碳化硅-六铝酸钙复合材料的抗渣机制:煤气化用无铬耐火材料新探索

doi:10.11896/cldb.21040081

Abstract
Figure/Table
References
Related Citation (2)

Download:

Full Text ( PDF ) (5308KB)
Export: BibTeX | EndNote (RIS)

Abstract High chromium refractory has been used as the lining of coal water slurry gasifier for a long time because of its excellent corrosion resistance. It has been a problem for many years to replace it with chrome free refractories. Silicon carbide and calcium hexaaluminate composite refractories (SiC-CA₆, SCA) were prepared by pressing and burning the mixture of silicon carbide particles and calcium hexaaluminate powders. The slag resistance tests with gasifier slag for high chromium refractory and SCA were carried out at 1 500 ℃ by crucible method and rotary slag resis-tance method, respectively. The erosion depth and penetration depth of the samples after slag tests were measured,and cracks were observed. The chemical compositions, phase compositions and microstructure of refractories and slags before and after slag tests were analyzed by SEM, EDS and XRD. The slag corrosion behavior and slag resistance mechanism of the new chrome-free refractory were explored. The results show that SCA has better slag penetration resistance and thermal shock resistance than high chromium refractory. The corrosion of SCA with slag is very weak because their reaction is only in the contact area. Once the slag infiltrates from the refractory surface, a kind of glass phase with high viscosity, whose components are mainly Al₂O₃, SiO₂ and CaO, will be formed by the reaction of slag and refractory at the interface. And then the glass phase fills the pores and makes the dense microstructure. A shield with the similar chemical composition of slag is formed at the interface between slag and SCA, which effectively prevents the erosion and penetration of slag. SCA has the potential to be used in coal water slurry gasi-fier because of its excellent comprehensive properties.

Key words： coal gasification chrome-free refractory calcium hexaaluminate slag resistance test silicon carbide composite refractories

Published: Online: 2022-10-26

CLC number:

TQ175

Fund:National Natural Science Foundation of China (U1604252, 52072346).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SUN Honggang
	SI Yaochen
	XIA Miao
	LI Hongxia
	ZHAO Shixian
	DU Yihao
	SHANG Xinlian

Cite this article:

SUN Honggang,SI Yaochen,XIA Miao, et al. Slag Resistance Mechanism of SiC-CA₆ Composites: New Exploration of Chrome-free Refractories for Coal Gasification[J]. Materials Reports, 2022, 36(20): 21040081-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21040081 OR http://www.mater-rep.com/EN/Y2022/V36/I20/21040081

