镍铝青铜基冷喷涂Cu402F与Cu涂层的力学性能

doi:10.11896/j.issn.1005-023X.2018.10.009

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (5425KB)
Export: BibTeX | EndNote (RIS)

Abstract Aiming at common failure modes of nickel aluminum bronze propeller in actual working condition, copper and Cu402F coating were deposited on nickel aluminum bronze 9442# alloy by cold spraying. Surface and cross-section morphology of coating were observed by OM and SEM; the phases of coating were tested by XRD; bonding strength, micro-hardness, elasticity modulus and tribologic properties were analyzed by tensile testing machine, nano indentation testing machine and friction and wear tester. The results revealed that Cu402F and copper coating was compact, which were 900 μm, the average bonding strength were 34.37 MPa and 18.6 MPa, micro-hardness were 5.79 GPa and 2.11 GPa, and elasticity modulus were 198.23 GPa and 138.54 GPa respectively. Friction coefficient and wear rate of Cu402F coating were lower, tribology properties was better than copper coating.

Key words： nickel aluminum bronze cold spray mechanical property

Published: 06 July 2018

CLC number:

TB301

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CHEN Zhenghan
	SUN Xiaofeng
	LI Zhanming
	SHI Yupeng

Cite this article:

CHEN Zhenghan,SUN Xiaofeng,LI Zhanming, et al. Mechanical Properties of Cold Sprayed Cu402F and Cu Coating Deposited on Nickel Aluminum Bronze[J]. Materials Reports, 2018, 32(10): 1618-1622.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.10.009 OR http://www.mater-rep.com/EN/Y2018/V32/I10/1618

1 刘道新.材料的腐蚀与防护[M].西安:西北工业大学出版社,2006:307.
2 Guo Zeliang, Fang Liang, Tang Wenxin. A review of corrosion properties of copper-alloys used in seawater pumps[J]. Materials Review,2003,17(8):22(in Chinese).
郭泽亮,方亮,汤文新.海水泵用铜合金的腐蚀性能评述[J].材料导报,2003,17(8):22.
3 Sun Feilong, Li Xiaogang, Lu Lin,et al. Corrosion behavior of copper alloys in deep ocean environment of South China Sea[J]. Acta Metallurgica Sinica,2013,49(10):1211.
4 Ji Yangyang, Tian Guizhong, Zhou Honggen. Development and present situation of marine propeller advance manufacturing techno-logy[J]. Ship Science and Technology,2015,37(5):9(in Chinese).
季洋阳,田桂中,周宏根.船用螺旋桨先进制造技术研究进展[J].舰船科学技术,2015,37(5):9.
5 兰现卿,韦玮,谭洪武,等.船舶铜质螺旋桨的修复技术[J].黄河水利职业技术学院学报,2011,23(1):24.
6 Zou Jiasheng, Luo Xinfeng, Ji Zuchun, et al. Study on welding properties of copper alloy for warship propeller[J]. Journal of Jiangsu University of Science and Technology (Natural Science Edition),2006,20(3):81(in Chinese).
邹家生,罗新峰,姬祖春,等.舰船螺旋桨用铜合金焊接性研究[J].江苏科技大学学报(自然科学版),2006,20(3):81.
7 Li C J. The state-of-art of research and development on cold spraying in China[J]. China Surface Engineering,2009,22(4):5(in Chinese).
李长久.中国冷喷涂研究进展[J].中国表面工程,2009,22(4):5.
8 Lupoi R, O'Neill W. Powder stream characteristics in cold spray nozzles [J]. Surface & Coatings Technology,2011,206(6):1069.
9 Kumar S, Arjuna Rao A. Influence of coating defects on the corrosion behavior of cold sprayed refractory metals[J]. Applied Surface Science,2017,396:760.
10 Assadi H, Kreye H, Gartner F. Cold spray—A materials perspective[J]. Acta Materialia,2016,116:382.
11 Chen Sida. Repair technology of copper alloy properller[J]. China Ship Repairing,1996(5):7(in Chinese).
陈斯达.铜合金螺旋桨修理技术[J].中国修船,1996(5):7.
12 Hedda Nordby Krogstad, Roy Johnsen. Corrosion properties of nickel-aluminium bronze in natural seawater—Effect of galvanic coupling to UNS S31603[J]. Corrosion Science,2017,121:43.
13 Li Wenya, Li Changjiu, Wang Yuyue, et al. Eeffct of parameters of cold sprayed Cu particles on its impacting behavior[J]. Acta Metallurgica Sinica,2005,41(3):282(in Chinese).
李文亚,李长久,王豫跃,等.冷喷涂Cu粒子参量对其碰撞变形行为的影响[J].金属学报,2005,41(3):282.
14 Zhang Huabing. Behaviors of particles and microstructures, mecha-nical properties of coating in cold spray[D]. Shanghai: Shanghai Jiao Tong University,2006(in Chinese).
章华兵.冷喷涂粒子变形结合行为及涂层组织力学性能研究[D].上海:上海交通大学,2006.
15 刘家浚.材料磨损原理及其耐磨性[M].北京:清华大学出版社,1993:53.