R L, et al. Applied Energy, 2016,171,113.
7 Hu Z Y, Lai Z X, Liu X, et al. Journal of Chongqing University of Technology (Natural Science), 2023, 37(5), 60 (in Chinese).
胡远志, 赖贞行, 刘西, 等. 重庆理工大学学报(自然科学), 2023, 37(5), 60.
8 Wang X G, Lei W Y, Zhu J L, et al. Materials Reports, 2023, 37(20), 198 (in Chinese).
王信刚, 雷为愉, 朱街禄, 等. 材料导报, 2023, 37(20), 198.
9 Song J J, Xu M B, Wang X L, et al. Drilling Fluid & Completion Fluid, 2019, 36(2), 218 (in Chinese).
宋建建, 许明标, 王晓亮, 等. 钻井液与完井液, 2019, 36(2): 218.
10 Zhang Y H, Liu Z Y, Tang B L, et al. Acta Materiae Compositae Sinica, 2018, 35(4), 980 (in Chinese).
张运华, 刘芷怡, 唐蓓莉, 等. 复合材料学报, 2018, 35(4), 980.
11 Yang G K, Jiang G S, Liu T L, et al. Materials Reports, 2021, 35(2), 2032 (in Chinese).
杨国坤, 蒋国盛, 刘天乐, 等. 材料导报, 2021, 35(2), 2032.
12 Chen C, Guo H F, Liu Y N, et al. Energy and Buildings. 2008;40: 882.
13 Liu X J, Feng Q, Peng Z G, et al. Energy, 2020, 208(8), 118175.
14 Liu J C, Chen Q, Liu Y P, et al. China Plastics, 2022, 36(1), 178 (in Chinese).
刘金成, 陈谦, 刘玉佩, 等. 中国塑料, 2022, 36(1), 178.
15 Huo J H, Peng Z G, Xu K, et al. Energy, 2019, 12, 186.
16 Yang G K, Liu T L, Aleksandravih B P, et al. Energy, 2022, 02, 253.
17 Huang Y, Liu H X, Wang C L, et al. Chinese Journal of Synthetic Che-mistry, 2022, 30(5), 365 (in Chinese).
黄熠, 刘和兴, 王成龙,等. 合成化学, 2022, 30(5), 365.
18 Zheng W B, Sun D, Li Y Y, et al. Journal of Chongqing University of Technology (Natural Science), 2023, 37(9), 356 (in Chinese).
郑炜博, 孙东, 李云飞, 等. 重庆理工大学学报(自然科学), 2023, 37(9), 356.
19 Zhang D Y, Bai K H, Li C C, et al. Materials Reports, 2022, 36(8), 170(in Chinese).
张东尧, 白开皓, 李传常, 等. 材料导报, 2022, 36(8), 170.
20 Wu D G, Guo N, Yin H Y, et al. Polymer Materials Science & Enginee-ring, 2020, 36(10), 1 (in Chinese).
吴殿国,郭娜,殷鸿尧,等. 高分子材料科学与工程. 2020, 36(10), 1.
21 Wang L L. Preparation and application of paraffin microcapsule phase change energy storage materials. Master's Thesis, Hunan Institute of Science and Technology, China, 2021 (in Chinese).
王莉莉. 石蜡微胶囊相变储能材料的制备及应用. 硕士学位论文,湖南理工学院,2021.
22 Huang L K. Journal of Chongqing University of Technology, 2022, 36(2), 101 (in Chinese).
黄兰可. 重庆理工大学学报(自然科学) , 2022, 36(2), 101.
23 Wang Y B, Li J W, Miao W J, et al. Construction and Building Mate-rials, 2021, 22, 297.