剧烈扭转压缩轧制45钢超细晶棒组织演变机理

doi:10.11896/cldb.22010069

Abstract
Figure/Table
References
Related Citation (2)

Download:

Full Text ( PDF ) (25884KB)
Export: BibTeX | EndNote (RIS)

Abstract Based on the self-developed severe torsional compression rolling method, taking 45 steel as the research object, the ultrafine-grained bar with a diameter of 25 mm was obtained by single pass rolling at 750 ℃ with a diameter reduction rate of 48%. The microstructure evolution and grain refinement mechanism were analyzed by scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM), and the mechanical properties were measured and analyzed. The results show thatthe degree of torsional compression in the center of the bar was slightly weaker than that of the edge, the grains were oriented along the axial direction and the grain size was refined to 2.3 μm. In contrast, the edge region experienced intense torsional compression, resulting in a uniform distribution of grain orientation and significant grain size refinement to 1.7 μm. The main refinement mechanism of grain:the transformation from austenite to ferrite induced by severe torsional compression deformation, as well as the occurrence of a sufficient continuous dynamic recovery and dynamic recrystallization process. After rolling, the yield strength, tensile strength and elongation of the steel bar were 402.5 MPa, 643.5 MPa and 25.7%, respectively, representing a 24%, 5.6%, and 14.7% increase compared to the pre-rolling values.

Key words： severe torsional compression deformation ultrafine grain dynamic recovery and dynamic recrystallization deformation-induced ferrite transformation

Published: 10 August 2023 Online: 2023-08-07

CLC number:

TG156.34

Fund:Research and Development Plan of Shaanxi Province (2020GY-253).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHAO Jiahao
	PANG Yuhua
	SUN Qi
	NIU Ben
	LIU Dong
	ZHANG Zhe

Cite this article:

ZHAO Jiahao,PANG Yuhua,SUN Qi, et al. Microstructure Evolution Mechanism of Ultrafine Grained Bar of 45 Steel Rolled by Severe Torsional Compression[J]. Materials Reports, 2023, 37(15): 22010069-5.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22010069 OR http://www.mater-rep.com/EN/Y2023/V37/I15/22010069

1 Wu S, Li X C, Zhang J, et al. Acta Metallurgica Sinica, 2014, 50 (4), 400 (in Chinese).
吴斯, 李秀程, 张娟, 等. 金属学报, 2014, 50(4), 400.
2 Huang G K, Qu L D, Lu Y Z, et al. Vacuum, 2018, 153, 39.
3 Shen J J. Hebei metallurgy, 2017 (8), 6 (in Chinese).
沈俊杰. 河北冶金, 2017 (8), 6.
4 Valiev R Z, Estrin Y, Horita Z, et al. Journal of Metals, 2006, 58(4), 33.
5 Bagherpour E, Pardis N, Reihanian M, et al. The International Journal of Advanced Manufacturing Technology, 2018, 100(5-8), 1647.
6 Dobatkin S, Zrnik J, Nikulin S, et al. Journal of Physics:Conference Series, 2010, 240(1), 012127.
7 Feng G H, Du Z Z, Wang J T, et al. Journal of Materials Research, 2011, 25 (2), 151 (in Chinese).
冯广海, 杜忠泽, 王经涛, 等. 材料研究学报, 2011, 25(2), 151.
8 Zrnik J, Pippan R, Scheriau S, et al. Journal of Materials Science, 2010, 45(17), 4822.
9 Ma E. Scripta Materialia, 2003, 49(7), 663.
10 Jia N N, Guo K, He Y M, et al. Materials Science and Engineering:A, 2017, 700, 175.
11 Liu L, Shi M J, Li H B. Hot Working Process, 2019, 48(3), 35 (in Chinese).
刘乐, 石妙杰, 李红斌. 热加工工艺, 2019, 48(3), 35.
12 Liu B X, Fan K Y, Yin F X, et al. Materials Science and Engineering:A, 2020, 774, 138954.
13 Lin P C, Pang Y H, Sun Q, et al. Acta Metallurgica Sinica, 2021, 57 (5), 605 (in Chinese).
林鹏程, 庞玉华, 孙琦, 等. 金属学报, 2021, 57(5), 60.
14 刘东, 庞玉华, 陶镳. 中国专利, 202010809863. 9, 2020.
15 Zhang Z, Liu D, Wang Y S, et al. Materials Letters, 2020, 276, 128209.
16 Pang Y H, Lin P C, Sun Q, et al. Archives of Civil and Mechanical Engineering, 2020, 20(4), 1.
17 Chen J L, Feng G H, Yang D, et al. Special steel, 2021, 42 (3), 12 (in Chinese).
陈继林, 冯光宏, 杨栋, 等. 特殊钢, 2021, 42(3), 12.
18 Storojeva L, Kaspar R, Ponge D. ISIJ International, 2004, 44(7), 1211.
19 Arruabarrena J, López B, Rodriguez-Ibabe J M. Metallurgical and Materials Transactions A, 2013, 45(3), 1470.
20 Dong H, Sun X J. Current Opinion in Solid State and Materials Science, 2005, 9(6), 269.
21 Wu S D, An X H, Han W Z, et al. Acta Metallurgica Sinica, 2010, 46 (3), 257 (in Chinese).
吴世丁, 安祥海, 韩卫忠, 等. 金属学报, 2010, 46(3), 257.
22 Wang Y M. Controlled rolling and controlled cooling of steel, Metallurgical Industry Press, China 2009, pp.15 (in Chinese).
王有铭. 钢材的控制轧制和控制冷却, 冶金工业出版社, 2009, pp.15.