MU10再生混凝土承重砌块力学性能与抗冻性试验研究

doi:10.11896/cldb.22070011

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (17078KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to further improve the utilization rate of waste concrete and promote the application of recycled concrete bearing blocks in severe cold areas, based on the analysis of the physical properties of recycled aggregate, the effects of 100% recycled coarse aggregate replacement rate, water-binder ratio, water consumption and fly ash content were considered, and the mix ratio of C30 recycled concrete was designed by orthogonal tests to prepare MU10 recycled concrete load-bearing blocks. By analyzing the mechanical properties of MU10 recycled concrete load-bearing blocks, the optimal mix ratio of MU10 recycled concrete load-bearing blocks was determined, and the frost resistance of MU10 recycled concrete load-bearing blocks was verified by environmental simulation box. The results show that compared with natural aggregate, recycled aggregate has a rougher surface, with some old cement mortar attached. It has the characteristics of low density, high porosity, water absorption and mud content, and the crushing index is about twice that of natural aggregate. The optimal mix ratio of MU10 recycled concrete load-bearing blocks is 1 172 kg/m³ recycled coarse aggregate, 578 kg/m³ natural river sand, 400 kg/m³ cement, 100 kg/m³ fly ash and 150 kg/m³ water. Its compressive strength is 11.4 MPa and flexure strength is 2.1 MPa, which can be used for load-bearing and seismic resistant masonry structures. After 50 freeze-thaw cycles, the quality loss and strength loss of MU10 recycled concrete load-bearing block are 1.2% and 18.1%, respectively. The frost resistance meets the requirements, and it can be used as a new wall material in severe cold areas.

Key words： recycled aggregate recycled concrete load-bearing block mixture ratio mechanical property frost resistance

Published: Online: 2024-06-25

CLC number:

TU522.3

Fund:National Natural Science Foundation of China (51708091) and the 13th Five-Year Key Project of the Education Department of Jilin Province(JJKH20200123KJ).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	QI Yunpeng
	WANG Qiusheng
	QIN Li
	SHANG Xiaoyu

Cite this article:

QI Yunpeng,WANG Qiusheng,QIN Li, et al. Experimental Study on Mechanical Properties and Frost Resistance of MU10 Recycled Concrete Load-Bearing Block[J]. Materials Reports, 2024, 38(11): 22070011-7.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22070011 OR http://www.mater-rep.com/EN/Y2024/V38/I11/22070011

1 Wang C H, Xiao J Z. China Civil Engineering Journal, 2022, 55(5), 37 (in Chinese).
王春晖, 肖建庄. 土木工程学报, 2022, 55(5), 37.
2 Shi X S, Wang Q Y, Qiu C C, et al. Advanced Engineering Sciences, 2010, 42(S1), 170 (in Chinese).
石宵爽, 王清远, 邱慈长, 等. 工程科学与技术, 2010, 42(S1), 170.
3 Gong L, Liang Y, Gong X L, et al. Journal of Basic Science and Engineering, 2023, 31(4), 1006 (in Chinese).
贡力, 梁颖, 宫雪磊, 等. 应用基础与工程科学学报, 2023, 31(4), 1006.
4 Liu K, Fu K, Sang Y, et al. Journal of Building Engineering, 2024, 90, 109450.
5 Zhu Y G, Rong D P, Xu P Z, et al. Materials Reports, 2021, 35(4), 4074 (in Chinese).
朱亚光, 戎丹萍, 徐培蓁, 等. 材料导报, 2021, 35(4), 4074.
6 Sun D S, Li Z Y, liu K W, et al. Materials Reports, 2021, 35(11), 11027 (in Chinese).
孙道胜, 李泽英, 刘开伟, 等. 材料导报, 2021, 35(11), 11027.
7 Yang L J, Li S Q. Advances in Materials Science and Engineering, 2019, 2019(6), 12.
8 Yuan H Q, Zhu L H, Wang Y X, et al. Advances in Materials Science and Engineering, 2021, 2021(7), 13.
9 Zhou W, Lu L H, Li Z. Key Engineering Materials, 2012, 1730, 509.
10 Zhuo L, Chen B F. Bulletin of the Chinese Ceramic Society, 2013, 32(10), 2155 (in Chinese).
卓玲, 陈宝璠. 硅酸盐通报, 2013, 32(10), 2155.
11 He X X, Liang X M. Advanced Materials Research, 2014, 3381, 1004.
12 Zhu L H, Dai J, Bai G L, et al. Construction and Building Materials, 2015, 94(9), 620.
13 Yu J, Zhang F, Bai G. Materials Research Innovations, 2015, 19, 579.
14 Zhang H Z, Zheng J L. Engineering Journal of Wuhan University, 2015, 48(6), 799.
张会芝, 郑建岚. 武汉大学学报(工学版), 2015, 48(6), 799.
15 Zheng J L, Zhang H Z. Engineering Mechanics, 2015, 32(5), 51 (in Chinese).
郑建岚, 张会芝. 工程力学, 2015, 32(5), 51.
16 Zhang H Z, Zheng J L. Journal of Building Materials, 2016, 19(2), 304 (in Chinese).
张会芝, 郑建岚. 建筑材料学报, 2016, 19(2), 304.
17 Cao W Q, Huang L, Gao Q, et al. Journal of Railway Science and Engineering, 2019, 16(2), 384 (in Chinese).
曹文权, 黄靓, 高琦, 等. 铁道科学与工程学报, 2019, 16(2), 384.
18 Shang X Y, Zheng S S, Xu Q, et al. Journal of Building Materials, 2015, 18(6), 1045 (in Chinese).
商效瑀, 郑山锁, 徐强, 等. 建筑材料学报, 2015, 18(6), 1045.
19 Chen W, Liu M, Zhang M L, et al. Journal of Central South University(Science and Technology), 2021, 52(11), 4063 (in Chinese).
陈伟, 刘蜜, 张明亮, 等. 中南大学学报(自然科学版), 2021, 52(11), 4063.
20 Chen W, Ying Z M Y, Zhang M L, et al. Earthquake Engineering and Engineering Dynamics, 2021, 41(4), 120 (in Chinese).
陈伟, 应湛梦云, 张明亮, 等. 地震工程与工程振动, 2021, 41(4), 120.
21 Qin L, Ding J N, Zhu J S. Transactions of the Chinese Society of Agricultural Engineering, 2017, 33(6), 133 (in Chinese).
秦力, 丁婧楠, 朱劲松. 农业工程学报, 2017, 33(6), 133.
22 Zheng C L, Li S X, Hou Y F, et al. Reviews on Advanced Materials Science, 2022, 61(1), 711.
23 Chen A J, Wang J, Ma Y. Acta Materiae Compositae Sinica, 2015, 32(4), 933 (in Chinese).
陈爱玖, 王静, 马莹. 复合材料学报, 2015, 32(4), 933.
24 Xie G L, Shen X D, Liu J Y, et al. Composites Science and Engineering, 2021(4), 55 (in Chinese).
解国梁, 申向东, 刘金云, 等. 复合材料科学与工程, 2021(4), 55.