选区激光熔化成型4Cr5MoSiV1钢的组织与性能优化

doi:10.11896/cldb.20050017

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (6662KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to optimize the microstructure and properties of 4Cr5MoSiV1 steel formed by selective laser melting technology, the effects of support structure and laser remelting on the morphology, microstructure, microhardness and tensile properties of 4Cr5MoSiV1 steel were studied. The results show that mechanical properties of the samples can be improved by fine grain strengthening, solution strengthening, precipitation strengthening and metallurgical quality increasing, and the metallurgical quality has a higher influence on the mechanical properties. The tensile strength, elongation after fracture, microhardness of top surface and bottom surface of 4Cr5MoSiV1 steel are 948.6 MPa, 9.3%, 578.2HV and 560.4HV respectively. The reduction of X/Y spacing of the support structure can increase the number of support structures, improve the support function, enhance the thermal conductivity, and increase the fine grain strengthening, solution strengthening and metallurgical quality of the samples, so the mechanical properties of the samples are improved. Cutting distance has little effect on the mechanical properties of the samples, but the difficulty of support removal is reduced. The effect of laser boundary remelting on the mechanical properties of the sample is small. After laser surface remelting, the grain coarsening and the second phase precipitation in the grain increase, the splashing particles, black smoke particles and pore defects basically disappear, and the mechanical properties of samples are significantly improved. The tensile strength, elongation after fracture, microhardness of top surface and bottom surface are 1 387.2 MPa, 14.6%, 632.4HV and 608.4HV respectively.

Key words： selective laser melting 4Cr5MoSiV1 steel support structure laser remelting microstructure

Published: 07 September 2021

CLC number:

TG142.1

About author:: Shuai Chen iscurrently a doctoral student at the Shi-jiazhuang Branch, Army Engineering University of PLA. His research work mainly focuses on the basic theory and application research of rapid prototyping of equipment parts.
Fenghe Tao, a professor and doctoral tutor of the Shi-jiazhuang Branch, Army Engineering University of PLA. He won 2 first prizes, 7 second prizes and 15 third prizes for military scientific and technological progress, and published more than 100 academic papers.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CHEN Shuai
	TAO Fenghe
	JIA Changzhi
	SUN Heyang

Cite this article:

CHEN Shuai,TAO Fenghe,JIA Changzhi, et al. Optimization of Microstructure and Properties of 4Cr5MoSiV1 Steel Formed by Selective Laser Melting[J]. Materials Reports, 2021, 35(16): 16126-16132.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20050017 OR http://www.mater-rep.com/EN/Y2021/V35/I16/16126

1 Xu G C, Li J W, Zuo P P, et al. Materials Review B: Research Papers, 2020(4), 08159(in Chinese).
徐国财, 黎军顽, 左鹏鹏, 等. 材料导报:研究篇, 2020(4), 08159.
2 Wang W Q, Li Y Q, Li X, et al. Materials Review B: Research Papers, 2020(1), 02077(in Chinese).
王文权, 李雅倩, 李欣, 等. 材料导报:研究篇, 2020(1), 02077.
3 Wen S F, Ji X T, Zhou Y, et al. Chinese Journal of Mechanical Engineering, 2018, 31(6), 68.
4 Wang M, Wu Y, Wei Q S, et al. Metals, 2020, 10(1), 116.
5 Ren B, Lu D H, Zhou R, et al. Metals, 219, 34(8), 1415.
6 Liu Z Y, Qian B, Li P, et al. Mechanical Science and Technology for Aerospace Engineering, 2019, 38(4), 566(in Chinese).
刘志远, 钱波, 李培, 等. 机械科学与技术, 2019, 38(4), 566.
7 Li B Q, Li Z H, Liu B, et al. Applied Laser, 2018, 38(5), 742(in Chinese).
李保强, 李忠华, 刘斌, 等.应用激光, 2018, 38(5), 742.
8 Wang D, Wu S B, Fu F, et al. Materials and Design, 2017, 117, 121.
9 Liu Y, Yang Y Q, Mai S Z, et al. Materials and Design, 2015, 87, 797.
10 Li D F. Optimization of support structure and technology research based on selective laser melting. Master's Thesis, Beijing University of Technology, China, 2017(in Chinese).
李东方. 基于激光选区熔化成型的支撑结构优化及工艺研究. 硕士学位论文, 北京工业大学, 2017.
11 Calignano F.Materials and Design, 2014, 64, 203.
12 Wang D, Ye G Z, Dou W H, et al. Optics and Laser Technology, 2020, 121, 105678.
13 Zhang W Y.Welding metallurgy, Machinery Industry Press, China, 1996(in Chinese).
张文钺.焊接冶金学, 机械工业出版社, 1996.
14 Chen S, Tao F H, Jia C Z.Foundry Technology, 2019, 40(7), 657(in Chinese).
陈帅, 陶凤和, 贾长治.铸造技术, 2019, 40(7), 657.
15 Chen S, Tao F H, Jia C Z. Chinese Journal of Lasers, 2019, 46(10), 1002005(in Chinese).
陈帅, 陶凤和, 贾长治.中国激光, 2019, 46(10), 1002005.
16 Ma M M. A comparative study on fundamentals of two typical laser additive manufacturing technologies of metallic. Ph.D. Thesis, Huazhong University of Science and Technology, China,2016(in Chinese).
马明明. 两种典型金属零部件激光增材制造技术基础比较研究. 博士学位论文, 华中科技大学, 2016.
17 Lei Y P, Murakawa H, Shi Y W, et al. Computational Materials Science, 2001, 21, 276.
18 Li C. Metallography principle, Harbin Institute of Technology Press, China, 1996(in Chinese).
李超.金属学原理, 哈尔滨工业大学出版社, 1996.
19 Hou W, Chen J, Chu S L, et al. Chinese Journal of Lasers, 2018, 45(7), 0702003(in Chinese).
侯伟, 陈静, 储松林, 等.中国激光, 2018, 45(7), 0702003.