硝酸和硝酸铈铵协同氧化改性木质活性碳纤维

doi:10.11896/j.issn.1005-023X.2018.09.015

Abstract
Figure/Table
References
Related Citation (1)

Download:

Full Text ( PDF ) (1185KB)
Export: BibTeX | EndNote (RIS)

Abstract The wooden activated carbon fiber(WACF) was immersed 5 h for oxidative modification, 0.005 mol/L to 0.050 mol/L ammonium ceric nitrate and 1.0 mol/L to 7.0 mol/L nitric acid were added, the modification temperature was 23 ℃ to 83 ℃. The surface and structural properties were characterized by XPS, RAMAN, water vapor adsorption and mercury adsorption. The results showed that the average value of oxygen/carbon ratio of modified WACF was 0.160, the content of phenolic groups and alcohol groups increased, it presented an inverse correlation between the content of carboxyeste and the intensity of oxidation. The degree of graphitization on the sample surface reduced slightly, and the degree of graphitization of the sample core increased. The pore volume decreased after synergistic modification, the specific surface area for water adsorption increased significantly. The adsorption capacity for mercury and the specific surface area for water adsorption were linearly related to the concentration of oxygen atoms. Nitric acid can increase the content of functional groups, and has little effect on the structure. While increasing the content of the functional group, ceric ammonium nitrate has a certain adjustment on the structure and pore, and definite selectivity for the adsorbed objects of diffe-rent diameters, which extends the application range of WACF.

Key words： wooden active carbon fiber ceric ammonium nitrate surface oxidation modification water adsorption synerge-tic modification

Published: 06 July 2018

CLC number:	TQ424.1+9
	TQ351.21

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	GAO Wei
	ZHAO Guangjie

Cite this article:

GAO Wei,ZHAO Guangjie. Synergetic Oxidation Modification of Wooden Activated Carbon Fiber with Nitric Acid and Ceric Ammonium Nitrate[J]. Materials Reports, 2018, 32(9): 1507-1512.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.09.015 OR http://www.mater-rep.com/EN/Y2018/V32/I9/1507

1 Prasad G K, Singh B, Batra K, et al.Comparative evaluation of modified whetlerites and impregnated carbons for sulphur mustard degradation[J].Carbon,2010,48(1):2.
2 Jiang L J, Liu Q C, Zhao Q, et al. Promotional effect of Ce on the SCR of NO with NH₃ at low temperature over MnO(x) supported by nitric acid-modified activated carbon[J].Research on Chemical Intermediates,2018,44(3):1729.
3 Yao S, Yang Y, Song S, et al.Preparation, characterization and photocatalytic activity of cerium-doped titanium dioxide supported on activated carbon fiber composite[J].Indian Journal of Chemistry,2014,53(6):665.
4 Chen S X, Chen J L,Wu Q Y. Chemical structure modification of activated carbon fibers by cerous nitrate [J].New Carbon Materials,2006,21(3):206(in Chinese).
陈水挟,陈建良,武清毓.利用铈盐改性修饰活性炭纤维结构[J].新型炭材料,2006,21(3):206.
5 Wang G J,Liu Y,Fu X T,et al. Preparation of cerium supported on modified activated carbon as adsorbent and its application in desulfurization[J].Petrochemical Technology,2014,43(6):625(in Chinese).
王广建,刘影,付信涛,等.改性活性炭负载铈吸附剂的制备及其脱硫性能[J].石油化工,2014,43(6):625.
6 Sarkisov L, Centineo A, Brandani S. Molecular simulation and experiments of water adsorption in a high surface area activated carbon: Hysteresis, scanning curves and spatial organization of water clusters[J].Carbon,2017,118:127.
7 Liu L, Tan S, Horikawa T, et al.Water adsorption on carbon—A review[J].Advances in Colloid and Interface Science,2017,250:64.
8 Charriere D, Behra P. Water sorption on coals[J].Journal of Colloid and Interface Science,2010,344(2):460.
9 Abiko H. Adsorption and desorption behavior of water and organic vapor of allophanic soil-templated porous carbon materials[J].Journal of the Ceramic Society of Japan,2012,120(1408):603.
10 Soares L C, Egreja Filho F B, Windmoller C C, et al.Mercury quantification in soils using thermal desorption and atomic absorption spectrometry: Proposal for an alternative method of analysis[J].Revista Brasileira De Ciencia Do Solo,2015,39(4):1100.
11 Ribeiro R F L, Germano A.Development and validation of a method for the determination of Hg in animal tissues (equine muscle, bovine kidney and swine kidney, and poultry muscle) by direct mercury analysis (DMA)[J].Microchemical Journal,2015,121:237.
12 Graci S, Collura R, Cammilleri G, et al.Mercury accumulation in mediterranean fish and cephalopods species of sicilian coasts: Correlation between pollution and the presence of anisakis parasites[J].Natural Product Research,2017,31(10):1156.
13 Ferlin S, Fostier A H, Melendez-Perez J J. A very simple and fast analytical method for atmospheric particulate-bound mercury determination[J].Analytical Methods,2014,6(13):4537.
14 Ma X, Zhao G.Variations in the microstructure of carbon fibers prepared from liquefied wood during carbonization[J].Journal of Applied Polymer Science,2011,121(6):3525.
15 Liu WJ, Zhao G J.Effect of temperature and time on microstructure and surface functional groups of activated carbon fibers prepared from liquefied wood[J].Bioresources,2012,7(4):5552.
16 Shimodaira N, Masui A.Raman spectroscopic investigations of activated carbon materials[J].Journal of Applied Physics,2002,92(2):902.
17 Wang Z, Yang F L, Zhang J, et al. Impact of EGR rate on soot nanostructure from a diesel engine fueled with biodiesel[J].Spectroscopy and Spectral Analysis,2017,37(6):1973.
18 Macedo J S, Otubo L, Ferreira O P, et al.Biomorphic activated po-rous carbons with complex microstructures from lignocellulosic residues[J].Microporous and Mesoporous Materials,2008,107(3):276.
19 Hefti M, Joss L, Marx D, et al. An experimental and modeling study of the adsorption equilibrium and dynamics of water vapor on activated carbon[J].Industrial & Engineering Chemistry Research,2015,54(48):12165.
20 Horikawa T, Muguruma T, Do D D, et al. Scanning curves of water adsorption on graphitized thermal carbon black and ordered mesoporous carbon[J].Carbon,2015,95:137.
21 Mamontov E, Yue Y, Bahadur J, et al.Hydration level dependence of the microscopic dynamics of water adsorbed in ultramicroporous carbon[J].Carbon,2017,111:705.
22 Ren J, Ye S, Chen J, et al.Research on surface properties of modified activated carbon fiber and its mercury adsorption performance[J].Acta Scientiae Circumstantiae,2010,30(7):1410.
23 Huang Z H, Kang F Y, Wu H, et al. Adsorption of benzene and methylethyl-ketone vapors at low concentration by wet oxidized po-rous carbons[J].J Tsinghua University (Science & Technology),2000,40(10):111(in Chinese)
黄正宏,康飞宇,吴慧,等.湿氧化改性多孔炭对低浓度苯和丁酮蒸汽的吸附[J].清华大学学报(自然科学版),2000,40(10):111.