基于壳聚糖/黄原胶互穿网络的导电水凝胶支架制备及性能研究

doi:10.11896/cldb.22030238

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (16835KB)
Export: BibTeX | EndNote (RIS)

Abstract Conductive scaffolds are used in neural tissue engineering, which is beneficial to cell proliferation and growth, but the conductive polymers inside the scaffolds usually bring cytotoxicity and cell adhesion problems caused by hydrophobic groups. In this study, a novel PEDOT-HA/CS/XG interpenetrating network conductive hydrogel scaffold was successfully prepared by combining xanthan gum (XG) with chitosan (CS) and introducing hyaluronic acid-doped poly-3,4-ethylene dioxythiophene (PEDOT-HA) conductive nanoparticles. In the experiment, gluconolactone (GDL) was used to dissolve CS to realize the combination of CS and XG, and the gelation time was shortened by optimizing the content of GDL. The introduction of PEDOT-HA conductive nanoparticles gave the scaffold material conductivity, and the effect of PEDOT-HA content on the porosity, electrical conductivity and water absorption of the scaffold material was determined, besides the degradability, rheology, thermal stability and mechanical properties of the scaffold were investigated. The results showed that the introduction of PEDOT-HA improved the porosity, electrical conductivity, elasticity and mechanical strength of the hydrogel, and the water absorption rate of the PEDOT-HA/CS/XG conductive hydrogel scaffold was between 2 575%—3 949%, and it has suitable degradation rate and thermal stability. Cell adhesion rate detection and scanning electron microscope (SEM) observation results showed that the introduction of PEDOT-HA was beneficial to the adhesion and growth of PC12 cells and formed a staggered network structure. The results of cell viability detection and fluorescence staining showed that PC12 cells maintained a good proliferation activity on the conductive hydrogel scaffold. After 5 d of culture, the cell viability on the 10% PEDOT-HA/CS/XG scaffold could reach the highest level of 120.42% in the control group, which proves that the PEDOT-HA/CS/XG conductive hydrogel scaffold has good biocompatibility and demonstrates potential for application in neural tissue engineering.

Key words： conductive hydrogels scaffolds poly 3,4-ethylene dioxythiophene xanthan gum chitosan tissue engineering

Published: 25 September 2023 Online: 2023-09-18

CLC number:

Q819

Fund:National Program on Key Basic Research Project of China (2018AAA0100300) and the Fundamental Research Funds for the Central Universities (DUT21YG107).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHOU Xin
	GUAN Shui
	SUN Changkai

Cite this article:

ZHOU Xin,GUAN Shui,SUN Changkai. Preparation and Properties of Conductive Hydrogel Scaffolds Based on Chitosan/Xanthan Gum Interpenetrating Networks[J]. Materials Reports, 2023, 37(18): 22030238-8.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22030238 OR http://www.mater-rep.com/EN/Y2023/V37/I18/22030238

