| METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
| Effect of Ammonia-type Alkaline Water Chemistry on Corrosion of 690TT |
| ZHAO Yongfu*, TANG Min, JIANG E, YIN Zhaohui, CHEN Zirui, ZHANG Gen, WU Zongpei, LI Yang
|
| Nuclear Power Institute of China, Chengdu 610213, China |
|
|
|
|
Abstract In order to clarify the influence of ammonia-type alkaline water chemistry on the corrosion behaviors of 690TT, the corrosion behavior of 690TT in B-Li-NH4OH and NH4OH solution were studied, the release characteristics of corrosion products from 690TT were analyzed, and the impact of ammonia alkaline solutions on corrosion behavior of 690TT was evaluated comprehensively. The results showed that 690TT was compatible with two kinds of ammonia-type alkaline water chemistry. The surface of 690TT formed dense oxide film, which was composed of NiFe2O4 and few Fe2O3 oxide film. The weight loss and corrosion releasing of 690TT in NH4OH solution were slightly lower than those in B-Li-NH4OH solution. However, the total amount of Ni released by 690TT was contrary to the results above. It could be related to the formation of [Ni(NH3)m]2+complexes between Ni and ammonia. The increasing of Ni releasing had adverse effect on the control of the irradiation field in primary loop in PWR. The results can provide data support for the design and application of ammonia-type alkaline water chemistry.
|
|
Published: 10 April 2024
Online: 2024-04-11
|
|
|
| Fund:Original Foundation of NPIC (YCHJJ17). |
|
|
1 Fruzzetti K,Tran P.Boiling water reactor chemistry performance monitoring report,EPRI,USA,2005,pp.12.
2 Jose S.Hydrogen water chemistry effects on BWR radiation buildup,EPRI,USA,1994,pp.6.
3 Jose S.Corrosion potential measurement sourcebook,EPRI,USA,1991,pp.17.
4 Tang H.Corrosion of heat exchanger tube for PWR steam generators.Master’s Thesis,Shanghai Jiao Tong University,China,2012 (in Chinese).
唐辉.核电站蒸汽发生器传热管耐腐蚀性能研究.硕士学位论文,上海交通大学,2012.
5 Wu X Q,Liu X H,Han E H,et al.Journal of Shanghai University (Natural Science),2015,21(2),141 (in Chinese).
吴欣强,刘侠和,韩恩厚,等.上海大学学报(自然科学版),2015,21(2),141.
6 Kysela J,Zmitko M,Yurmanow V A,et al.Nuclear Engineering and Design,1996,160,185.
7 Chen Z R,Zhao Y F,Tang M,et al.Frontiers in Materials,2022,9,910186.
8 Kim T K,Baek J H,Choi B S,et al.Metals and Materials International,2007,13,47. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2024, Vol. 38 