考虑静荷载与环境耦合作用的钢结构涂层劣化实验研究

doi:10.11896/cldb.22040312

Abstract
Figure/Table
References
Related Citation (8)

Download:

Full Text ( PDF ) (61370KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to study the deterioration performance of steel structure coating under the static load, temperature variation and sandstorm erosion, a static loading system for steel structure coating specimen was designed. Then the experiment research was carried out on the conventional and durable coating system of steel bridges by static loading, temperature control and the airflow spray method. The degradation of coatings under the coupling action of static load and temperature variation were tested by the pull-of test, and the coating damage modes of adhesion and cohesive were quantitatively measured. Combined with pull-of test and thickness measurement results, the dynamic deterioration process of coating resistance was obtained. The erosion resistance of coatings under the static load and temperature variation was studied by the airflow spray method, and the degradation process of coatings working performance under the coupling action of static load and environment was obtained based on the experimental results. The results show that the coupling effect of static load and environment makes the resistance of topcoat attenuate until its protective function is destroyed, the temperature variation causes coating materials transform to brittle materials, static load accelerates the dete-rioration rate of coating, and sandstorm erosion is going to strip coatings from the system. Then the coatings are deactivated successively since the coupling action cause the recession of system resistance, the coating system completely loses resistance and eventually peels off from the substrate. For the experimental coating systems, after 30 d of static load and temperature variation, the adhesion of coating decreased by 8.97%, the thickness, erosion amount and critical erosion angle increased by 25.3%, 46.15% and 17.4%, respectively.

Key words： steel structure coating static load large temperature difference sand erosion deterioration mechanism experimental research

Published: Online: 2024-10-12

CLC number:

TU593

Fund:This work was financially supported by the Major Project of National Natural Science Foundation of China (11790281) and Scientific Research Project of Gansu Provincial Department of Transportation (2020-08).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	QI Yanfu
	LIN Pengzhen
	LI Yan
	PAN Yalei

Cite this article:

QI Yanfu,LIN Pengzhen,LI Yan, et al. Experimental Study of Steel Structure Coating Deterioration Considering Coupling Effect of Static Load and Environment[J]. Materials Reports, 2024, 38(18): 22040312-10.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22040312 OR http://www.mater-rep.com/EN/Y2024/V38/I18/22040312

1 Lyon S B, Bingham R, Mills D J. Progress in Organic Coatings, 2017, 102, 2.
2 Tang P, Liu L X, Cao D P, et al. Materials Protection, 2020, 53(2), 126(in Chinese).
汤朋, 刘兰轩, 曹东萍, 等. 材料保护, 2020, 53(2), 126.
3 Bian M H, Peng J N, Yin L Q, et al. Materials Protection, 2019, 52(7), 128(in Chinese).
边美华, 彭家宁, 尹立群, 等. 材料保护, 2019, 52(7), 128.
4 MayerP, Lubecki M, Stosiak M, et al. International Journal of Adhesion and Adhesives, 2022, 117, 103183
5 Miszczyk A, Darowicki K. Progress in Organic Coatings, 2003, 46(1), 49.
6 Pan Y, Zhang S P, Zhou J L, et al. Paint and Coatings Industry, 2010, 40(4), 68(in Chinese).
潘莹, 张三平, 周建龙, 等. 涂料工业, 2010, 40(4), 68.
7 Shin A, Bhang S, Kim H. et al. Journal of Industrial and Engineering Chemistry, 2021, 97, 402.
8 Hao Y H, Duan G L, Ren Y, et al. Journal of Building Materials, 2015, 18(4), 596(in Chinese).
郝贠洪, 段国龙, 任莹, 等. 建筑材料学报, 2015, 18(4), 596.
9 Hao Y H, Li J, Liu Y L. Materials Reports, 2019, 33(8), 1389(in Chinese).
郝贠洪, 李洁, 刘永利. 材料导报, 2019, 33(8), 1389.
10 Hao Y H, Li J, Tian X L, et al. Journal of Building Materials, 2020, 23(2), 407(in Chinese).
郝贠洪, 李洁, 田旭乐, 等. 建筑材料学报, 2020, 23(2), 407.
11 Qian A, Wang P, Tan X M, et al. Mechanical Science and Technology for Aerospace Engineering, 2017, 36(S1), 84(in Chinese).
钱昂, 王鹏, 谭晓明, 等. 机械科学与技术, 2017, 36(S1), 84.
12 Smith S, Caillouette L, Jourdan J, et al. In:Pipelines 2015 Conference:Recent Advances in Underground Pipeline Engineering and Construction. Maryland, 2015, pp.1677.
13 Fredj N, Cohendoz S, Feaugas X, et al. Progress in Organic Coatings, 2008, 63(3), 316.
14 Fredj N, Cohendoz S, Feaugas X, et al. Progress in Organic Coatings, 2011, 72(3), 260.
15 Pan C, Cui Y, Liu L, et al. Journal of Materials Engineering and Performance, 2020, 29(2), 1400.
16 Lazorenko G, Kasprzhitskii A, Nazdracheva T. Construction and Building Materials, 2021, 288, 123115.
17 Li K. Research for the steel highway bridge design method of probability limited status based on reliability theory. Ph.D. Thesis, Tongji University, China, 2007 (in Chinese).
李昆. 基于可靠度理论的公路钢桥概率极限状态设计方法研究. 博士学位论文, 同济大学, 2007.
18 Fang B Y, Han E H, Wang J Q, et al. Journal of Aeronautical Materials, 2003, 23(3), 33(in Chinese)
方丙炎, 韩恩厚, 王俭秋, 等. 航空材料学报, 2003, 23(3), 33.
19 Nachlas J A. Quality and Reliability Engineering International, 1986, 2(1), 3.
20 Wang Y D, Tang Y C. Communications in Statistics:Theory and Methods, 2021, 49(13/15), 3663.
21 Li Y Y, Zhang Q, Chen Y, et al. Journal of Desert Research, 2014, 34(1), 206(in Chinese).
李岩瑛, 张强, 陈英, 等. 中国沙漠, 2014, 34(1), 206.
22 Zhu W B, Zhu L Q. Journal of Henan University (Natural Science), 2017, 47(6), 631(in Chinese).
朱文博, 朱连奇. 河南大学学报(自然科学版), 2017, 47(6), 631.
23 Song J, Chun X, Bai X M, et al. Journal of Desert Research, 2016, 36(3), 597(in Chinese).
宋洁, 春喜, 白雪梅, 等. 中国沙漠, 2016, 36(3), 597.
24 Nguyen T, Hubbard J, Pommersheim J. Journal of Coatings Technology, 1996, 68(855), 45.
25 Kallias A N, Imam B, Chryssanthopoulos M K. Structure and Infrastructure Engineering, 2017, 13(4), 440.