1 Mchugh D, Gil J. Journal of Cell Biology, 2018, 217(1), 65.
2 Niri A D, Zarchi A A K, Harati P G, et al. Artificial Organs, 2019, 43(10), 947.
3 Dong Z, Pei Z, Li Z, et al. Neuroscience Letters, 2017, 651, 109.
4 Meng X T, Du Y S, Dong Z Y, et al. Journal of Neural Engineering, 2020, 17(5), 056048.
5 Zhang Q S, Yan Y H, Li S P, et al. Biomedical Materials, 2009, 4(3), 035008.
6 Ng J Y, Obuobi S, Chua M L, et al. Carbohydrate Polymers, 2020, 241, 116345.
7 Byram P K, Sunka K C, Barik A, et al. International Journal of Biological Macromolecules, 2020, 165, 874.
8 Le Y G. 3D Bioprinting chondroconductive scaffolds based on photo-crosslinkable xanthan for customized cartilage tissue engineering. Ph.D. Thesis, Guangxi Medical University, China, 2019 (in Chinese).
勒义官. 可紫外光交联的黄原胶墨水3D生物打印用于软骨组织工程研究. 博士学位论文, 广西医科大学, 2019.
9 Kurita K. Marine Biotechnology, 2006, 8(3), 203.
10 Chang S, Lin H T V, Wu G J, et al. Carbohydrate Polymers, 2015, 134, 74.
11 Jiang T, Deng M, James R, et al. Acta Biomaterialia, 2014, 10(4), 1632.
12 Westin C B, Trinca R B, Zuliani C, et al. Materials Science & Enginee-ring C, 2017, 80, 594.
13 Rao K M, Kumar A, Han S S. Journal of Materials Science & Technology, 2018, 34(8), 1371.
14 Hu Y, Ma S S, Yang Z H, et al. Colloids and Surfaces B-Biointerfaces, 2016, 140, 382.
15 Akay S, Heils R, Trieu H K, et al. Carbohydrate Polymers, 2017, 161, 228.
16 Lv X J, Liu Y E, Song S B, et al. Carbohydrate Polymers, 2019, 205, 312.
17 Zha F W, Chen W, Lv G W, et al. Materials Science & Engineering C, 2021, 120, 111795.
18 Xiao Y H, Li C M, Yu S C, et al. Talanta, 2007, 72(2), 532.
19 Abedi A, Hasanzadeh M, Tayebi L. Materials Chemistry and Physics, 2019, 237, 121882.
20 Yang B G, Yao F L, Ye L, et al. Biomaterials Science, 2020, 8(11), 3173.
21 Xu C, Guan S, Wang S P, et al. Materials Science & Engineering C, 2018, 84, 32.
22 Asplund M, Thaning E, Lundberg J, et al. Biomedical Materials, 2009, 4(4), 45009.
23 Wang S P, Guan S, Wang J, et al. Journal of Bioscience and Bioenginee-ring, 2017, 123(1), 116.
24 Mantione D, Del A I, Schaafsma W, et al. Macromolecular Bioscience, 2016, 16(8), 1227.
25 Ozgenel G Y. Microsurgery, 2003, 23(6), 575.
26 Wang S P. The preparation of three-dimensional conductive scaffolds and their effect on the proliferation and differentiation of neural stem cells in vitro. Ph.D. Thesis, Dalian University of Technology, China, 2018 (in Chinese).
王树萍. 三维导电支架的制备及其对神经干细胞体外增殖与分化的影响. 博士学位论文, 大连理工大学, 2018.
27 Han Y, Zeng Q Y, Li H Y, et al. Acta Biomaterialia, 2013, 9(11), 9107.
28 Hu X Y, Man Y, Li W F, et al. Polymers, 2019, 11(10), 1601.
29 Wang S P, Guan S, Zhu Z B, et al. Materials Science & Engineering C, 2017, 71, 308.
30 Xu J, Hu X Y, Jiang S Y, et al. Polymers, 2019, 11(2), 230.
31 Santini M T, Rainaldi G, Indovina P L. International Journal of Radiation Biology, 2009, 85(4), 294.
32 Liu X F, Miller A L, Park S, et al. ACS Applied Materials & Interfaces, 2017, 9(17), 14677.
33 Zhu Z B, Guan S, Wang S P, et al. Journal of Chemical Engineering of Chinese Universities, 2017, 31(5), 1143 (in Chinese).
朱智博, 关水, 王树萍, 等. 高校化学工程学报, 2017, 31(5), 1143.
34 Wang S P, Guan S, Xu C, et al. Journal of Chemical Engineering of Chinese Universities, 2014, 28(3), 592 (in Chinese).
王树萍, 关水, 徐超, 等. 高校化学工程学报, 2014, 28(3), 592.
35 Wu H, Zhang J, Luo Y, et al. Journal of the Mechanical Behavior of Biomedical Materials, 2015, 50, 192.
36 Bresolin T M B, Milas M, Rinaudo M, et al. International Journal of Biological Macromolecules, 1998, 23(4), 263.
37 Zhou S H. Conformation transition of xanthan in aqueous solution and its rheological research. Master's Thesis, Shanghai Jiao Tong University, China, 2008 (in Chinese).
周盛华. 黄原胶在水溶液中的构象转变及其流变学研究. 硕士学位论文, 上海交通大学, 2008.
38 Falland C L, Scholze M, Hammer N, et al. Journal of the Mechanical Behavior of Biomedical Materials, 2018, 77, 609.
39 Zhang R R. Research on the viscoelastic mechanical behavior of brain tissue. Master's Thesis, Dalian University of Technology, China, 2017 (in Chinese).
张润润. 脑组织粘弹性力学行为研究. 硕士学位论文, 大连理工大学, 2017.
40 Tang S M D, White J D, Tien L W, et al. Proceedings of the National Academy of Sciences of the United States of America, 2014, 111(38), 13811.
41 Vanwachem P B, Beugeling T, Feijen J, et al. Biomaterials, 1985, 6(6), 403.