燃料油与紫外光共同作用下热塑性聚氨酯结构与性能演变规律

doi:10.11896/cldb.22050216

Abstract
Figure/Table
References
Related Citation (4)

Download:

Full Text ( PDF ) (8673KB)
Export: BibTeX | EndNote (RIS)

Abstract Thermoplastic polyurethanes (TPU) have the advantages of good wear resistance and oil resistance, which makes them widely used in the field of oil storage and transportation, but it is found that the combined influence of fuel oil and ultraviolet light will accelerate the aging of materials during use. The research on the evolution of the structure and performance of TPU under the joint action of fuel oil and ultraviolet light has important guiding significance for ensuring the safety of oil storage and transportation containers and improving oil resistance. In this work, TPU was immersed in simulated fuel oil B liquid, gasoline, diesel fuel and aviation kerosene, and ultraviolet aging was carried out at the same time as the sample without oil treatment, and the structure and performance changes of TPU at different aging times were analyzed by FTIR, mechanics, GPC and other characterization methods, and the reasons why fuel oil treatment accelerated the change of TPU structure and performance were analyzed. The results show that with the increase of UV aging time, the chemical bonds such as -N-H bonds and ether bonds in the infrared spectrum of vacuum heat treatment UV aging samples and oil treatment UV aging samples are destroyed, but the change trend of oil treatment samples is more obvious. With the increase of ultraviolet aging time, the molecular weight of the B liquid treated sample shows a trend of first decreasing and then slightly increasing, indicating that the TPU chemical bond is broken first, and then cross-linking and other reactions occurr under the action of light irradiation. After 100 h of UV aging, the mechanical properties of B liquid, gasoline and aviation coal treated samples are basically lost. After UV aging for 200 h, the mechanical properties of the diesel treatment sample are basically lost. Through the enrichment and infrared analysis of the treated B liquid, it is found that after TPU come into contact with the oil, the anti-aging agent in the material precipitates, which significantly reduces the anti-ultraviolet aging performance.

Key words： thermoplastic polyurethanes(TPU) fuel oil UV aging oil resistance

Published: 25 March 2024 Online: 2024-04-07

CLC number:

TQ334.9

Corresponding Authors: ^*13911447793@139.com

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	YAN Ge
	ZHANG Huijuan
	CAI Lihai
	SHAO Weiguang
	LIU Wenyan

Cite this article:

YAN Ge,ZHANG Huijuan,CAI Lihai, et al. Evolution of the Structure and Properties of Thermoplastic Polyurethane Under the Joint Action of Fuel Oil and Ultraviolet Light[J]. Materials Reports, 2024, 38(6): 22050216-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22050216 OR http://www.mater-rep.com/EN/Y2024/V38/I6/22050216

1 Jia Z M, Guo Z W, Li Y Q, et al. Ship Engineering, 2019, 41(9), 93(in Chinese).
贾郑铭, 郭智威, 李永清, 等. 船舶工程, 2019, 41(9), 93.
2 An S D, Zhang X W, Zhu W Y, et al. Plastics Science and Technology, 2021, 49(12), 29(in Chinese).
安绍都, 张学文, 祝问遥, 等. 塑料科技, 2021, 49(12), 29.
3 Zhang X J, Zhao L, Zheng Z Q, et al. Journal of machine Design, 2015, 32(7), 61(in Chinese).
张新杰, 赵林, 郑中强, 等. 机械设计, 2015, 32(7), 61.
4 Gardette J L, Lemaire J. Polymer Degradation and Stability, 1984, 6(3), 135.
5 Rosu D, Rosu L, Cascaval C N. Polymer Degradation and Stability, 2009, 94(4), 591.
6 Yang H. Study on the aging and anti-aging of thermoplastic polyurethane elastomer. Master's Thesis, Xiamen University, China, 2017(in Chinese).
杨慧. 热塑性聚氨酯弹性体的老化与防老化研究. 硕士学位论文, 厦门大学, 2017.
7 You G X, Cai S D, Zhou X L, et al. Engineering Plastics Application, 2017, 45(9), 93(in Chinese).
游革新, 蔡斯迪, 周序霖, 等. 工程塑料应用, 2017, 45(9), 93.
8 Aglan H, Calhoun M, Allie L. Journal of Applied Polymer Science, 2008, 108(1), 558.
9 Boubakri A, Guermazi N, Elleuch K, et al. Materials Science and Engineering, 2010, 527(7-8), 1649.
10 Li H H. Studies on structures of thermoplastic polyurethane and aging behaviors. Master's Thesis, Fudan University, China, 2013(in Chinese).
李慧慧. 热塑性聚氨酯弹性体结构及其老化性能的研究. 硕士学位论文, 复旦大学, 2013.
11 Mishra A K, Chattopadhyay D K, Sreedhar B, et al. Progress in Organic Coatings, 2006, 55(3), 231.
12 Geng S, Gao J, Li X G, et al. Journal of University of Science and Technology Beijing, 2009, 31(6), 752(in Chinese).
耿舒, 高瑾, 李晓刚, 等. 北京科技大学学报, 2009, 31(6), 752.
13 Zhang H J, Shao W G, Liu W Y, et al. Special Purpose Rubber Products, 2019, 40(2), 72(in Chinese).
张慧娟, 邵伟光, 刘文言, 等. 特种橡胶制品, 2019, 40(2), 72.
14 Aguirresarobe R H, Irusta L, Fernandez-Berridi M J. Polymer Degradation and Stability, 2012, 97(9), 1671.
15 Tao C. Regulation of micro-phase separation morphology, properties and applications of polyurethane. Master's Thesis, Anhui University, China, 2018(in Chinese).
陶灿. 聚氨酯的微相分离结构调控、性能和应用. 硕士学位论文, 安徽大学, 2018.
16 Tian Q, Krakovský I, Yan G, et al. Polymers, 2016, 8(5), 197.
17 Xie F, Zhang T, Bryant P, et al. Progress in Polymer Science, 2019, 90, 261.
18 Qie J W, Li W L, Zhou C R. Journal of Chemical Engineering of Chinese Universities, 2016, 30(5), 1112. (in Chinese).
郄晶伟, 李文俐, 周彩荣. 高校化学工程学报, 2016, 30(5), 1112.
19 Zhang J Y, Chen C J. Guangdong Chemical Industry, 2010, 37(11), 230(in Chinese).
张建雨, 陈常见. 广东化工, 2010, 37(11), 230.
20 Yang G, Chen Q, Wang Y, et al. Polymer Journal, 1997, 29(2), 108.
21 Yi Z L. Synthesis and UV irradiation properties of PVC based UV absor-ber. Master's Thesis, Shihezi University, China, 2016(in Chinese).
尹祉力. PVC基紫外线吸收剂的合成及其对PVC抗紫外光老化性能研究. 硕士学位论文, 石河子大学, 2016.