1 Li H X, Sun H G. Refractories, 2018,52(2), 81(in Chinese).
李红霞, 孙红刚. 耐火材料, 2018, 52(2), 81.
2 Chen Z Y. Refractories, 2010, 44(S1), 6(in Chinese).
陈肇友. 耐火材料, 2010, 44(S1), 6.
3 Mao Y D, Liu L, Li K Z. Materials Reports B:Research Papers, 2020, 34(10), 20061(in Chinese).
毛燕东, 刘雷, 李克忠. 材料导报:研究篇, 2020, 34(10), 20061.
4 Kwong K, Bennett J, Nakano J. In: Ninth International Conference on Molten slags, fluxes and salts (Molten 12). Beijing, China, 2012, pp.403.
5 Li H X. Refractory for coal gasification and its engineering application, Chemical Industry Press, China, 2020(in Chinese).
李红霞. 煤气化装置用耐火材料与工程应用, 化学工业出版社, 2020.
6 Lim K. Interceram, 1983, 32(4), 34.
7 Bennett J P, Kwong K S. Metallurgical and Materials Transactions A, 2011, 42(4), 888.
8 Chen J, Xiao J, Zhang Y, et al. Journal of the American Ceramic Society, 2020, 103(5), 3299.
9 Bennett J P, Riggs B W, Kwong K S, et al. In: Proceedings of the Unified International Technical Conference on Refractories. Vancouver, Canada, 2013, pp.1197.
10 Sun H G, Chen J, Fan Z H, et al. Large Scale Nitrogenous Fertilizer Industry, 2011, 34(S2), 108(in Chinese).
孙红刚, 陈杰, 范志辉, 等. 大氮肥, 2011, 34(S2), 108.
11 Qian F, Duan X K, Yang W G, et al. Materials Reports A:Review Papers, 2019, 33(12), 3882(in Chinese).
钱凡, 段雪珂, 杨文刚,等. 材料导报:综述篇,2019,33(12),3882.
12 Li G H, Tian Z Q, Chen S J et al. Materials Reports, 2014, 28(Z1), 328(in Chinese).
李国华, 田志强, 陈树江, 等. 材料导报, 2014, 28(Z1), 328.
13 Mandal S, Kumar C J D, Kumar D, et al. Journal of the American Ceramic Society, 2020, 103(12), 7095.
14 Yan W, Li N. Materials Reports, 2008, 22(Z1), 412(in Chinese).
鄢文, 李楠. 材料导报, 2008, 22(Z1), 412.
15 CaI B L. Study on the corrosion mechanism of refractory materials for coal-water slurry gasifier. Ph.D. Thesis, University of Science and Technology Beijing, China, 2018.(in Chinese).
蔡斌利. 水煤浆气化装置用耐火材料侵蚀机理研究. 博士学位论文, 北京科技大学, 2018.
16 Hemrick J G, Armstrong B, Rodrigues-Schroer A, et al. In: Proceedings of the Unified International Technical Conference on Refractories. Vancouver, Canada, 2013,pp.1211.
17 Bennett J P, Kwong K S, Powell C P, et al. In: 20th Annual Conference on Fossil Energy Materials. Knoxville, USA, 2006, pp.200.
18 Bie C, Sang S, Li Y, et al. Ceramics International, 2016, 42(12), 14161.
19 Dai L M, Xiao G Q, Ding D H. Materials Reports,, 2021, 35(3), 3057(in Chinese).
代黎明, 肖国庆, 丁冬海. 材料导报, 2021, 35(3), 3057.
20 Kwong K S, Bennett J P, Powell C A, et al.In: Unified International Technical Conference on Refractories. Orlando, Florida, USA, 2005, pp.70.
21 Sun H G, Xia L H, Tao L P, et al. In: The Unified International Technical Conference on Refractories. Santiago, Chile, 2017, pp.630.
22 Cai B L, Li H X, Zhao S X, et al. Refractories, 2016, 50(6), 411(in Chinese).
蔡斌利, 李红霞, 赵世贤, 等. 耐火材料, 2016, 50(6), 411.
23 Cai B L, Li H X, Zhao S X. Journal of the Chinese Ceramic Society, 2018,46(3), 434(in Chinese).
蔡斌利, 李红霞, 赵世贤, 等. 硅酸盐学报, 2018,46(3), 434.
24 Cai B, Li H, Zhao S, et al. Ceramics International, 2018, 44(5), 4592.
25 Li H X, Sun H G, Li P T, et al. Large Scale Nitrogenous Fertilizer Industry, 2018, 41(2), 80(in Chinese).
李红霞, 孙红刚, 李鹏涛, 等. 大氮肥, 2018, 41(2), 80.
26 Si Y C, Li H X, Sun H G, et al. Refractories, 2020, 54(1), 52(in Chinese).
司瑶晨, 李红霞, 孙红刚, 等. 耐火材料, 2020, 54(1), 52.
27 Si Y C. Study on coal slag corrosion resistance of SiC-CA₆ composites. Master’s Thesis, Sinosteel Luoyang Institute of Refractories Research, China, 2020(in Chinese).
司瑶晨. SiC-CA₆复合材料的抗煤渣侵蚀性能研究. 硕士学位论文,中钢集团洛阳耐火材料研究院, 2020.
28 Wang L. Preparation of SiC-MgAl₂O₄ composite and its resistance to coal slag corrosion. Master’s Thesis, Sinosteel Luoyang Institute of Refractories Research, China, 2019.(in Chinese).
王岚. SiC-MgAl2O₄复合材料的制备及抗煤渣侵蚀性能研究. 硕士学位论文,中钢集团洛阳耐火材料研究院, 2019.
29 Si Y C, Xia M, Sun H G, et al. Refractories, 2021, 55(1), 40(in Chinese).
司瑶晨,夏淼, 孙红刚, 等. 耐火材料, 2021, 55(1), 40.
30 Wang L, Li H X, Sun H G, et al. Refractories, 2019, 53(5), 359(in Chinese).
王岚, 李红霞, 孙红刚, 等. 耐火材料, 2019, 53(5), 359.