| Study on the Synergistic Effect of Cement Slurry-carbonation for Enhancing Recycled Concrete Aggregate |
| FENG Chunhua, CUI Buwen, GUO Hui, ZHANG Wenyan, ZHU Jianping*
|
| School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000, Henan, China |
|
|
|
|
Abstract Improving the performance of recycled concrete aggregate (RCA) has important research implications for their wider application in structural engineering. In this study, the RCA was enhanced by the synergistic effect of cement paste-carbonation, and analyzed in comparison with unreinforced, single cement slurry reinforced, and single carbonation reinforced treated RCA. The results showed that the basic properties of RCA after cement slurry-carbonation synergistic strengthening were significantly improved, and the water absorption, crushing value and porosity were reduced by 16.04%, 19.77% and 36.29%, respectively, compared with untreated RCA. In contrast to single reinforcement, the synergistic effect of cement hydration and carbonation can further utilize the carbonation products to repair the adhesion mortar and interfacial transition zone (ITZ) of RCA while reinforcing the RCA surface. It can be clearly stated that the use of cement slurry-carbonation synergistic reinforcement treatment is an effective, environmentally friendly and low-cost method of RCA enhancement.
|
|
Published: 10 November 2023
Online: 2023-11-10
|
|
|
| Fund:Key Public Welfare Special Project of Henan Province (201300311000), Key Scientific Research Project in Colleges and Universities of Henan Province (22A430022), and Henan Outstanding Foreign Scientists' Workroom (GZS2021003). |
|
|
1 Wang J, Zhang J, Cao D, et al. Construction and Building Materials, 2020, 234, 117366.
2 Duan Z H, Jiang S S, Xiao J Z, et al. Journal of Building Materials, 2021, 24(3), 545(in Chinese).
段珍华, 江山山, 肖建庄, 等. 建筑材料学报, 2021, 24(3), 545.
3 Chen C H, Liu R G, Zhu P H, et al. Journal of Building Materials, 2021, 24(6), 1216(in Chinese).
陈春红, 刘荣桂, 朱平华, 等. 建筑材料学报, 2021, 24(6), 1216.
4 Ho H L, Huang R, Lin W T, et al. Construction and Building Materials, 2018, 160, 278.
5 Feng C, Cui B, Huang Y, et al. Construction and Building Materials, 2022, 317, 126168.
6 Zhang H, Zhao Y, Meng T, et al. Construction and Building Materials, 2015, 95, 721.
7 Liang C, Lu N, Ma H, et al. Journal of CO2 Utilization, 2020, 39, 101185.
8 Kou S C, Zhan B J, Poon C. Cement and Concrete Composites, 2014, 45(1), 22.
9 Pan G, Zhan M, Fu M, et al. Construction and Building Materials, 2017, 154, 810.
10 Qiu J, Ting D, Yang E H. Construction and Building Materials, 2014, 57, 144.
11 Li W, Long C, Tam V W Y, et al. Construction and Building Materials, 2017, 142, 42.
12 Gao S, Guo J, Gong Y, et al. Case Studies in Construction Materials, 2022, 16, e01034.
13 Said A M, Ayad A, Talebi E, et al. Journal of the American Concrete Institute, 2017, 314, 1.
14 Kim J. Construction and Building Materials, 2021, 301, 124091.
15 Yue L, Li J. Construction and Building Materials, 2014, 53, 511.
16 Guo H, Shi C, Guan X, et al. Cement and Concrete Composites, 2018, 89, 251.
17 Yue G B. Study on the recycled concrete multi-interface structure and the damage mechanism of performance. Ph. D. Thesis, Qingdao University of Technology, China, 2018(in Chinese).
岳公冰. 再生混凝土多重界面结构与性能损伤机理研究. 博士学位论文, 青岛理工大学, 2018. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2023, Vol. 37 